Solid-phase decarburization of high-carbon ferromanganese powders （HCFPs） was conducted using calcium carbonate powders （CCPs） as a decarburizer by microwave heating. Solid-phase decarburization kinelSics was inve...Solid-phase decarburization of high-carbon ferromanganese powders （HCFPs） was conducted using calcium carbonate powders （CCPs） as a decarburizer by microwave heating. Solid-phase decarburization kinelSics was investi- gated by isothermal method. The results show that the HCFPs show excellent microwave absorption at a higher av- erage heating rate of 80 ℃/min, while CCPs exhibit poor microwave absorption at a lower heating rate of 5--20 ℃/min; the heating characteristics are in-between when HCFPs and CCPs are mixed. The average heating rates of the mix- ture are 32.14, 31.25, 31.43, and 30.77 ℃/rain when the mixture is heated up to 900, 1000, 1100, and 1200 ℃, respectively. The good microwave absorption property of the mixed material lays the foundation for the solid-phase decarburization of HCFPs containing CCPs. Solid-phase decarburization of HCFPs containing CCPs is a first-order reaction by microwave heating. Apparent activation energy of solid-phase decarburization is 55.07 kJ/mol, which is far less than that of ordinary carbon gasification reaction and that of solid-phase decarburization under the same de- carburization condition by conventional heating. It indicates that microwave heating not only produces thermal effect, but also has non-thermal effect.展开更多
基金Item Sponsored by National Natural Science Foundation of China and Baosteel Group Corporation(50974149)
文摘Solid-phase decarburization of high-carbon ferromanganese powders （HCFPs） was conducted using calcium carbonate powders （CCPs） as a decarburizer by microwave heating. Solid-phase decarburization kinelSics was investi- gated by isothermal method. The results show that the HCFPs show excellent microwave absorption at a higher av- erage heating rate of 80 ℃/min, while CCPs exhibit poor microwave absorption at a lower heating rate of 5--20 ℃/min; the heating characteristics are in-between when HCFPs and CCPs are mixed. The average heating rates of the mix- ture are 32.14, 31.25, 31.43, and 30.77 ℃/rain when the mixture is heated up to 900, 1000, 1100, and 1200 ℃, respectively. The good microwave absorption property of the mixed material lays the foundation for the solid-phase decarburization of HCFPs containing CCPs. Solid-phase decarburization of HCFPs containing CCPs is a first-order reaction by microwave heating. Apparent activation energy of solid-phase decarburization is 55.07 kJ/mol, which is far less than that of ordinary carbon gasification reaction and that of solid-phase decarburization under the same de- carburization condition by conventional heating. It indicates that microwave heating not only produces thermal effect, but also has non-thermal effect.