Nominal composition of Ca1-xZnxTiO3 ： 0. 002Pr^3 ＋ （x = 0. 000 - 0. 200） phosphors were prepared by conventional solid reaction route. XRD and PL measurements were used to investigate the solid-solution structure ...Nominal composition of Ca1-xZnxTiO3 ： 0. 002Pr^3 ＋ （x = 0. 000 - 0. 200） phosphors were prepared by conventional solid reaction route. XRD and PL measurements were used to investigate the solid-solution structure and luminescence properties of Zn-doped Ca1-xZnxTiO3：0.002Pr^3＋ phosphors. The effect of solid-solution structure formed by substitution between Ca^2 ＋ and Zn^2＋ ions on the luminescent properties was analyzed. The results reveal that, with the increase of Zn substitution content below 0.010, lattice parameters and the intensity of excitation peak at both 260 and 330 nm as well as the corresponding 610 nm emission intensity are monotonously decreased quickly in a similar tendency. Also, the evolution of luminescence intensity and crystal cell parameters against Zn doping concentration are in good agreement. Above results are closely related with the structure change within Ca1- xZnxTiO3：0.002Pr^3＋ solid-solution phase formed by the Zn ions substitution for the Ca sites. Present study reveals that the solid-solution structure formed by substitution between Ca^2＋ and Zn^2＋ ions has significant effect on the luminescence properties of single phase Ca1-xZnxTiO3：0.002Pr^3＋ phosphors.展开更多
The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with r...The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.展开更多
文摘Nominal composition of Ca1-xZnxTiO3 ： 0. 002Pr^3 ＋ （x = 0. 000 - 0. 200） phosphors were prepared by conventional solid reaction route. XRD and PL measurements were used to investigate the solid-solution structure and luminescence properties of Zn-doped Ca1-xZnxTiO3：0.002Pr^3＋ phosphors. The effect of solid-solution structure formed by substitution between Ca^2 ＋ and Zn^2＋ ions on the luminescent properties was analyzed. The results reveal that, with the increase of Zn substitution content below 0.010, lattice parameters and the intensity of excitation peak at both 260 and 330 nm as well as the corresponding 610 nm emission intensity are monotonously decreased quickly in a similar tendency. Also, the evolution of luminescence intensity and crystal cell parameters against Zn doping concentration are in good agreement. Above results are closely related with the structure change within Ca1- xZnxTiO3：0.002Pr^3＋ solid-solution phase formed by the Zn ions substitution for the Ca sites. Present study reveals that the solid-solution structure formed by substitution between Ca^2＋ and Zn^2＋ ions has significant effect on the luminescence properties of single phase Ca1-xZnxTiO3：0.002Pr^3＋ phosphors.
基金the National Natural Science Foundation of China (No. 51602126)the National Key Research and Development Plan of China (No. 2016YFB0303505)+1 种基金China and University of Jinan Postdoctoral Science Foundation (No. 2017M622118 and XBH1716)the 111 Project of International Corporation on Advanced Cement-based Materials (D17001).
文摘The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.