Double-perovskite type oxide LaSrFeCoO_6 was used as oxygen carrier for chemical looping steam methane reforming（CL-SMR） due to its unique structure and reactivity. Solid-phase, amorphous alloy, sol-gel and micro-em...Double-perovskite type oxide LaSrFeCoO_6 was used as oxygen carrier for chemical looping steam methane reforming（CL-SMR） due to its unique structure and reactivity. Solid-phase, amorphous alloy, sol-gel and micro-emulsion methods were used to prepare the LaSrFeCoO_6 samples, and the as-prepared samples were characterized by means of X-ray diffraction（XRD）, hydrogen temperature-programmed reduction（H_2-TPR）, X-ray photoelectron spectroscopy（XPS）, Brunauer-Emmett-Teller（BET） surface area. Results showed that the samples made by the four different methods exhibited pure crystalline perovskite structure. The ordered double perovskite LaSrFeCoO_6 was regarded as a regular arrangement of alternating FeO_6 and CoO_6 corner-shared octahedra, with La and Sr cations occupying the voids in between the octahedral. Because the La^（3＋） and Sr^（2＋） ions in A-site did not take part in reaction, the TPR patterns showed the reductive properties of the B-site metals. The reduction peaks at low temperature revealed the reduction of adsorbed oxygen on surface and combined with the reduction of Co^（3＋） to Co^（2＋） and to Co^0, while the reduction of Fe^（3＋） to Fe^（2＋） and the partial reduction of Fe^（2＋） to Fe^0 occurred at higher temperatures. From the point of view of the oxygen-donation ability, resistance to carbon formation, as well as hydrogen generation capacity, the sample made by micro-emulsion method exhibited the best reactivity. Its redox reactivity was very stable in ten successive cycles without deactivation. Compared to the single perovskite-type oxides LaFeO_3 and LaCoO_3, the double perovskite LaSrFeCoO_6 exhibited better syngas and hydrogen generation capacity.展开更多
基金Project supported by the National Natural Science Foundation of China(51406208,51406214)Science & Technology Research Project of Guangdong Province(2013B050800008,2015A010106009)
文摘Double-perovskite type oxide LaSrFeCoO_6 was used as oxygen carrier for chemical looping steam methane reforming（CL-SMR） due to its unique structure and reactivity. Solid-phase, amorphous alloy, sol-gel and micro-emulsion methods were used to prepare the LaSrFeCoO_6 samples, and the as-prepared samples were characterized by means of X-ray diffraction（XRD）, hydrogen temperature-programmed reduction（H_2-TPR）, X-ray photoelectron spectroscopy（XPS）, Brunauer-Emmett-Teller（BET） surface area. Results showed that the samples made by the four different methods exhibited pure crystalline perovskite structure. The ordered double perovskite LaSrFeCoO_6 was regarded as a regular arrangement of alternating FeO_6 and CoO_6 corner-shared octahedra, with La and Sr cations occupying the voids in between the octahedral. Because the La^（3＋） and Sr^（2＋） ions in A-site did not take part in reaction, the TPR patterns showed the reductive properties of the B-site metals. The reduction peaks at low temperature revealed the reduction of adsorbed oxygen on surface and combined with the reduction of Co^（3＋） to Co^（2＋） and to Co^0, while the reduction of Fe^（3＋） to Fe^（2＋） and the partial reduction of Fe^（2＋） to Fe^0 occurred at higher temperatures. From the point of view of the oxygen-donation ability, resistance to carbon formation, as well as hydrogen generation capacity, the sample made by micro-emulsion method exhibited the best reactivity. Its redox reactivity was very stable in ten successive cycles without deactivation. Compared to the single perovskite-type oxides LaFeO_3 and LaCoO_3, the double perovskite LaSrFeCoO_6 exhibited better syngas and hydrogen generation capacity.
