Direct electrodeposition of quarternary Mg-Zn-Li-Ca alloys on a molybdenum electrode from LiCl-KCl-MgCl2-ZnCl2-CaCl2 melts at 943 K was investigated.Cyclic voltammograms（CVs） show that the deposition potential of Li...Direct electrodeposition of quarternary Mg-Zn-Li-Ca alloys on a molybdenum electrode from LiCl-KCl-MgCl2-ZnCl2-CaCl2 melts at 943 K was investigated.Cyclic voltammograms（CVs） show that the deposition potential of Li shifts in a positive direction after adding MgCl2,ZnCl2 and CaCl2.Chronopotentiometric measurements indicate that the codepositon of Mg,Li,Zn,and Ca occurs at current densities lower than-1.55 A/cm2.X-ray diffraction（XRD） indicates that Mg-Zn-Li-Ca alloys with different phases were prepared via galvanostatic electrolysis.The microstructures of typical phase of Mg-Zn-Li-Ca alloys were characterized by optical microscopy（OM） and scanning electron microscopy（SEM）.The analysis of energy dispersive spectrometry（EDS） shows that elements of Mg and Ca distribute homogeneously in the Mg-Zn-Li-Ca alloy.However,element Zn mainly locates at the edges of the domain.展开更多
基金Project(2011AA03A409) supported by the High-tech Research and Development Program of ChinaProjects(21103033,21101040, 21173060,91226201) supported by the National Natural Science Foundation of China+1 种基金Project(HEUCF20130012) supported by the Fundamental Research Funds for the Central Universities,ChinaProject(1253G016) supported by the Foundation for University Key Teacher of Heilongjiang Province of China
文摘Direct electrodeposition of quarternary Mg-Zn-Li-Ca alloys on a molybdenum electrode from LiCl-KCl-MgCl2-ZnCl2-CaCl2 melts at 943 K was investigated.Cyclic voltammograms（CVs） show that the deposition potential of Li shifts in a positive direction after adding MgCl2,ZnCl2 and CaCl2.Chronopotentiometric measurements indicate that the codepositon of Mg,Li,Zn,and Ca occurs at current densities lower than-1.55 A/cm2.X-ray diffraction（XRD） indicates that Mg-Zn-Li-Ca alloys with different phases were prepared via galvanostatic electrolysis.The microstructures of typical phase of Mg-Zn-Li-Ca alloys were characterized by optical microscopy（OM） and scanning electron microscopy（SEM）.The analysis of energy dispersive spectrometry（EDS） shows that elements of Mg and Ca distribute homogeneously in the Mg-Zn-Li-Ca alloy.However,element Zn mainly locates at the edges of the domain.