The activity of CaO and LaOin the liquid ternary slay CaO-SiO-LaOhas been de-termined by equilibrating Sn with the slag phase in a graphite crucible under l arm of CO at1600C.The experimental results ,showed that the ...The activity of CaO and LaOin the liquid ternary slay CaO-SiO-LaOhas been de-termined by equilibrating Sn with the slag phase in a graphite crucible under l arm of CO at1600C.The experimental results ,showed that the activity of CaO and LaOchanges slowlywhile the ratio of mole fraction.x/x,is less than unit.hut varies sharply while the ra-rio increases from 1 to 1.2.In addition,by equilibrating Sn with the binary slagBO-LaOsaturated witlt solid LaOat three different temperatures,the relation betweenIgγ~0 and I/T is determined as follows:Igγ~0=-20400/T+11.37(1500-1600C)A random network model of molten silicate structure was applied to CaO-SiO-La2O.It was found that the experimentally determined activity-composition curve of CaO arequalitatively reproduced by the curves calculated with the model,but the curves of LaOareconsiderahly different from the calculated ones.It implies that the model used is over-simpli-fied and that the difference in interaction energy between the metal cations of different valenceand silicate anions should be considered.展开更多
文摘The activity of CaO and LaOin the liquid ternary slay CaO-SiO-LaOhas been de-termined by equilibrating Sn with the slag phase in a graphite crucible under l arm of CO at1600C.The experimental results ,showed that the activity of CaO and LaOchanges slowlywhile the ratio of mole fraction.x/x,is less than unit.hut varies sharply while the ra-rio increases from 1 to 1.2.In addition,by equilibrating Sn with the binary slagBO-LaOsaturated witlt solid LaOat three different temperatures,the relation betweenIgγ~0 and I/T is determined as follows:Igγ~0=-20400/T+11.37(1500-1600C)A random network model of molten silicate structure was applied to CaO-SiO-La2O.It was found that the experimentally determined activity-composition curve of CaO arequalitatively reproduced by the curves calculated with the model,but the curves of LaOareconsiderahly different from the calculated ones.It implies that the model used is over-simpli-fied and that the difference in interaction energy between the metal cations of different valenceand silicate anions should be considered.