In this study Eucalyptus tannin (T) was isolated from outer bark of Eucalyptus trees;as sodium phenoxide salt and used as extender or copolymer into phenol formaldehyde (PF) resin at five percent (10, 20, 30, 40 and 5...In this study Eucalyptus tannin (T) was isolated from outer bark of Eucalyptus trees;as sodium phenoxide salt and used as extender or copolymer into phenol formaldehyde (PF) resin at five percent (10, 20, 30, 40 and 50)% W/W. Tan-nin-phenol formaldehyde (TPF) and tannin formaldehyde-phenol formaldehyde (TFPF) resins that synthesized in this study were evaluated as adhesive material for cellulosic fibers by study the mechanical properties of the composite sheets .The results show that the substituting of (PF) with tannin at (10 –50)% W/W give resins with mechanical properties comparable or near to those of pure (PF) , where the tensile strength at break (Tb) ranging from 15.15 Mpa to 22.27 Mpa as compared with 17.6 Mpa for pure (PF);while the impact strength properties (Im) of composites sheets increased with increased the (T) percents which were about 5.16 KJ/m2 for (TPF – 10%) and 7.21 KJ/m2 for (TPF - 50%) .On the other hand modification of (T) to tannin formaldehyde resin (TF) appear less performance at the results of this study , this effect probably to low penetration of (TFPF) resins between the small voids of cellulose fibers when soaked it in resin solutions. In general the results of this study indicate that the Eucalyptus tannin can be used for par-tial substitution of (PF) to produce resins with feasible mechanical properties and can be used in some applications of (PF) resins.展开更多
In this paper, the preparation of graphene oxide was achieved by Hummers method and the surface modification was achieved by poly(hexaneditiol), which was a synthetic thermotropic liquid crystalline polymer. The c-PHD...In this paper, the preparation of graphene oxide was achieved by Hummers method and the surface modification was achieved by poly(hexaneditiol), which was a synthetic thermotropic liquid crystalline polymer. The c-PHDT/GO/PF composites were prepared by blending, rolling and compression molding techniques. Then, the as-prepared samples were characterized by FTIR, Raman, XRD, TGA and POM to obtain information on their structures and properties. After that, the effects of c-PHDT/GO content on the mechanical properties, friction performance and dynamic mechanical performance of c-PHDT/GO/PF composites were studied by Mechanical and Dynamic Mechanical Analysis (DMA) methods. Also, Scanning Electron Microscope (SEM) was used for the characterization of wear and fracture surface morphology. The results revealed that the reinforcing effect of c-PHDT/GO was significant as a considerable enhancement on the mechanical performance of c-PHDT/GO/PF composite as compared to pure phenol-formaldehyde composites was observed: the impact strength, bending modulus and bending strength increased from 1.63 kJ/m2, 8.61 GPa and 41.55 MPa to 2.31 kJ/m2, 10.16 GPa and 54.40 MPa respectively at the c-PHDT/GO content = 0.75%. Moreover, the initial storage modulus increased by 28.4%, while the wear mass loss decreased by 17.8%. More importantly, the reinforcement by c-PHDT/GO was further enhanced as compared to GO/PF and p-PHDT/GO/PF composites, the impact strength of c-PHDT/GO/PF composite increased by 27.6% and 11.1%, the bending strength increased by 11.8% and 7.6%, the initial storage modulus increased by 16.2% and 4.2% and the mass loss due to wear decreased by 12.7% and 8.8%, respectively. Based on these results, we can conclude that the surface modification of GO by poly(hexanedithiol), which includes synergistic effect by c-PHDT and GO, improves the interfacial adhesion between GO and the resin matrix, thus reinforcing the composites.展开更多
For manufacturing low-formaldehyde emission particleboard from wheat straw and urea-formaldehyde （UF） resins using urea treatment for indoor environments, we investigated the influence of urea treatment on the forma...For manufacturing low-formaldehyde emission particleboard from wheat straw and urea-formaldehyde （UF） resins using urea treatment for indoor environments, we investigated the influence of urea treatment on the formaldehyde emission, physical and mechanical properties of the manufactured particleboard. Wheat straws were treated at three levels of urea concentration （5%, 10%, 15%） and 95℃ as holding temperature. Wheat straw particleboards were manufactured using hot press at 180℃ and 3 MPa with two types of UF adhesive （UF-45, UF-91）. Then the formaldehyde emission values, physical properties and mechanical properties were considered. The results show that the for- maldehyde emission value was decreased by increasing urea concentration. Furthermore, the results indicate that the specimens under urea treatment have better mechanical and physical properties compared with control specimens. Also specimens under urea treatment at 10% concentration and UF-91 type adhesive have the most optimum physical and mechanical strength.展开更多
The poor bonding performance between aqueous adhesives represented by melamine-urea formaldehyde(MUF)resins and reed straw hinders their applications in the field of non-wood-based panels.Multi-hydroxyl polymers are h...The poor bonding performance between aqueous adhesives represented by melamine-urea formaldehyde(MUF)resins and reed straw hinders their applications in the field of non-wood-based panels.Multi-hydroxyl polymers are highly reactive and are often used as crosslinkers.This study fabricated a resin with a strengthened crosslinked structure by combining a multi-hydroxyl polymer and MUF resin prepolymer.The reed particleboard was prepared by using this resin as an adhesive and reed stalk as the matrix.The results show that neighboring molecules combined to form C–O–C bonds that strengthened the cross-linked structure of the resin.In addition,the viscosity of the resin was increased,and a continuous adhesive layer on the surface of reed particles was formed,which slowed the penetration of reed particles.The adhesive layer significantly improved the mechanical properties of the reed particleboard.The maximum modulus of rupture(MOR),modulus of elasticity(MOE),and internal bonding strength(IB)of the reed particleboard were 33.53,4126,and 0.79 MPa,respectively.The IB of the board was 3.3 times higher than that of the reed particleboard prepared with a conventional MUF resin.Reed straw is a non-wood biomass material that has the advantage of sustainable development and may replace woodbased materials to produce particleboard.This resin-prepared reed particleboard is expected to be used in areas such as custom furniture and engineering materials.展开更多
文摘In this study Eucalyptus tannin (T) was isolated from outer bark of Eucalyptus trees;as sodium phenoxide salt and used as extender or copolymer into phenol formaldehyde (PF) resin at five percent (10, 20, 30, 40 and 50)% W/W. Tan-nin-phenol formaldehyde (TPF) and tannin formaldehyde-phenol formaldehyde (TFPF) resins that synthesized in this study were evaluated as adhesive material for cellulosic fibers by study the mechanical properties of the composite sheets .The results show that the substituting of (PF) with tannin at (10 –50)% W/W give resins with mechanical properties comparable or near to those of pure (PF) , where the tensile strength at break (Tb) ranging from 15.15 Mpa to 22.27 Mpa as compared with 17.6 Mpa for pure (PF);while the impact strength properties (Im) of composites sheets increased with increased the (T) percents which were about 5.16 KJ/m2 for (TPF – 10%) and 7.21 KJ/m2 for (TPF - 50%) .On the other hand modification of (T) to tannin formaldehyde resin (TF) appear less performance at the results of this study , this effect probably to low penetration of (TFPF) resins between the small voids of cellulose fibers when soaked it in resin solutions. In general the results of this study indicate that the Eucalyptus tannin can be used for par-tial substitution of (PF) to produce resins with feasible mechanical properties and can be used in some applications of (PF) resins.
文摘In this paper, the preparation of graphene oxide was achieved by Hummers method and the surface modification was achieved by poly(hexaneditiol), which was a synthetic thermotropic liquid crystalline polymer. The c-PHDT/GO/PF composites were prepared by blending, rolling and compression molding techniques. Then, the as-prepared samples were characterized by FTIR, Raman, XRD, TGA and POM to obtain information on their structures and properties. After that, the effects of c-PHDT/GO content on the mechanical properties, friction performance and dynamic mechanical performance of c-PHDT/GO/PF composites were studied by Mechanical and Dynamic Mechanical Analysis (DMA) methods. Also, Scanning Electron Microscope (SEM) was used for the characterization of wear and fracture surface morphology. The results revealed that the reinforcing effect of c-PHDT/GO was significant as a considerable enhancement on the mechanical performance of c-PHDT/GO/PF composite as compared to pure phenol-formaldehyde composites was observed: the impact strength, bending modulus and bending strength increased from 1.63 kJ/m2, 8.61 GPa and 41.55 MPa to 2.31 kJ/m2, 10.16 GPa and 54.40 MPa respectively at the c-PHDT/GO content = 0.75%. Moreover, the initial storage modulus increased by 28.4%, while the wear mass loss decreased by 17.8%. More importantly, the reinforcement by c-PHDT/GO was further enhanced as compared to GO/PF and p-PHDT/GO/PF composites, the impact strength of c-PHDT/GO/PF composite increased by 27.6% and 11.1%, the bending strength increased by 11.8% and 7.6%, the initial storage modulus increased by 16.2% and 4.2% and the mass loss due to wear decreased by 12.7% and 8.8%, respectively. Based on these results, we can conclude that the surface modification of GO by poly(hexanedithiol), which includes synergistic effect by c-PHDT and GO, improves the interfacial adhesion between GO and the resin matrix, thus reinforcing the composites.
文摘For manufacturing low-formaldehyde emission particleboard from wheat straw and urea-formaldehyde （UF） resins using urea treatment for indoor environments, we investigated the influence of urea treatment on the formaldehyde emission, physical and mechanical properties of the manufactured particleboard. Wheat straws were treated at three levels of urea concentration （5%, 10%, 15%） and 95℃ as holding temperature. Wheat straw particleboards were manufactured using hot press at 180℃ and 3 MPa with two types of UF adhesive （UF-45, UF-91）. Then the formaldehyde emission values, physical properties and mechanical properties were considered. The results show that the for- maldehyde emission value was decreased by increasing urea concentration. Furthermore, the results indicate that the specimens under urea treatment have better mechanical and physical properties compared with control specimens. Also specimens under urea treatment at 10% concentration and UF-91 type adhesive have the most optimum physical and mechanical strength.
基金supported by the Hunan Province Science and Technology Major Project[2021NK1050]Strategic Research and Consulting Project of the Chinese Academy of Engineering:Research on Green and Low-Carbon Technology Innovation Strategy of Wood-Based Panel Industry[2022-XY-62]+1 种基金Changsha Science and Technology Project[kq2004096]Hunan Provincial Technical Innovation Platform and Talent Program in Science and Technology[2016TP1013].
文摘The poor bonding performance between aqueous adhesives represented by melamine-urea formaldehyde(MUF)resins and reed straw hinders their applications in the field of non-wood-based panels.Multi-hydroxyl polymers are highly reactive and are often used as crosslinkers.This study fabricated a resin with a strengthened crosslinked structure by combining a multi-hydroxyl polymer and MUF resin prepolymer.The reed particleboard was prepared by using this resin as an adhesive and reed stalk as the matrix.The results show that neighboring molecules combined to form C–O–C bonds that strengthened the cross-linked structure of the resin.In addition,the viscosity of the resin was increased,and a continuous adhesive layer on the surface of reed particles was formed,which slowed the penetration of reed particles.The adhesive layer significantly improved the mechanical properties of the reed particleboard.The maximum modulus of rupture(MOR),modulus of elasticity(MOE),and internal bonding strength(IB)of the reed particleboard were 33.53,4126,and 0.79 MPa,respectively.The IB of the board was 3.3 times higher than that of the reed particleboard prepared with a conventional MUF resin.Reed straw is a non-wood biomass material that has the advantage of sustainable development and may replace woodbased materials to produce particleboard.This resin-prepared reed particleboard is expected to be used in areas such as custom furniture and engineering materials.