氟钙钛型自保护药芯焊丝降氢机理的研究

探讨氟化物、大理石、高价氧化物和稀土氧化物在氟钙钛渣系自保护药芯焊丝中的降氢机理。结果表明，适当提高药芯中多种氟化物、大理石及稀土氧化物含量，将有利于降低焊缝中扩散氢含量。

高韧性自保护药芯焊丝

采用正交设计方法。研制出一种新型氟钙钛渣系（ＧａＦ_２－ＴｉＯ_２－ＭｇＯ）的自保护药芯焊丝，其焊接工艺性能良好，烟雾少，并且熔敷金属组织均匀、细小，塑性和低温韧性高，是与５５０ＭＰａ级低合金高强钢相匹配的一种高效焊接材料，适于野外焊接重要结构。

氟化物对自保护药芯焊丝的影响

通过改变自保护药芯焊丝药芯中氟化物的种类及加入量,系统的研究了氟化物对碱性熔渣的熔点、粘度、表面张力、流动性及其电弧稳定性的影响,采用排液法进行测氢,研究分析了氟化物对焊缝中扩散氢的影响。

Investigation on mechanism of fixing nitrogen in self-shielded flux cored arc welding

Prevention of nitrogen porosity in weld metal deposited with self-shielded flux cored wire with CaF2-TiO2-MgO slag system can be accomplished by using a 'killing agent' such as titanium to react with nitrogen dissolved in the weld metal. The amount of titanium needed to prevent porosity is calculated thermodynamically for various dissolved nitrogen levels. Experimental flux cored wires are used to verify the thermodynamic model. It is concluded that approximately 0.11 wt% titanium in the weld deposit is need to prevent nitrogen porosity when welding without externally applied shielding.

自保护药芯焊丝中固氮机制的研究

在ＣａＦ２－ＴｉＯ２－ＭｇＯ渣系自保护药芯焊丝缝中，可采用固氮元素钛达到消除氮气孔的目的，在不同氮含量水平下，通过热力学方法计算防止氮气孔的最低钛量结果表明：大致０．１１Ｗｔ％的钛量即可防止焊缝中出现氮气孔．