Transmission electron microscopy （TEM） and physics-chemical phase analysis were employed to investigate the precipitates in high strength steels microalloyed with Ti produced by compact strip production （CSP）. It ...Transmission electron microscopy （TEM） and physics-chemical phase analysis were employed to investigate the precipitates in high strength steels microalloyed with Ti produced by compact strip production （CSP）. It was seen that precipitates in Ti microalloyed steels mainly included TiN, Ti4C2S2, and TiC. The size of TiN particles varied from 50 to 500 nm, and they could precipitate during or before soaking. The Ti4C2S2 with the size of 40-100 nm might precipitate before rolling, and the TiC particles with the size of 5-50 nm precipitated heterogeneously. High Ti content would lead to the presence of bigger TiC particles that precipitated in austenite, and by contrast, TiC particles that precipitated in ferrite and the transformation of austenite to ferrite was smaller. They were less than 30 nm and mainly responsible for precipitate strengthening. It should be noted that the TiC particles in higher Ti content were generally smaller than those in the steel with a lower Ti content.展开更多
Microalloying element Nb in low carbon steels produced by compact strip production （CSP） process plays an important role in inhibiting recrystallization, decreasing the transformation temperature and grain refinemen...Microalloying element Nb in low carbon steels produced by compact strip production （CSP） process plays an important role in inhibiting recrystallization, decreasing the transformation temperature and grain refinement.With decreasing the rolling temperature, dislocations can be pinned by carbonitrides and the strength is increased. Based on the two sublattice model, with metal atom sublattice and interstitial atom sublattice,a thermodynamic model for carbonitride was established to calculate the equilibrium between matrix and carbonitride. In the steel produced by CSP, the calculation results showed that the starting temperature of precipitation of Ti and Nb are 1340℃ and 1040℃, respectively. In the range of 890-950℃, Nb rapidly precipitated. And the maximum of the atomic fraction of Nb in carbonitride was about 0.68. The morphologies and energy spectrum of the precipitates showed that （NbTi） （CN） precipitated near the dislocations. The experiment results show that Nb rapidly precipitated when the temperature was lower than 970℃, and the atomic fraction of Nb in carbonitride was about 60%-80%. The calculation results are in agreement with the experiment data. Therefore the thermodynamic model can be a useful assistant tool in the research on the precipitates in the low carbon steels produced by CSP.展开更多
The effect of boron on hot strips of low carbon steel produced by compact strip production （CSP） to reduce the strength to a certain degree was investigated, which is quite different from that of high-strength low a...The effect of boron on hot strips of low carbon steel produced by compact strip production （CSP） to reduce the strength to a certain degree was investigated, which is quite different from that of high-strength low alloy steel. The mechanical properties and microstructural evolution of the hot strip were studied using optical microscopy and tensile tests. By means of an electrolytic dissolution technique and Thermo-Cal calculation, the precipitates containing boron were analyzed and detected. From the electron backscattered diffraction analysis, it can be deciphered whether the microstructure has recrystallized or not. Furthermore, the effect of boron segregation on the recrystallization or non-recrystallization conditions can be distinguished. The segregation behavior of boron was investigated in boron-containing steel. The nonequilibrium segregation of boron during processing was discussed on the basis of the forming complexes with vacancies that migrate to the boundaries prior to annihilation, which was confirmed by the subsequent cold rolling with annealing experiments.展开更多
Based on the casting manufacture practice of steel slabs by CSP technology, the flow and the temperature fields of the funnel mould and the secondary cooling segment were simulated using the commercial code, CFX4. Com...Based on the casting manufacture practice of steel slabs by CSP technology, the flow and the temperature fields of the funnel mould and the secondary cooling segment were simulated using the commercial code, CFX4. Compared with other physical investigations, the correlative data of the present simulation results are in good agreement with them. Therefore, a more comprehensive survey for metallurgy characteristic of the flow and the temperature fields in CSP continuous casting process can be achieved.展开更多
Cold-rolled steel sheets in automotive applications require an excellent deep draw ability, which is characterized by the Lankford value （r-value）. In this study, a correlation was identified between r-value and pan...Cold-rolled steel sheets in automotive applications require an excellent deep draw ability, which is characterized by the Lankford value （r-value）. In this study, a correlation was identified between r-value and pancake-shaped grain flatness which is indicated as the ratio of grain diameter in the rolling direction （RD） and normal direction （ND） of sheets （dr/dn）. A mathematical model （ r = e^0.345（dn^1/2-dr^1/2） ） was developed to calculate r-value by the microstructure of steel sheets hot-rolled by compact strip production （CSP）. It is shown that the r-value is higher, if the microstructure of steel sheet is of pancake-shaped grains elongated in the rolling direction. The calculated r-value is confirmed to fit exactly to the measured one from the large-scale production.展开更多
Two experiments were carried out on the same compact strip production (CSP) line, which differs in that one of them experienced γ→α→γ thermal history. The differences in microstructure, precipitation, misorientat...Two experiments were carried out on the same compact strip production (CSP) line, which differs in that one of them experienced γ→α→γ thermal history. The differences in microstructure, precipitation, misorientation etc between two experiments were investigated by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron back-scattered diffraction (EBSD) and positron annihilation technique (PAT). The carbon concentration in matrix is more inhomogeneous in the experiment than that with γ→α→γ7 thermal history. The specific precipitation characteristic in the experiment without γ→α→γ thermal history is discussed on the basis of different carbon diffusion behavior and interaction between dislocation and excess carbon.展开更多
Large quantity of fine Ti（C,N） particles, 15-30 nm in size, were observed in low carbon hot strips added to a small amount of Ti and produced by CSP process. The results showed that the precipitation of Ti（C,N） mo...Large quantity of fine Ti（C,N） particles, 15-30 nm in size, were observed in low carbon hot strips added to a small amount of Ti and produced by CSP process. The results showed that the precipitation of Ti（C,N） mostly took place during soaking and hot rolling, which is significantly different from that in the conventional production. These fine Ti carbonitride particles could be very effective on the austenite grain refinement by hindering grain growth of recrystallized austenite. Their precipitation behavior was discussed and compared with that of the steels produced in the conventional production.展开更多
文摘Transmission electron microscopy （TEM） and physics-chemical phase analysis were employed to investigate the precipitates in high strength steels microalloyed with Ti produced by compact strip production （CSP）. It was seen that precipitates in Ti microalloyed steels mainly included TiN, Ti4C2S2, and TiC. The size of TiN particles varied from 50 to 500 nm, and they could precipitate during or before soaking. The Ti4C2S2 with the size of 40-100 nm might precipitate before rolling, and the TiC particles with the size of 5-50 nm precipitated heterogeneously. High Ti content would lead to the presence of bigger TiC particles that precipitated in austenite, and by contrast, TiC particles that precipitated in ferrite and the transformation of austenite to ferrite was smaller. They were less than 30 nm and mainly responsible for precipitate strengthening. It should be noted that the TiC particles in higher Ti content were generally smaller than those in the steel with a lower Ti content.
基金This work was supported by the National Natural Science Foundation of China under grant Nos. 50334010 and 50271009.
文摘Microalloying element Nb in low carbon steels produced by compact strip production （CSP） process plays an important role in inhibiting recrystallization, decreasing the transformation temperature and grain refinement.With decreasing the rolling temperature, dislocations can be pinned by carbonitrides and the strength is increased. Based on the two sublattice model, with metal atom sublattice and interstitial atom sublattice,a thermodynamic model for carbonitride was established to calculate the equilibrium between matrix and carbonitride. In the steel produced by CSP, the calculation results showed that the starting temperature of precipitation of Ti and Nb are 1340℃ and 1040℃, respectively. In the range of 890-950℃, Nb rapidly precipitated. And the maximum of the atomic fraction of Nb in carbonitride was about 0.68. The morphologies and energy spectrum of the precipitates showed that （NbTi） （CN） precipitated near the dislocations. The experiment results show that Nb rapidly precipitated when the temperature was lower than 970℃, and the atomic fraction of Nb in carbonitride was about 60%-80%. The calculation results are in agreement with the experiment data. Therefore the thermodynamic model can be a useful assistant tool in the research on the precipitates in the low carbon steels produced by CSP.
基金This work was financially supported by the National Natural Science Foundation of China (No. 50774110)Fok Ying Tong Edu-cation Foundation (No.104017).
文摘The effect of boron on hot strips of low carbon steel produced by compact strip production （CSP） to reduce the strength to a certain degree was investigated, which is quite different from that of high-strength low alloy steel. The mechanical properties and microstructural evolution of the hot strip were studied using optical microscopy and tensile tests. By means of an electrolytic dissolution technique and Thermo-Cal calculation, the precipitates containing boron were analyzed and detected. From the electron backscattered diffraction analysis, it can be deciphered whether the microstructure has recrystallized or not. Furthermore, the effect of boron segregation on the recrystallization or non-recrystallization conditions can be distinguished. The segregation behavior of boron was investigated in boron-containing steel. The nonequilibrium segregation of boron during processing was discussed on the basis of the forming complexes with vacancies that migrate to the boundaries prior to annihilation, which was confirmed by the subsequent cold rolling with annealing experiments.
基金Item Sponsored by Scientific Research Program Foundation of Shanghai City of China(04DZ05621)
文摘Based on the casting manufacture practice of steel slabs by CSP technology, the flow and the temperature fields of the funnel mould and the secondary cooling segment were simulated using the commercial code, CFX4. Compared with other physical investigations, the correlative data of the present simulation results are in good agreement with them. Therefore, a more comprehensive survey for metallurgy characteristic of the flow and the temperature fields in CSP continuous casting process can be achieved.
文摘Cold-rolled steel sheets in automotive applications require an excellent deep draw ability, which is characterized by the Lankford value （r-value）. In this study, a correlation was identified between r-value and pancake-shaped grain flatness which is indicated as the ratio of grain diameter in the rolling direction （RD） and normal direction （ND） of sheets （dr/dn）. A mathematical model （ r = e^0.345（dn^1/2-dr^1/2） ） was developed to calculate r-value by the microstructure of steel sheets hot-rolled by compact strip production （CSP）. It is shown that the r-value is higher, if the microstructure of steel sheet is of pancake-shaped grains elongated in the rolling direction. The calculated r-value is confirmed to fit exactly to the measured one from the large-scale production.
基金Authors acknowledge the financial support from the National Natural Science Foundation of China(No.50334010).
文摘Two experiments were carried out on the same compact strip production (CSP) line, which differs in that one of them experienced γ→α→γ thermal history. The differences in microstructure, precipitation, misorientation etc between two experiments were investigated by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron back-scattered diffraction (EBSD) and positron annihilation technique (PAT). The carbon concentration in matrix is more inhomogeneous in the experiment than that with γ→α→γ7 thermal history. The specific precipitation characteristic in the experiment without γ→α→γ thermal history is discussed on the basis of different carbon diffusion behavior and interaction between dislocation and excess carbon.
基金This work was financially supported by the National Natural Science Foundation of China (No.50371009)
文摘Large quantity of fine Ti（C,N） particles, 15-30 nm in size, were observed in low carbon hot strips added to a small amount of Ti and produced by CSP process. The results showed that the precipitation of Ti（C,N） mostly took place during soaking and hot rolling, which is significantly different from that in the conventional production. These fine Ti carbonitride particles could be very effective on the austenite grain refinement by hindering grain growth of recrystallized austenite. Their precipitation behavior was discussed and compared with that of the steels produced in the conventional production.