The mathematical models are developed to evaluate the ultimate tensile strength( UTS) and hardness of CNTs / Al2024 composites fabricated by high-energy ball milling. The effects of the preparation variables which are...The mathematical models are developed to evaluate the ultimate tensile strength( UTS) and hardness of CNTs / Al2024 composites fabricated by high-energy ball milling. The effects of the preparation variables which are milling time,rotational speed,mass fraction of CNTs and ball to powder ratio on UST and hardness of CNTs / Al2024 composites are investigated. Based on the central composite design( CCD),a quadratic model is developed to correlate the fabrication variables to the UST and hardness. From the analysis of variance( ANOVA),the most influential factor on each experimental design response is identified. The optimum conditions for preparing CNTs / Al2024 composites are found as follows: 1. 53 h milling time,900 r / min rotational speed,mass fraction of CNTs 2. 87% and Ball to powder ratio 25 ∶ 1. The predicted maximum UST and hardness are 273.30 MPa and 261.36 HV,respectively. And the experimental values are 283.25 MPa and256.8 HV,respectively. It is indicated that the predicted UST and hardness after process optimization are found to agree satisfactory with the experimental values.展开更多
This study investigated the effects of adding graphene nanoplates(GNPs)and carbon nanotubes(CNTs)into the Al7075 matrix via the stir casting method on the microstructure and mechanical properties of the fabricated com...This study investigated the effects of adding graphene nanoplates(GNPs)and carbon nanotubes(CNTs)into the Al7075 matrix via the stir casting method on the microstructure and mechanical properties of the fabricated composites.By increasing the volume fraction of rein-forcements,the fraction of porosity increased.The X-ray diffraction results showed that the addition of reinforcements into the Al7075 changed the dominant crystal orientation from(002)to(111).Field emission scanning electron microscopy images also showed the distribution of clustered reinforcements in the matrix.Between the two reinforcements,the addition of CNTs generated a lower fraction of porosities.Through the addition of 0.52vol%GNPs into the matrix,the hardness,ultimate tensile strength and uniform elongation increased by 44%,32%,and 180%,respectively.Meanwhile,the presence of 0.71vol%CNTs in the matrix increased the hardness,tensile strength and uniform elongation by 108%,129%,and 260%,respectively.展开更多
Carbon nauotube（ CNT） reinforced aluminum metal matrix composites were welded by electron beam welding and the microstructures of welded joints were investigated. The result showed that the interracial reaction happ...Carbon nauotube（ CNT） reinforced aluminum metal matrix composites were welded by electron beam welding and the microstructures of welded joints were investigated. The result showed that the interracial reaction happened between the CNTs and Al matrix, which resulted in producing brittle Al4 C3 compounds in electron beam welds. The extent of interfacial reaction varies gradually in the depth and width direction. The length of the reactants Al4C3 became short duo to the temperature gradient in the molten pool. The quantity and size of Al4 C3 compounds increased with the increase of beam current and the decrease of welding speed in the middle zone of weld. However, no needle-like phase Al4C3 was observed in HAZ.展开更多
Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sinter...Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sintering temperature of 1500 °C and time of 10 min exhibited optimum mechanical properties at room temperature in terms of fracture toughness and transverse rupture strength.MoSi_2 based composite with 6.0% CNTs(volume fraction) had the highest fracture toughness,transverse rupture strength and hardness,which were improved by about 25.7%,51.5% and 24.4% respectively,as compared with pure MoSi_2.A Mo_(4.8)Si_3C_(0.6) phase was detected in CNTs/MoSi_2 composites by both X-ray diffraction(XRD) method and microstructure analysis with scanning electron microscopy(SEM).It is believed that the fine grains and well dispersed small Mo_(4.8)Si_3C_(0.6) particles had led to a higher hardness and strength of CNTs/MoSi_2 composites because of their particle pullout,crack deflection and micro-bridging effects.展开更多
Si/Cu3Si@C composites encapsulated in CNTs network(SCC-CNTs) were synthesized via the combination of ball-milling and CVD methods. SCC-CNTs consist of conductive Cu3Si, amorphous carbon layer, cross-linked CNTs, and t...Si/Cu3Si@C composites encapsulated in CNTs network(SCC-CNTs) were synthesized via the combination of ball-milling and CVD methods. SCC-CNTs consist of conductive Cu3Si, amorphous carbon layer, cross-linked CNTs, and the etched pores, which can play the synergistic effects on the improvement of electronic conductivity and Li^+ diffusion. The volume expansion of Si anode is also suppressed during the electrochemical process. The SCC-CNTs composites demonstrate a remarkably improved electrochemical performance compared with pure Si, which can deliver a discharge capacity of 2 171 mAh·g^-1 at 0.4 A·g^-1 with ICE of 85.2%, and retain 1197 mAh· g^-1 after 150 cycles. This work provides a facile approach to massively produce the high-performance Si-based anode materials for next-generation LIBs.展开更多
The mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering (SPS) were investigated. The results showed that the densities of the sintered composites gradually increa...The mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering (SPS) were investigated. The results showed that the densities of the sintered composites gradually increased with increasing sintering temperature and that the highest microhardness and compressive strength were achieved in the specimen sintered at 450A degrees C. CNTs dispersed uniformly in the Al-Si10Mg matrix when the addition of CNTs was less than 1.5wt%. However, when the addition of CNTs exceeded 1.5wt%, the aggregation of CNTs was clearly observed. Moreover, the mechanical properties (including the densities, compressive strength, and microhardness) of the composites changed with CNT content and reached a maximum value when the CNT content was 1.5wt%. Meanwhile, the minimum average friction coefficient and wear rate of the CNT/AlSi10Mg composites were obtained with 1.0wt% CNTs.展开更多
基金Sponsored by the Program for Innovative Research Team in University of Yunnan Province and Major Projects of Yunnan Province(Grant No.2014FC001)
文摘The mathematical models are developed to evaluate the ultimate tensile strength( UTS) and hardness of CNTs / Al2024 composites fabricated by high-energy ball milling. The effects of the preparation variables which are milling time,rotational speed,mass fraction of CNTs and ball to powder ratio on UST and hardness of CNTs / Al2024 composites are investigated. Based on the central composite design( CCD),a quadratic model is developed to correlate the fabrication variables to the UST and hardness. From the analysis of variance( ANOVA),the most influential factor on each experimental design response is identified. The optimum conditions for preparing CNTs / Al2024 composites are found as follows: 1. 53 h milling time,900 r / min rotational speed,mass fraction of CNTs 2. 87% and Ball to powder ratio 25 ∶ 1. The predicted maximum UST and hardness are 273.30 MPa and 261.36 HV,respectively. And the experimental values are 283.25 MPa and256.8 HV,respectively. It is indicated that the predicted UST and hardness after process optimization are found to agree satisfactory with the experimental values.
文摘This study investigated the effects of adding graphene nanoplates(GNPs)and carbon nanotubes(CNTs)into the Al7075 matrix via the stir casting method on the microstructure and mechanical properties of the fabricated composites.By increasing the volume fraction of rein-forcements,the fraction of porosity increased.The X-ray diffraction results showed that the addition of reinforcements into the Al7075 changed the dominant crystal orientation from(002)to(111).Field emission scanning electron microscopy images also showed the distribution of clustered reinforcements in the matrix.Between the two reinforcements,the addition of CNTs generated a lower fraction of porosities.Through the addition of 0.52vol%GNPs into the matrix,the hardness,ultimate tensile strength and uniform elongation increased by 44%,32%,and 180%,respectively.Meanwhile,the presence of 0.71vol%CNTs in the matrix increased the hardness,tensile strength and uniform elongation by 108%,129%,and 260%,respectively.
基金supported by the fund of Doctoral Startup Research of Nanchang Hangkong University(EA201203402)Aeronautical Science Foundation(20135456009)+1 种基金National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology(gf201401003)State Key Laboratory of Solidification Processing in NWPU(SKLSP201412)
文摘Carbon nauotube（ CNT） reinforced aluminum metal matrix composites were welded by electron beam welding and the microstructures of welded joints were investigated. The result showed that the interracial reaction happened between the CNTs and Al matrix, which resulted in producing brittle Al4 C3 compounds in electron beam welds. The extent of interfacial reaction varies gradually in the depth and width direction. The length of the reactants Al4C3 became short duo to the temperature gradient in the molten pool. The quantity and size of Al4 C3 compounds increased with the increase of beam current and the decrease of welding speed in the middle zone of weld. However, no needle-like phase Al4C3 was observed in HAZ.
基金Project(51371155)supported by the National Natural Science Foundation of ChinaProject(2014H0046)supported by the Key Science and Technology Project of Fujian Province,China+2 种基金Project(3502Z20143036)supported by the Scientific Research Fund of Xiamen,ChinaProject(JB13149)supported by the Education Department Science and Technology Project of Fujian Province,ChinaProject(2012D131)supported by the Natural Science Foundation Guidance Project of Fujian Province,China
文摘Molybdenum disilicide(MoSi_2) based composites with various contents of carbon nanotubes(CNTs) were fabricated by spark plasma sintering(SPS) in vacuum under a pressure of 25 MPa.The composites obtained under a sintering temperature of 1500 °C and time of 10 min exhibited optimum mechanical properties at room temperature in terms of fracture toughness and transverse rupture strength.MoSi_2 based composite with 6.0% CNTs(volume fraction) had the highest fracture toughness,transverse rupture strength and hardness,which were improved by about 25.7%,51.5% and 24.4% respectively,as compared with pure MoSi_2.A Mo_(4.8)Si_3C_(0.6) phase was detected in CNTs/MoSi_2 composites by both X-ray diffraction(XRD) method and microstructure analysis with scanning electron microscopy(SEM).It is believed that the fine grains and well dispersed small Mo_(4.8)Si_3C_(0.6) particles had led to a higher hardness and strength of CNTs/MoSi_2 composites because of their particle pullout,crack deflection and micro-bridging effects.
基金Funded by the National Key R&D Program of China(No.2016YFB0100302)
文摘Si/Cu3Si@C composites encapsulated in CNTs network(SCC-CNTs) were synthesized via the combination of ball-milling and CVD methods. SCC-CNTs consist of conductive Cu3Si, amorphous carbon layer, cross-linked CNTs, and the etched pores, which can play the synergistic effects on the improvement of electronic conductivity and Li^+ diffusion. The volume expansion of Si anode is also suppressed during the electrochemical process. The SCC-CNTs composites demonstrate a remarkably improved electrochemical performance compared with pure Si, which can deliver a discharge capacity of 2 171 mAh·g^-1 at 0.4 A·g^-1 with ICE of 85.2%, and retain 1197 mAh· g^-1 after 150 cycles. This work provides a facile approach to massively produce the high-performance Si-based anode materials for next-generation LIBs.
基金supported by the National Natural Science Foundation of China(NSFC,China) under Grant Number of 51405467Chongqing Research of Application Foundation and Advanced Technology(project No.cstc2016jcyj A0016)the Key Program of the Chinese Academy of Sciences(No.KGZD-EW-T0)
文摘The mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering (SPS) were investigated. The results showed that the densities of the sintered composites gradually increased with increasing sintering temperature and that the highest microhardness and compressive strength were achieved in the specimen sintered at 450A degrees C. CNTs dispersed uniformly in the Al-Si10Mg matrix when the addition of CNTs was less than 1.5wt%. However, when the addition of CNTs exceeded 1.5wt%, the aggregation of CNTs was clearly observed. Moreover, the mechanical properties (including the densities, compressive strength, and microhardness) of the composites changed with CNT content and reached a maximum value when the CNT content was 1.5wt%. Meanwhile, the minimum average friction coefficient and wear rate of the CNT/AlSi10Mg composites were obtained with 1.0wt% CNTs.