The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with r...The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.展开更多
采用CaxSi合金前驱物和Eu B6常压氮化制备了Ca Al Si N3∶Eu2+氮化物红色荧光粉。研究了不同烧结温度、添加助熔剂及二次烧结对发光性能的影响。通过扫描电子显微镜(SEM)、X射线衍射(XRD)、荧光分光光度计对发光材料的形貌、晶体结构、...采用CaxSi合金前驱物和Eu B6常压氮化制备了Ca Al Si N3∶Eu2+氮化物红色荧光粉。研究了不同烧结温度、添加助熔剂及二次烧结对发光性能的影响。通过扫描电子显微镜(SEM)、X射线衍射(XRD)、荧光分光光度计对发光材料的形貌、晶体结构、发光性能与热稳定性进行了研究。分析结果表明:通过合金前驱物常压氮化法得到的氮化物荧光粉具有Ca Al Si N3结构,空间群为Cmc21。Ca Al Si N3∶Eu2+红色荧光粉的最佳烧结温度为1 550℃。添加质量分数为6%的Sr F2助熔剂后,荧光粉发光强度的提升效果最好。添加6%Sr F2助熔剂及二次烧结后得到的荧光粉的晶粒生长更加完整,颗粒度明显改善,发射光谱的相对强度也明显提高,比未加助熔剂单次烧结的荧光粉相对强度提高了近一倍。将发射峰位在640 nm的Ca0.98Al Si N3∶0.02Eu2+红色荧光粉应用在白光LED的封装中,获得了色温为3 109 K、显色指数为92.5以及色温为4 989K、显色指数为95.8的高显色白光LED,说明本文合成的氮化物红色荧光粉可以实现暖白光和正白光高显色的白LED发光器件。展开更多
Synthesis of oxynitride solid solutions CaAl4-xSixO7-xNx:Eu2+ (x = 0 - 4) was attempted by the solid state reaction (SSR) methods using Si3N4 and AlN as nitrogen sources. The Ca3Al8Si4O17N4 (x = 4/3) sample with the h...Synthesis of oxynitride solid solutions CaAl4-xSixO7-xNx:Eu2+ (x = 0 - 4) was attempted by the solid state reaction (SSR) methods using Si3N4 and AlN as nitrogen sources. The Ca3Al8Si4O17N4 (x = 4/3) sample with the high phase purity was obtained when AlN was used as a nitrogen source whereas the sample synthesized using Si3N4 as another nitrogen source contained a Ca2Al2SiO7 impurity. Thus, it was revealed that AlN was a preferable nitrogen source for the synthesis of Ca3Al8Si4O17N4 by the SSR method. The solid solutions around x = 4/3 activated with Eu2+ exhibited bluish-green luminescence with emission maxima at 480 nm by the excitation at 250 - 450 nm. Thus, the CaAl4-xSixO7-xNx: Eu2+ solid solutions especially for Ca3Al8Si4O17N4:Eu2+ (x = 4/3) were developed as novel展开更多
基金the National Natural Science Foundation of China (No. 51602126)the National Key Research and Development Plan of China (No. 2016YFB0303505)+1 种基金China and University of Jinan Postdoctoral Science Foundation (No. 2017M622118 and XBH1716)the 111 Project of International Corporation on Advanced Cement-based Materials (D17001).
文摘The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.
文摘采用CaxSi合金前驱物和Eu B6常压氮化制备了Ca Al Si N3∶Eu2+氮化物红色荧光粉。研究了不同烧结温度、添加助熔剂及二次烧结对发光性能的影响。通过扫描电子显微镜(SEM)、X射线衍射(XRD)、荧光分光光度计对发光材料的形貌、晶体结构、发光性能与热稳定性进行了研究。分析结果表明:通过合金前驱物常压氮化法得到的氮化物荧光粉具有Ca Al Si N3结构,空间群为Cmc21。Ca Al Si N3∶Eu2+红色荧光粉的最佳烧结温度为1 550℃。添加质量分数为6%的Sr F2助熔剂后,荧光粉发光强度的提升效果最好。添加6%Sr F2助熔剂及二次烧结后得到的荧光粉的晶粒生长更加完整,颗粒度明显改善,发射光谱的相对强度也明显提高,比未加助熔剂单次烧结的荧光粉相对强度提高了近一倍。将发射峰位在640 nm的Ca0.98Al Si N3∶0.02Eu2+红色荧光粉应用在白光LED的封装中,获得了色温为3 109 K、显色指数为92.5以及色温为4 989K、显色指数为95.8的高显色白光LED,说明本文合成的氮化物红色荧光粉可以实现暖白光和正白光高显色的白LED发光器件。
文摘Synthesis of oxynitride solid solutions CaAl4-xSixO7-xNx:Eu2+ (x = 0 - 4) was attempted by the solid state reaction (SSR) methods using Si3N4 and AlN as nitrogen sources. The Ca3Al8Si4O17N4 (x = 4/3) sample with the high phase purity was obtained when AlN was used as a nitrogen source whereas the sample synthesized using Si3N4 as another nitrogen source contained a Ca2Al2SiO7 impurity. Thus, it was revealed that AlN was a preferable nitrogen source for the synthesis of Ca3Al8Si4O17N4 by the SSR method. The solid solutions around x = 4/3 activated with Eu2+ exhibited bluish-green luminescence with emission maxima at 480 nm by the excitation at 250 - 450 nm. Thus, the CaAl4-xSixO7-xNx: Eu2+ solid solutions especially for Ca3Al8Si4O17N4:Eu2+ (x = 4/3) were developed as novel