Effects of MgO content and CaO/Al_2O_3 ratio on surface tension of calcium aluminate refining slag

Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.

温度和气氛对CaO-SiO2-Al2O3-MgO-FetO渣系FetO活度的影响

采用Mo|Mo+MoO2|ZrO2(MgO)|Fe+(FetO)+Ag|Fe固体电解质电池测定不同温度和气氛条件下定组成CaO-SiO2-Al2O3-MgO-FetO五元渣系的FetO活度。结果表明,当Ar作为保护气氛时,温度由1 673 K升高到1 785 K,炉渣的FetO活度变化不明显。当气氛中CO,CO2和Ar组成固定时,炉渣的FetO活度随温度的升高而增大。温度为1 673 K时,炉渣的FetO活度随着气氛中CO2/CO的增加而增大。温度和气氛对渣系FetO活度的影响均通过体系的O2分压实现。

炉渣组分对CaO-Al_2O_3-SiO_2-TiO_2-MgO-Na_2O渣系与铁液间硫分配比的影响

针对高碱度高氧化铝的Ca O-Al_2O_3-Si O_2-Ti O_2-Mg O-Na_2O六元渣系,通过在1 773 K温度下测定其与铁液间的硫分配比,研究该渣系的脱硫性能.利用偏最小二乘法回归分析,建立了可较好预测硫分配比的回归方程,利用回归方程分析了炉渣碱度(mCa O/mSi O_2)、Mg O、Ti O_2、Al_2O_3以及Na_2O对硫分配比的影响.结果表明,当炉渣碱度大于2.9时,炉渣硫分配比均在140以上,表明该渣系具有较强的脱硫能力.在实验范围内,硫分配比随炉渣碱度的增加而提高.当碱度一定时,Mg O对硫分配比的影响不大,Ti O_2、Al_2O_3均使硫分配比降低,其中Al_2O_3降低硫分配比较为明显.硫分配比随Na_2O增加而增加,少量的Na_2O即可明显提高炉渣的脱硫能力.

CaO-MgO比例对中高铝瓷球性能的影响

保持Al2O3和SiO2含量不变,变化CaO和MgO的比例制造氧化铝瓷球。研究了不同CaO、MgO含量对瓷球密度、烧结以及耐磨性的影响。结果表明,随着CaO含量降低、MgO含量的升高,瓷球烧成温度升高,密度相近,但磨耗降低。

CaO/MgO比对固硫剂固硫率的影响

通过对不同燃烧温度和固硫剂添加量下CaO/MgO之比与固硫率之间关系的研究发现,燃烧温度相同而CaO/MgO之比不同时,固硫率不同;燃烧温度不同时,最佳CaO/MgO之比也不同,而且随温度升高而向CaO增多、MgO减少的方向变化。最佳固硫温度以及固硫剂添加量均和CaO/MgO之比与固硫率之间的关系无关。

CaO/MgO对花岗岩尾矿微晶玻璃物相和性能的影响

以花岗岩尾矿为主要原料(掺入质量分数:56%),TiO_(2)为主晶核剂,适量Na_(2)SiF_(6)为助熔剂和晶核剂,添加部分辅助原料,采用整体析晶法,制备了R_(2)O-CaO-MgO-Al_(2)O_(3)-SiO_(2)系花岗岩尾矿建筑微晶玻璃。研究了CaO/MgO质量比对微晶玻璃析晶能力、物相、微观结构及性能的影响。结果表明:CaO/MgO质量比的增加有利于增强基础玻璃的析晶能力,当CaO/MgO质量比≤0.88时,微晶玻璃的主晶相为钙长石和角闪石,当CaO/MgO质量比>0.88时,主晶相转变为钙长石,且钙长石衍射峰的强度随着CaO/MgO质量比的增加而增大;随CaO/MgO质量比的增加,晶体数量逐渐增多,晶粒尺寸增大;微晶玻璃的体积密度和显微硬度随CaO/MgO质量比的增加呈先增大后减小的趋势,当CaO/MgO质量比为0.57时,体积密度达到最大值2.7525 g/cm^(3),当CaO/MgO质量比为0.71时,显微硬度达到最大值为8.6 GPa。

CaO/MgO摩尔比对无光釉结构与性能的影响

以天然的矿物原料,采用传统的制备工艺,通过改变配方中烧滑石和方解石的相对含量,制备出了1200℃烧成效果良好的无光釉。并借助SEM、XRD和光泽度仪等测试手段研究了CaO/MgO摩尔比对无光釉结构和光泽度的影响,并探讨了其无光机理。结果表明:CaO/MgO摩尔比对钙镁复合无光釉的结构和性能有较大影响,随着CaO/MgO摩尔比的增大,釉中晶体尺寸逐渐增大,并由堇青石和顽火辉石向透辉石转变,当CaO/MgO摩尔比增大至2. 28时,主晶相变为30~40μm的钙长石。当CaO/MgO摩尔比为1. 06时获得的无光釉综合效果最优,其光泽度为16,该釉层中含有大量的直径2~3μm,长度10~20μm的棒状和叶片状透辉石晶体。晶体尺寸和晶体含量是影响无光釉效果的主要因素,晶体尺寸过小或晶体含量过少均不利于良好无光釉的形成。

CaO-MgO-SiO_2-Al_2O_3类夹杂物塑性化对帘线钢加工断丝率的影响

通过分析70 t转炉流程和180 t转炉流程生产的LX72A帘线钢合股断丝率,得出中心偏析相同的条件下,当钢中脆性夹杂物比例由90.7%降至20.5%,也就是塑性夹杂物的比例由9.3%提高79.5%时,平均盘条断丝率由4.20次/t降至2.56次/t。通过采用碱度1.05不含MgO的LF精炼渣,控制钢中Als含量≤0.001%,氧含量≤22×10^(-6),可有效地降低钢中脆性夹杂物含量,降低盘条断丝率。

CaO/MgO对黄兔毫釉毫纹的影响研究

兔毫釉属高温钙釉,实验以红土、草木灰、石灰石等为主要原料,采用电窑在氧化气氛中烧制,研究了不同CaO和MgO的相对含量对釉面毫纹的影响。实验结果表明:当CaO和MgO的摩尔比为(0.40∶0.38)~(0.45∶0.33)时,釉中显微结构析出枝状ε-Fe_(2)O_(3)晶体较少,尺寸约150nm~250nm,釉面呈颜色较浅的毫纹;当CaO和MgO的摩尔比增至(0.50∶0.28)~(0.55∶0.23),釉中所析出的ε-Fe_(2)O_(3)晶体呈短柱状,尺寸约70 nm~150 nm,釉面毫纹数量增加;当CaO和MgO的摩尔比增至(0.60∶0.18)~(0.65∶0.13),釉中所析出形态为枝状晶花ε-Fe_(2)O_(3)晶体数量较多,釉面呈现数量多、形态粗的黄色毫纹;当CaO和MgO的摩尔比增至0.70∶0.08,釉中析出了钙长石晶簇和黄色ε-Fe_(2)O_(3)枝状晶花,钙长石周围易形成富Ca、Fe的分相结构,促进了ε-Fe_(2)O_(3)枝状晶花的析出,导致釉面形成形态较粗的橘黄色兔毫纹。

CaO/MgO摩尔比对太阳能电池封装玻璃性能的影响

利用普通Na2O-CaO-SiO2玻璃体系,通过调整CaO/MgO摩尔比,针对太阳能电池用封装玻璃组分的性能,研究了不同CaO/MgO摩尔比对玻璃软化温度、转变温度、膨胀系数及高低温黏度的影响规律,探讨了不同CaO/MgO摩尔比值对玻璃力学性能的影响。

MgO/CaO对仿南宋官窑青釉的影响

结合相关文献中有关南宋冰裂纹青釉原理及其制备工艺,以白云石、方解石、木金土等为主要原料制备南宋官窑青瓷釉。通过单因素实验考察配方组成(MgO/CaO摩尔比)对南宋官窑青釉釉面效果的影响。实验结果表明:当MgO/CaO为0.25时,制备了色饱和度L*、a*、b*值分别为39.98、-6.21、7.59,光泽度<60%,裂纹效果较好的南宋官窑青釉。随着MgO/CaO含量进一步增加,釉面从粉青色突变为乳白色,釉面的光泽度也随之降低。XRD和显微镜结果表明随着MgO/CaO含量的增加,石英、辉石和顽火辉石等晶体数量不断增多所致。

吹风比对热障涂层-气膜冷却系统CMAS侵蚀过程及隔热性能的影响

针对熔融硅酸盐环境沉积物(CMAS)侵蚀诱发含冷却孔热障涂层结构热防护性能下降的问题,研究了不同吹风比下的CMAS的非均匀侵蚀行为及其对热障涂层(TBCs)隔热性能的影响.在Fluent软件中,考虑热传导、热对流和热辐射(热辐射使用离散纵坐标辐射模型),建立共轭传热模型得到了在吹风比为1.5、1.0和0.5时TBC-气膜冷却系统的温度分布,在ABAQUS中建立三维相场模型(PFM)模拟CMAS的非均匀侵蚀行为,定量分析不同吹风比下CMAS侵蚀行为对TBC-气膜冷却系统温度分布的影响.分析了侵蚀300 h前后TBCs-气膜冷却系统温度场的变化,探讨了在不同吹风比下CMAS非均匀侵蚀对TBCs靠近主流入口、冷却孔入口前缘、冷却孔出口后缘和主流出口4个典型位置沿涂层厚度方向路径上热阻的影响.结果表明:TBC-气膜冷却系统在工作条件下具有三维温度梯度,沿主流流动方向和沿TBCs厚度方向上有较高的温度梯度,冷却孔附近区域温度分布的不均匀度高.陶瓷(TC)层中的CMAS浓度分布呈明显的不均匀性,在高温度区域内CMAS侵蚀速率更高,吹风比降低会引起TC层温度上升,温度不均匀性下降,CMAS的侵蚀程度增加,浓度分布的不均匀性下降.CMAS侵蚀会降低TBCs的隔热性能,吹风比为1.5、1.0和0.5时,侵蚀前后TBCs在靠近主流入口位置沿厚度方向路径上热阻下降率最高,分别为16.47%、17.13%和17.55%.CMAS侵蚀对TBCs在冷却孔出口后缘的隔热性能的影响较小,热阻在侵蚀前后的变化不大.

循环流化床内高CaO含量煤自脱硫的试验研究

对开远褐煤在 1 MWth循环流化床 ( CFB)燃烧室中的自脱硫性能进行了试验研究和分析 ,发现在CFB燃烧条件下 ,高 Ca O含量煤具有很高的自脱硫效率 ;石灰石的添加量与煤的自脱硫能力密切相关。图 4表 4参

镁铝物质的量比对MoSx/MgO-Al_(2)O_(3)催化剂COS加氢性能的影响

采用共沉淀法制得镁铝物质的量比为0、0.2、0.5、1.0的MgO-Al_(2)O_(3)载体,采用浸渍法负载活性组分钼,进行预硫化分别制得Mo/M-A_(0)-S、Mo/M-A_(0.2)-S、Mo/M-A_(0.5)-S和Mo/M-A_(1.0)-S催化剂。使用固定床实验装置评价了其催化转化焦炉煤气中COS加氢的性能,采用X光电子能谱和拉曼光谱等手段对催化剂的结构及Mo物种的存在形式进行了分析,将分析结果与镁铝物质的量比进行了关联,探讨了镁铝物质的量比对催化剂性能的影响。结果表明,改变镁铝物质的量比可依次调变MgO-Al_(2)O_(3)载体的物化结构、预硫化前样品中钼的分散及其与载体间相互作用以及催化剂中MoS_(2)活性相的数量和堆叠方式,进而调控催化剂的活性和选择性。控制镁铝物质的量比符合MgAl_(2)O_(4)中镁铝化学计量比0.5时,最有利于生成MgAl_(2)O_(4);MgAl_(2)O_(4)可减弱钼与载体间的相互作用,强化钼在载体表面的均匀分散,促使更多钼在预硫化过程中转变为MoS_(2)活性相,进而提高催化剂的性能。Mo/M-A_(0.5)-S催化剂的性能最佳,其在280℃,空速62000 h^(−1)的条件下,前550 min可维持高达97.7%的COS转化率,近100%的H_(2)S选择性。

MgO/MgCl_2物质的量比对镁水泥基稻草板性能的影响

镁水泥基稻草板是以氯氧镁水泥为胶凝相,稻草为增强相的一种新型建筑材料.通过试验研究MgO/MgCl2物质的量比对镁水泥基稻草板静曲强度、软化系数和开始吸潮返卤时间的影响规律,并对试验结果进行分析讨论.结果表明:当n(MgO)n(MgCl2)为7时,材料的机械性能和耐水性均为最佳,此时水化产物以518相为主.

脱钙对水泥浆体中C-S-H凝胶结构的影响

采用X射线荧光分析、X射线衍射、Fourier红外光谱、^(29)Si固体核磁共振谱结合去卷积技术研究了脱钙对水泥(ASTMⅠ型)浆体中C-S-H凝胶结构的影响.结果表明:对于水化3,28d的水泥浆体,其脱钙过程均为2个阶段,即:当水泥浆体的钙硅比(摩尔比)由2.78左右降至2.00左右时,几乎全部游离的CH被脱去,C-S-H凝胶部分脱钙,浆体的脱钙主要在这个阶段完成,C-S-H平均链长分别由2.4,2.9增加至4.4,5.8,且I(Q^2)/I(Q^1)增加;当水泥浆体的钙硅比降至1.83左右时,C-S-H凝胶脱钙,并产生了更显著的聚合,C-S-H平均链长进一步分别增加至6.2,9.9,且I(Q^2)/I(Q^1)继续增加;Alite和Belite在整个脱钙过程中的变化并不明显.脱钙过程中C-S-H二聚体向更高聚合态转变,但是Al掺杂会影响C-S-H结构的稳定性.从分子尺度理解,脱钙如能使桥硅氧四面体结构稳定,对于C-S-H结构的优化是有利的.

骨料界面特性对混凝土力学性能的影响

采用计算机断层扫描成像(CT)技术、扫描电镜(SEM)、X射线能谱仪(EDS)、显微硬度(MH)等各种微细观测试手段对砂岩、锈染砂岩、锈面砂岩、板岩及大理岩骨料界面特性开展了试验研究,分析了以上几种骨料的界面特性对混凝土力学性能的影响机理.研究表明:不同骨料界面区微结构相差很大,不同骨料的化学成分和矿物组成影响了界面区水化产物的数量、形态、尺寸和生长发育特性;骨料的界面区显微硬度与界面区钙硅比有良好的对应关系,钙硅比越大则界面显微硬度越低;大理岩混凝土的起裂强度明显低于砂岩、板岩和锈染砂岩混凝土,且相同荷载条件下,大理岩混凝土的裂纹面积远高于其他骨料混凝土.

高铁一水硬铝石型铝土矿的低钙比烧结

研究烧结法处理我国高铁中等品位矿石的工艺条件,确定钙比为1.5时熟料中存在3CaO·2SiO2和2CaO·2SiO2。结果表明,增大钙比使熟料Al2O3溶出率、SiO2溶出率均有所降低;延长烧成时间,提高烧成温度有利于Al2O3溶出率的增加和SiO2溶出率的降低;提高铁铝比,熟料最佳烧成温度降低,烧成温度范围变窄;提出的Al2O3有效溶出率概念表明,钙比为1.5时,熟料烧成效果最好;确定高铁铝土矿适宜的烧成制度为：烧成温度1250～1300℃,烧成时间20～40min,钙比1.5。

不同煤种对混煤自固硫的影响

以平朔煤作为中硫煤,选用三个典型低硫煤与其进行不同比例掺配,并研究了煤种对混煤固硫效果的影响.结果表明:混煤固硫率的大小与(Ca+Mg)/S摩尔比和灰中(CaO+MgO)的含量有关;低、低(Ca+Mg)/S摩尔比煤掺配后,混煤的(CaO+MgO)利用率随(Ca+Mg)/S摩尔比的增大呈整体下降趋势,降硫效果主要取决于配煤对硫分的稀释作用;低、高(Ca+Mg)/S摩尔比煤掺配后,混煤的(CaO+MgO)利用率在(Ca+Mg)/S摩尔比为0.8～1时达到最大值,降硫效果取决于配煤对硫分的稀释作用和自身固硫作用.

钙镁硅酸盐系列结晶釉的研究——钙、镁氧化物对结晶釉析晶的影响

针对钙镁硅酸盐系列结晶釉,研究配方中钙、镁氧化物含量及CaO/MgO比值发生变化时,对釉烧温度及析晶体矿物种属、析晶集合体形态的影响;分析探讨钙、镁氧化物影响析晶的作用机理。研究表明,CaO/MgO比值近于1时,釉烧温度相对较低;CaO/MgO比值向大于1或小于1方向变化时,釉的烧成温度趋于升高。CaO/MgO比值在影响釉析晶体矿物种属的同时,影响析晶集合体的形态特征,认为这是由矿物的析晶习性决定的。