The microstructure of CaO-P_2O_5-SiO_2-MgO-F^- glass-ceramics duringcrystallization were investigated and the crystallized phases were identified with DTA (DifferentialThermal Analysis), SEM (Scanning Electron Microsc...The microstructure of CaO-P_2O_5-SiO_2-MgO-F^- glass-ceramics duringcrystallization were investigated and the crystallized phases were identified with DTA (DifferentialThermal Analysis), SEM (Scanning Electron Microscope) and XRD (X- ray Diffraction) techniques. Themechanical properties such as bending strength and fracture toughness, as well as their changes withadvancing crystallization were determined. The results show that the changes of the mechanicalproperties are correlated with the microstructures. The sample heated up to 810 deg C and soaked for4 h has smaller crystalline size and less volum fraction of fluorophlogopite, so it has higherbending strength (about 190 MPa), and higher crack toughness (about 2.63 MPa centre dot m^1/2).展开更多
The crystallization behavior and mechanical properties of CaO-Al2O3-SiO2 (CAS) system glass-ceramics with addition of Y2O3 were investigated. The optimal sintering temperatures of all heat-treated glasses were altered...The crystallization behavior and mechanical properties of CaO-Al2O3-SiO2 (CAS) system glass-ceramics with addition of Y2O3 were investigated. The optimal sintering temperatures of all heat-treated glasses were altered and the crystallization was accelerated with Y2O3 addition, and only wollastonite as a main crystalline phase was precipitated. The volume fraction of crystalline phase and density were increased with Y2O3 addition. The results suggest that the CAS glass-ceramics would get the lowest sintering temperature and optimal microstructure with the addition of Y2O3 by 3.25 %. The bending strength has a maximum due to the oriented and interlocked wollastonite crystal, which causes crack divert or blunts to limit the further development of the flaw size and increases the surface energy of fracture.展开更多
ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient t...ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient temperature furnace, DTA and XRD. Then, sintering process of the glass-ceramics was investigated by testing sintering shrinkage, dielectric constant and loss. The experimental results shows that the glass-ceramics doped with nucleating additives represents higher crystallization, with ZrO2 as an exceptional effective dopant to promote the precipitation of wollastonite crystal. Finally, ZrO2 containing glass-ceramics was chosen to study the influence of sintering temperature and soaking time with the help of X-ray diffraction analysis and density measurement. The glass-ceramics can be well consolidated at 850 ℃ for 10 min, with low dielectric constant （5.87） and loss （3.21×10^-4）, which is desirable for LTCC application.展开更多
The effect of Cr2O3 on the nucleation and crystallization of Na2O-CaO-Al2O3-SiO2-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specro...The effect of Cr2O3 on the nucleation and crystallization of Na2O-CaO-Al2O3-SiO2-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1 .5 % (mass fraction) Cr2O3 can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr2O4] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO3 grew epitaxially.展开更多
文摘The microstructure of CaO-P_2O_5-SiO_2-MgO-F^- glass-ceramics duringcrystallization were investigated and the crystallized phases were identified with DTA (DifferentialThermal Analysis), SEM (Scanning Electron Microscope) and XRD (X- ray Diffraction) techniques. Themechanical properties such as bending strength and fracture toughness, as well as their changes withadvancing crystallization were determined. The results show that the changes of the mechanicalproperties are correlated with the microstructures. The sample heated up to 810 deg C and soaked for4 h has smaller crystalline size and less volum fraction of fluorophlogopite, so it has higherbending strength (about 190 MPa), and higher crack toughness (about 2.63 MPa centre dot m^1/2).
文摘The crystallization behavior and mechanical properties of CaO-Al2O3-SiO2 (CAS) system glass-ceramics with addition of Y2O3 were investigated. The optimal sintering temperatures of all heat-treated glasses were altered and the crystallization was accelerated with Y2O3 addition, and only wollastonite as a main crystalline phase was precipitated. The volume fraction of crystalline phase and density were increased with Y2O3 addition. The results suggest that the CAS glass-ceramics would get the lowest sintering temperature and optimal microstructure with the addition of Y2O3 by 3.25 %. The bending strength has a maximum due to the oriented and interlocked wollastonite crystal, which causes crack divert or blunts to limit the further development of the flaw size and increases the surface energy of fracture.
基金Funded by the Shanghai Leading Academic Discipline Project (B502)Shanghai Key Laboratory Project (08DZ2230500)
文摘ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient temperature furnace, DTA and XRD. Then, sintering process of the glass-ceramics was investigated by testing sintering shrinkage, dielectric constant and loss. The experimental results shows that the glass-ceramics doped with nucleating additives represents higher crystallization, with ZrO2 as an exceptional effective dopant to promote the precipitation of wollastonite crystal. Finally, ZrO2 containing glass-ceramics was chosen to study the influence of sintering temperature and soaking time with the help of X-ray diffraction analysis and density measurement. The glass-ceramics can be well consolidated at 850 ℃ for 10 min, with low dielectric constant （5.87） and loss （3.21×10^-4）, which is desirable for LTCC application.
文摘The effect of Cr2O3 on the nucleation and crystallization of Na2O-CaO-Al2O3-SiO2-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1 .5 % (mass fraction) Cr2O3 can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr2O4] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO3 grew epitaxially.