Effect of hot rolling on microstructure and tribology behaviors of Ti-50.8Ni alloy

We link different microstructures to tribological behaviors of Ti-50.8 Ni(mole fraction, %) in reciprocating mode at room temperature(20 ℃). Hot-rolled alloys with B2 phase exhibit lower coefficient of friction and wear rate compared to the ones with B19?. Stress-induced martensitic transformation occurs during sliding. However, multi-pass hot rolling weakens the wear resistance. In this study, microstructures were characterized through electron backscatter diffraction and transmission electron microscopy(EBSD/TEM). From the concept of energy conservation, the effects of weak intensity of hot-rolled textures on the wear resistance are minimal. Based on the result that the alloy with a higher portion of coincidence site lattice boundaries shows lower martensitic start transformation temperature in the DSC curves than that with higher KAM values, the delay on B2-B19? transformation from {112}B2 twins outweighs dislocations. Moreover, widely distributed small-angle grain boundaries owing to dynamic recovery improve the wear resistance effectively compared to those that are well-recrystallized.

Optimization of Grain Boundary Character Distribution in Fe-18Cr-18Mn-0.63N High-Nitrogen Austenitic Stainless Steel

Grain boundary engineering（GBE） is a practice of improving resistance to grain boundary failure of the material through increasing the proportion of low Σ coincidence site lattice（CSL） grain boundaries（special grain boundaries） in the grain boundary character distribution（GBCD）. The GBCD in a cold rolled and annealed Fe-18Cr-18Mn-0.63N high-nitrogen austenitic stainless steel was analyzed by electron back scatter difraction（EBSD）. The results show that the optimization process of GBE in the conventional austenitic stainless steel cannot be well applied to this high-nitrogen austenitic stainless steel. The percentage of low ΣCSL grain boundaries could increase from 47.3% for the solid solution treated high-nitrogen austenitic stainless steel specimen to 82.0% for the specimen after 5% cold rolling reduction and then annealing at 1423 K for 10 min.These special boundaries of high proportion efectively interrupt the connectivity of conventional high angle grain boundary network and thus achieve the GBCD optimization for the high-nitrogen austenitic stainless steel.

Improving Intergranular Stress Corrosion Cracking Resistance in a Fe–18Cr–17Mn–2Mo–0.85N Austenitic Stainless Steel Through Grain Boundary Character Distribution Optimization

The grain boundary character distribution(GBCD) optimization and its effect on the intergranular stress corrosion cracking(IGSCC) resistance in a cold-rolled and subsequently annealed Fe-18 Cr-17 Mn-2 Mo-0.85 N high-nitrogen nickel-free austenitic stainless steel were systematically explored.The results show that stacking faults and planar slip bands appearing at the right amount of deformation(lower than 10%) are beneficial cold-rolled microstructures to the GBCD optimization.The proportion of special boundaries gradually increases in the subsequent stages of recrystallization and grain growth,accompanying with the growth of twin-related domain in the experimental steel.In this way,the fraction of low ∑ coincidence site lattice(CSL) boundaries can reach as high as 82.85% for the specimen cold-rolled by 5% and then annealed at 1423 K for 72 h.After GBCD optimization,low ∑ CSL boundaries and the special triple junctions(J2,J3) of high proportion can greatly hinder the nitride precipitation along grain boundaries and enhance the capability for intergranular crack arrest,thus improving the IGSCC resistance of the experimental steel.