Al_(2)O_(3)在储能材料中的应用研究进展

Al_(2)O_(3)作为陶瓷材料、催化剂、催化剂载体及研磨磨料等有广泛的应用。因氧化铝具有优良的抗酸碱腐蚀性和力学等性能且热稳定性好、来源丰富,所以近年来逐渐开始应用在储能材料领域,进一步拓展了氧化铝的应用范围。主要针对氧化铝包覆后的二次储能电池正极材料、负极材料,以及改进隔膜的力学性能等方面进行研究。报道了近年来氧化铝在锂离子电池、钠离子电池、锂硫电池、电解液、隔膜方面的应用研究进展。

Modification of Nano-α-Al2O3 and Its Influence on the Surface Properties of Waterborne Polyurethane Resin Composite Passivation Films

Silane coupling agent KH560 was used to modify the surface of nano-α-Al2O3 in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al2O3 was determined by nano-particle size analyzer, and the effects of nano-α-Al2O3 content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al2O3 were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al2O3 dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al2O3 increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al2O3.

Effect of Al2O3 on the Process Performance of ZrO2 Microspheres

Al2O3-ZrO2 microspheres were prepared by internal gelation method.The effects of Al3+on the stability of solution and performance of gel spheres were studied.Al3+had a great influence on the stability of the solutions,and the more of the amount of Al3+,the shorter of the stabilization time.Because Al3+did not copolymerize with Zr4+during the sol-gel transformation,the strength of gel sphere added with Al3+was low and deformed easily as it was squeezed.The results of our experiments well verify Glasser team’s speculation and conclusions.At the same time,based on the experimental results,we prepared Al2O3-ZrO2 composite microspheres with higher content of Al2O3 by controlling the pH of the solution.The change curve of viscosity with time and the stabilization time of the solution with different Al3+dosage were given,which could provide references for industrial mass production.Samples without hydrothermal treatment cracked severely,while the samples hydrothermally treated kept structural integrity with no cracks after calcined.Al2O3-ZrO2 microspheres with no segregation and phase separation were prepared and alumina evenly distributed in the zirconia matrix.When the content of Al2O3 was low,the tetragonal phase was stable.And the cubic phase was obtained when the content of Al2O3 was more.

Al_2O_3/CTS复合微球对Cr(VI)的吸附性能研究

制备了Al_2O_3/CTS复合微球,研究Al_2O_3/CTS复合微球吸附剂对Cr(VI)的吸附性能。并探讨了Al_2O_3/CTS吸附剂对Cr(VI)的吸附机理,获得相关热力学参数,表明Al_2O_3/CTS复合微球吸附剂对Cr(VI)去除效果良好,是一种很有应用前景的水处理剂。

Support Effects on Thiophene Hydrodesulfurization over Co-Mo-Ni/Al_2O_3 and Co-Mo-Ni/TiO_2-Al_2O_3 Catalysts

A carbon-based sulfonated catalyst was prepared by direct sulfonation and carbonization （in moderate conditions：200 ＆#176;C, 12 h） of red liquor solids, a by-product of paper-making process. The prepared sulfonated cata-lyst （SC） had aromatic structure, composed of carbon enriched inner core, and oxygen-containing （SO3H, COOH, OH） groups enriched surface. The SO3H, COOH, OH groups amounted to 0.74 mmol·g^-1, 0.78 mmol·g^-1, 2.18 mmol·g^-1, respectively. The fresh SC showed much higher catalytic activity than that of the traditional solid acid catalysts （strong-acid 732 cation exchange resin, hydrogen type zeolite socony mobile-five （HZSM-5）, sulfated zir-conia） in esterification of oleic acid. SC was deactivated during the reactions, through the mechanisms of leaching of sulfonated species and formation of sulfonate esters. Two regeneration methods were developed, and the catalytic activity can be mostly regenerated by regeneration Method 1 and be fully regenerated by regeneration Method 2, respectively.

Effects of MgO/Al2O3 ratio on viscous behaviors and structures of MgO-Al2O3-TiO2-CaO-SiO2 slag systems with high TiO2 content and low CaO/SiO2 ratio

The effects of MgO/Al2 O3 ratio on the viscous behaviors of MgO-Al2 O3-TiO2-CaO-SiO2 systems were investigated by the rotating cylinder method.Raman spectroscopy was used to analyze the structural characteristics of slag and Factsage 7.0 was adopted to demonstrate the liquidus temperature of slag.The results show that the viscosity and activation energy for viscous flow decrease when the MgO/Al2O3 ratio increases from 0.82 to 1.36.The break point temperature and liquidus temperature of slag initially decrease and subsequently increase.The complex viscous structures are gradually depolymerized to simple structural units.In conclusion,with the increase of MgO/Al2O3 ratio,the degree of polymerization of slag decreases,which improves the fluidity of slag.The variations of liquidus temperature of slag lead to the same changes of break point temperature.

Effects of Cerium Oxide on Ni/Al_2O_3 Catalysts for Decomposition of CH_4 and C_2H_4

Characteristics of carbon deposition of CH 4 and C 2H 4 decomposition over supported Ni and Ni Ce catalysts were studied by using a pulse reaction as well as BET, TPR, XPS and hydrogen chemisorption techniques. It is found that there is a metal semiconductor interaction (MScI) in the Ni Ce catalyst, and the effect of MScI on the carbon deposition of CH 4 decomposition is opposite to that of C 2H 4. A novel model of carbon deposition of CH 4 or C 2H 4 decomposition was proposed.

Facile Preparation of Al2O3 Hollow Microspheres Via a Urea-mediated Precipitation Process

Al2 O3 hollow microspheres without noticeable aggregation have been prepared via a facile templating route with urea-mediated precipitation. The precipitation process is different from the surfaceadsorption method which is confined to the adsorption capacity of the template surface. TEM and SEM images indicate that most of these Al2 O3 hollow microspheres with shell thickness of tens of nanometers and diameters in a narrow range of 100-200 nm consist of a shell of closely packed nanoparticles. The optimal amount of H2 O and EtOH are 40 and 120 m L, respectively. The specific surface area, average pore size and pore volume of the Al2 O3 hollow microspheres（calcinated at 600 ℃） are 328.52 m2/g, 17.496 nm and 1.985 cm3/g, respectively. As the calcination temperature increases from 600 to 1 100 ℃, the phase composition changes from γ-Al2 O3 to θ-Al2 O3 and a-Al2 O3, and the surface morphology appears to change from a relatively rough surface formed by nanoparticles to a smooth surface formed by lamellar, which lead to the closure of pore channels and the reduction of specific surface.

Effects of Y_2O_3 on Thermal Shock of Al_2O_3/TiCN Composites

Thermal shock resistance of Al2O3-TiCN(30%)-Y2O3(0.2%) composite was studied by hot pressing(HP) method at different temperatures. The study shows that thermal shock resistance of the material is determined by its microstructure and reinforced mechanism. According to SEM and calculation of thermal shock, the fractured surface of Al2O3-30%TiCN-0.2%Y2O3 composite is undulate. The residual strength of Al2O3-30%TiCN-0.2%Y2O3 is higher than Al2O3-30%TiCN at 200～800 ℃ after thermal shock. Cracks initiation resistance (R′)and cracks propagation resistance (R″″)of Al2O3-30%TiCN-0.2%Y2O3 composite increases 12% and 5% respectively compared with that of Al2O3-30%TiCN. It matches with experimental results. The addition of Y2O3 forms YAG that inhibits crystal growth, and increases fracture stress, fracture toughness, cracks initiation resistance and cracks propagation resistance. Therefore, thermal shock resistance increases. The fracture work of Al2O3-30%TiCN and Al2O3-30%TiCN-0.2%Y2O3 composites are 132 and 148 J·m-2 respectively.

Effects of Cerium on the Mechanical Properties of the ZA22／Al_2O_3 Composites

ZA22/Al2O3 composites were prepared by means of squeeze casting process. The effects of Ce on the ultimate tensile strength (UTS), impact toughness, and hardness of the composites were studied. The results show that both the UTS and the hardness are improved and the impact toughness is decreased with the increase of the volume fraction of fibers (Vf). After Ce is added ,UTS (Vf>15%) and the hardness are improved at room temperature because of the modification of Ce, but the impact toughness and UTS at elevated temperature are lowered.The filtered action of the fiber preform results in that the influence of the amount of Ce added from 0. 1 wt% to 0. 5 wt% on the mechanical properties of the composites can be ignored.

Preparation of Calcium Cross-linked Nano-Fe3O4 Modified Zeolite Microspheres for Cu^2+ Adsorption from Wastewater

Artificial zeolite was modified by nano-Fe3O4 for development of functional adsorbents.Subsequently,adsorbents such as calcium cross-linked nano-Fe3O4 microspheres (Ca-MS),calcium cross-linked nano-Fe3O4 modified zeolite microspheres (Ca-MZS) and iron cross-linked nano-Fe3O4 modified zeolite microspheres (Fe-MZS) were prepared and compared for their adsorption performance.The effects of adsorbent dosage,solution pH,initial concentration and ion content on the removal of Cu^2+ from wastewater are investigated,and the adsorption kinetics and isotherms for the adsorbent materials were analyzed.The experimental results indicate that for the initial concentration of Cu^2+ of 30 mg/L,the adsorption is noted to be most stable.The optimal initial pH for adsorbing Cu^2+ is observed to be 5.5.At an optimal dosage of Ca-MZS of 900 mg/L,the adsorption capacity is measured to be 28.25 mg/g,along with the removal rate of 72.49%.The addition of Na+ and K+ affects the adsorption of Cu^2+.For the Na^+ and K^+ concentration of 0.2 mmol/L,the Cu^2+ removal rate by Ca-MZS drops to 11.94% and 22.12%,respectively.As compared with the adsorbents such as Natural Zeolite (NZ),Ca-MS and Fe-MZS,Ca-MZS demonstrates the best removal effect in solution,where the removal rate reaches 84.27%,with the maximum adsorption capacity of 28.09 mg/g.The Cu^2+ adsorption kinetics of Ca-MZS is observed to follow the Elovich kinetic model,with the adsorption isotherm data fitting the Freundlich isotherm model by using the non-linear method.

Optimization and Effects of Catalytic Ozonation of Actual Phenolic Wastewater by CuO/Al2O3

In order to improve the ability of ozone to catalyze the degradation of phenolic pollutants in wastewater,the CuO/Al2O3 catalysts was prepared by the impregnation precipitation method and an ozone catalytic oxidation system was constructed.The actual phenolic sewage was used as the treatment object.And the reaction conditions of the system were optimized,and the treatment effect was determined,while the non-catalytic system was used as a control group.At the same time,the influence of salt and ammonia nitrogen related water quality on the system was studied.The optimal reaction conditions for the treatment of phenolic wastewater covered:a catalyst dosage of 30 g/L,an ozone flow rate of 0.3 m3/h,a pH value of 8.80,and a reaction time of 15 minutes.Under these conditions,the phenol and COD removal rates of the system reached 98.7%and 49.4%,respectively,which were by 31.3 percentage points and 16.2 percentage points higher than that of the ozonation system alone.The salt and ammonia nitrogen in the sewage can reduce the oxidation effect of the system.When the salinity reached 10%and the ammonia nitrogen content reached 13 000 mg/L,the removal rate of phenol could be reduced by about 20%.The results of this paper have a reference value for phenol wastewater treatment engineering.

Simulation of the effects of different substrates, temperature,and substrate roughness on the mechanical properties of Al_2O_3 coating as tritium penetration barrier

Residual thermal stress in the system is a serious problem that affects the application of tritium permeation barrier coatings in fusion reactors. The stress not only determines the adhesion between coating and substrate, but also changes the properties of the material. In this study,finite element analysis was used to investigate the relationship between the residual thermal stress and the mechanical properties of Al_2O_3 tritium penetration barrier systems. Moreover, the residual thermal stress influenced by factors such as different substrates, temperature, and substrate roughness was also analyzed. The calculation showed that the hardness and elastic modulus increased with increasing compressive stress. However, the hardness and elastic modulus decreased with increasing tensile stress. The systems composed of Al_2O_3 coatings and different substrates exhibited different trends in mechanical properties. As the temperature increased, the hardness and the elastic modulus increased in an Al_2O_3/316 L stainless steel system; the trend was opposite in an Al_2O_3/Si system.Apart from this, the roughness of the substrate surface in the system could magnify the change in hardness and elastic modulus of the coating. Results showed that all these factors led to variation in the mechanical properties of Al_2O_3 tritium permeation barrier systems. Thus, thedetailed reasons for the changes in mechanical properties of these materials need to be analyzed.

Total Ionization Dose Effects on Charge Storage Capability of Al2O3/HfO2/Al2O3-Based Charge Trapping Memory Cell

Because of the discrete charge storage mechanism, charge trapping memory（CTM） technique is a good candidate for aerospace and military missions. The total ionization dose（TID） effects on CTM cells with Al2O3/HfO2/Al2O3（AHA） high-k gate stack structure under in-situ 10 keV x-rays are studied. The C-V characteristics at different radiation doses demonstrate that charge stored in the device continues to be leaked away during the irradiation,thereby inducing the shift of flat band voltage（V（fb））. The dc memory window shows insignificant changes, suggesting the existence of good P/E ability. Furthermore, the physical mechanisms of TID induced radiation damages in AHA-based CTM are analyzed.

Effects of MgO content and CaO/Al_2O_3 ratio on surface tension of calcium aluminate refining slag

Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.

Effects of temperature and initial molar ratio of Na_2O to Al_2O_3 on agglomeration of fine Al(OH)_3 seed in synthetic Bayer solution

Fine Al（OH）3 crystals were aggregated from supersaturated aluminate solution in the batch reaction tanks. By means of laser particle size analyzer and scanning electron microscopy, the influences of temperature and initial molar ratio of Na2O to Al2O3 （aK） on agglomeration of fine seed in Bayer process were investigated. The results show that agglomeration is almost finished in 8 h, and seeds with size less than 2 μm are easily aggregated together, and almost disappear in 8 h under the optimal process conditions. In the aluminate solution with the same moderate initial aK, when the reaction temperature reaches 75 ℃, the secondary nucleation does not occur, and the effect of agglomeration is better. And at the same reaction temperature, when the initial aK is 1.62, the initial supersaturation of aluminate solution is moderate, the binders on the surfaces of the seed are enough to maintain the agglomeration process, and the agglomeration degree is better. From SEM images, agglomeration mainly occurs in the fine particles, the combinations among the fine particles are loose and the new formed coarse crystal shapes are irregular.

Morphology and Frictional Characteristics Under Electrical Currents of Al_2O_3/Cu Composites Prepared by Internal Oxidation

Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.

纯铜组元对Al_(2)O_(3)弥散强化铜变形性能的影响

为改善Al_(2)O_(3)弥散强化铜的变形性能,通过向弥散强化铜中加入软质相纯铜组元,研究纯铜组元对弥散强化铜烧结坯变形性能的影响。对弥散铜烧结坯进行热压缩变形实验,获得了其不同热变形条件下的真应力应变曲线,建立了基于双曲正弦本构关系Arrhenius流变应力模型的本构方程,并计算获得热激活能值Q与应变速率敏感系数值m;对热挤压试样,进行室温性能检测和微观组织表征。结果表明:加入纯铜组元后,弥散铜烧结坯应力应变曲线峰值应力下降,曲线走势波动减弱,变形试样缺陷减少,热激活能Q降低,变形难度下降。应变速率较低时,纯铜组元的加入使得m值增加,弥散强化铜的塑性变好;应变速率较高时,纯铜组元的加入加剧基体软硬相不协调变形,m值降低,塑性变差。纯铜组元的加入使热挤压弥散铜的强化相浓度降低,硬度下降,导电率提升,晶粒变大。

CTS/Al2O3微球对酸性红的吸附性能研究

制备CTS/Al2O3微球,研究CTS/Al2O3微球对酸性红的吸附性能;探讨CTS/Al2O3微球对酸性红的吸附机理,获得相关动力学参数。结果表明:CTS/Al2O3微球吸附剂对酸性红去除效果良好,是一种很有应用前景的染料废水处理剂。

Interface characteristics of Al_2O_3－13%TiO_2 ceramic coatings prepared by laser cladding

Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.