Removal of SO2 and NOx by pulsed corona combined with in situ alkali absorption was experimentally investigated.In the reactor,a plate-wire-plate combination is devised for generating pulsed corona and then alkaline a...Removal of SO2 and NOx by pulsed corona combined with in situ alkali absorption was experimentally investigated.In the reactor,a plate-wire-plate combination is devised for generating pulsed corona and then alkaline absorbent slurries were introduced into the reactor by a continuous band conveying system to capture the gaseous reaction products.It was found that both SO2 and NO could be removed by corona combined with in situ alkali absorption.The removal of SO2 increased to 75%with the corona discharge,compared with 60%removal only with Ca(OH)2 absorption.About 40%removal of NO was reached by pulsed corona combined with in situ Ca(OH)2 absorption.It was found that SO2 and NO in the gas stream are oxidized to SO3 and NO2 by pulsed corona respectively,and then absorbed by the alkali in the reactor.The removals of SO2 as well as NO were higher with Ca(OH)2 as the absorbent,compared with using CaCO3 or ZnO.展开更多
Six additives,i.e.,limestone,lime,magnesite,magnesia,dolomite and light-burned-dolomite,were added for investigating their influences on the pellet quality.For green balls,adding lime and light-burned-dolomite makes t...Six additives,i.e.,limestone,lime,magnesite,magnesia,dolomite and light-burned-dolomite,were added for investigating their influences on the pellet quality.For green balls,adding lime and light-burned-dolomite makes the wet drop strength decrease firstly,and then increase with further increase of additive dosage.Ca(OH)2 affects the bentonite properties at the beginning,but the binding property of Ca(OH)2 will be main when the dosage is higher.The other four additives decrease the drop strength for their disadvantageous physical properties.For preheated pellets,no mater what kind of additive is added,the compressive strength will be decreased because of unmineralized additives.For roasted pellets,calcium additives can form binding phase of calcium-ferrite,and suitable liquid phase will improve recrystallization of hematite,but excessive liquid will destroy the structure of pellets,so the compressive strength of pellet increases firstly and then drops.When adding magnesium additives,the strength will be decreased because of the oxidation of magnetite retarded by MgO.展开更多
基金Supported by the Science and Technology Development Project of Zhejiang Province(2007C13085)Hangzhou City(20070733B28)
文摘Removal of SO2 and NOx by pulsed corona combined with in situ alkali absorption was experimentally investigated.In the reactor,a plate-wire-plate combination is devised for generating pulsed corona and then alkaline absorbent slurries were introduced into the reactor by a continuous band conveying system to capture the gaseous reaction products.It was found that both SO2 and NO could be removed by corona combined with in situ alkali absorption.The removal of SO2 increased to 75%with the corona discharge,compared with 60%removal only with Ca(OH)2 absorption.About 40%removal of NO was reached by pulsed corona combined with in situ Ca(OH)2 absorption.It was found that SO2 and NO in the gas stream are oxidized to SO3 and NO2 by pulsed corona respectively,and then absorbed by the alkali in the reactor.The removals of SO2 as well as NO were higher with Ca(OH)2 as the absorbent,compared with using CaCO3 or ZnO.
基金Project(2008BAB32B06) supported by the Key Projects in the National Science and Technology Pillar Program during the 11th Five-year Plan PeriodProject(2009ybfz20) supported by the Program for Excellent Doctor’s Degree Paper in Central South University,ChinaProject(1343/74333001114) supported by the Postgraduate’s Paper Innovation Fund of Hunan Province,China
文摘Six additives,i.e.,limestone,lime,magnesite,magnesia,dolomite and light-burned-dolomite,were added for investigating their influences on the pellet quality.For green balls,adding lime and light-burned-dolomite makes the wet drop strength decrease firstly,and then increase with further increase of additive dosage.Ca(OH)2 affects the bentonite properties at the beginning,but the binding property of Ca(OH)2 will be main when the dosage is higher.The other four additives decrease the drop strength for their disadvantageous physical properties.For preheated pellets,no mater what kind of additive is added,the compressive strength will be decreased because of unmineralized additives.For roasted pellets,calcium additives can form binding phase of calcium-ferrite,and suitable liquid phase will improve recrystallization of hematite,but excessive liquid will destroy the structure of pellets,so the compressive strength of pellet increases firstly and then drops.When adding magnesium additives,the strength will be decreased because of the oxidation of magnetite retarded by MgO.