The aims of this study are to investigate the effects of Nd addition in the Mg-Al-Ca alloys on microstructure and mechanical properties.Microstructure of as-cast Mg-5Al-3Ca alloy containing Nd consists ofα-Mg matrix,...The aims of this study are to investigate the effects of Nd addition in the Mg-Al-Ca alloys on microstructure and mechanical properties.Microstructure of as-cast Mg-5Al-3Ca alloy containing Nd consists ofα-Mg matrix, eutectic phase and Al-Nd rich intermetallic compound.As Nd addition was increased,α-Mg matrix morphology was changed from dendritic to equiaxed grains and average value of grain size was decreased.Nd addition to Mg-5Al-3Ca based alloys resulted in the formation of Al-Nd rich intermetallic compounds at grain boundary andα-Mg matrix grains.And these Al-Nd rich intermetallic compounds were dispersed homogeneously.In these alloys,two kinds of eutectic phases were observed,i.e.coarse irregular-shape structure at grain boundary and fine needle-shape structure in theα-Mg matrix grain.It is found that the ultimate strength showed the maximum value of 271 MPa at Mg-5Al-3Ca-2Nd alloy and elongation was decreased as the addition of Nd was increased.展开更多
Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re...Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.展开更多
文摘The aims of this study are to investigate the effects of Nd addition in the Mg-Al-Ca alloys on microstructure and mechanical properties.Microstructure of as-cast Mg-5Al-3Ca alloy containing Nd consists ofα-Mg matrix, eutectic phase and Al-Nd rich intermetallic compound.As Nd addition was increased,α-Mg matrix morphology was changed from dendritic to equiaxed grains and average value of grain size was decreased.Nd addition to Mg-5Al-3Ca based alloys resulted in the formation of Al-Nd rich intermetallic compounds at grain boundary andα-Mg matrix grains.And these Al-Nd rich intermetallic compounds were dispersed homogeneously.In these alloys,two kinds of eutectic phases were observed,i.e.coarse irregular-shape structure at grain boundary and fine needle-shape structure in theα-Mg matrix grain.It is found that the ultimate strength showed the maximum value of 271 MPa at Mg-5Al-3Ca-2Nd alloy and elongation was decreased as the addition of Nd was increased.
文摘Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.
