Twenty-one square concrete columns were constructed and tested. The testing results indicate that bonded carbon fiber reinforced plastics(CFRP) sheets can be used to increase the strength and improve the serviceabilit...Twenty-one square concrete columns were constructed and tested. The testing results indicate that bonded carbon fiber reinforced plastics(CFRP) sheets can be used to increase the strength and improve the serviceability of damaged concrete columns at low temperatures. The failure of the specimens,in most cases,takes place within the middle half of the columns. And the failure of strengthened columns is sudden and explosive. The CFRP sheets increase both the axial load capacity and the ultimate concrete compressive strain of the columns. The ultimate loads of strengthened columns at-10,0 and 10 ℃ increase averagely by 9.09%,6.63% and 17.83%,respectively,as compared with those of the control specimens. The axial compressive strength of strengthened columns is related to the curing temperatures. The improvement of axial compressive strength decreases with reducing temperature,and when the temperature drops to a certain value,the improvement increases with falling temperature.展开更多
Formation of entrance and exit defects in coarse pitch orbital drilling(CPOD)of carbon fiber reinforced plastic(CFRP)plates was investigated.Deep observation on entrance and exit morphology shows tear and burr are typ...Formation of entrance and exit defects in coarse pitch orbital drilling(CPOD)of carbon fiber reinforced plastic(CFRP)plates was investigated.Deep observation on entrance and exit morphology shows tear and burr are typical defects.Meanwhile,tear is more obvious than burr,and more entrance tears emerge than exit tears.As one of the major causes of entrance and exit defects in CPOD,cutting forces were substaintially studied by contrast experiments.Then,the effect of cutting parameters on entrance and exit tear was qualitatively analyzed through a single factor test.Experiment results indicate that the variation of rotation speed has little influence on entrance and exit tear.Increasing tangential feed per tooth can enlarge entrance tear,but bring little effect on exit tear.By increasing axial feed pitch,the hole entrance and exit show severe tear.When revolution radius grows bigger and bigger,entrance and exit tear firstly decreases,and then increases.Finally,the models of tear and delamination during CPOD of CFRP were established,the formation mechanisms of entrance and exit defects were revealed,and the control strategies were accordingly put forward.展开更多
Compression tests on twenty unidirectional(UD) carbon fibre reinforced plastic(CFRP) specimens are conducted, the statistics on the measured compressive strength is calculated, and the fracture surface is characterize...Compression tests on twenty unidirectional(UD) carbon fibre reinforced plastic(CFRP) specimens are conducted, the statistics on the measured compressive strength is calculated, and the fracture surface is characterized. Two types of different fracture surface are experimentally observed, and they are corresponding to very different values on the compressive strength. A finite element(FE) analysis is conducted to investigate the influence of random fibre packing on the compressive strength. And a riks method(provided in ABAQUS software) is applied in FE model to analyze fibre buckling behaviour in the vicinity of compressive failure. The FE analysis agrees well with the experimental observation on the two types of buckling modes and also the partition of compressive strength. It is clearly shown that the random fibre packing lays a significant influence on the random variability of compressive strength of CFRP.展开更多
In order to well protect Chinese ancient buildings, aseismic behaviors of Chinese ancient tenon-mortise joints strengthened by carbon fibre reinforced plastic （CFRP） are studied by experiments. Based on the actual s...In order to well protect Chinese ancient buildings, aseismic behaviors of Chinese ancient tenon-mortise joints strengthened by carbon fibre reinforced plastic （CFRP） are studied by experiments. Based on the actual size of an ancient building, a wooden frame model with a scale of 1 ： 8 of the prototype structure is built considering the swallow-tail type of tenon-mortise connections. Low cyclic reversed loading tests are carried out including three groups of unstrengthened structures and two groups of structures strengthened with CFRP. Based on experimental data, moment-rotation angle hysteretic curves and skeleton curves for each joint are obtained. The energy dissipation capability, stiffness degradation and deformation performance of the joints before and after being strengthened are also analyzed. Results show that after being strengthened with CFRP, the tenon value pulled out of the mortise is reduced; the bending strength and the energy dissipation capabilities of the joint are enhanced; stiffness degradation of the joint is not obvious; and the deformation performance of the joint remains good. Thus, the CFRP has good effects on strengthening the tenon-mortise joints of Chinese ancient buildings.展开更多
基金Project(04043076) supported by the Outstanding Youth Foundation for Scientific and Technological Research of Anhui Province, ChinaProject(2007jq1035) supported by the Scientific Research Projects for Young College Teachers of Anhui Province, China
文摘Twenty-one square concrete columns were constructed and tested. The testing results indicate that bonded carbon fiber reinforced plastics(CFRP) sheets can be used to increase the strength and improve the serviceability of damaged concrete columns at low temperatures. The failure of the specimens,in most cases,takes place within the middle half of the columns. And the failure of strengthened columns is sudden and explosive. The CFRP sheets increase both the axial load capacity and the ultimate concrete compressive strain of the columns. The ultimate loads of strengthened columns at-10,0 and 10 ℃ increase averagely by 9.09%,6.63% and 17.83%,respectively,as compared with those of the control specimens. The axial compressive strength of strengthened columns is related to the curing temperatures. The improvement of axial compressive strength decreases with reducing temperature,and when the temperature drops to a certain value,the improvement increases with falling temperature.
基金supported in part by the Major Project of the Ministry of Science and Technology of China(No.2012ZX04003-031)the Innovation Project of Jiangsu Province(No.2016-05)
文摘Formation of entrance and exit defects in coarse pitch orbital drilling(CPOD)of carbon fiber reinforced plastic(CFRP)plates was investigated.Deep observation on entrance and exit morphology shows tear and burr are typical defects.Meanwhile,tear is more obvious than burr,and more entrance tears emerge than exit tears.As one of the major causes of entrance and exit defects in CPOD,cutting forces were substaintially studied by contrast experiments.Then,the effect of cutting parameters on entrance and exit tear was qualitatively analyzed through a single factor test.Experiment results indicate that the variation of rotation speed has little influence on entrance and exit tear.Increasing tangential feed per tooth can enlarge entrance tear,but bring little effect on exit tear.By increasing axial feed pitch,the hole entrance and exit show severe tear.When revolution radius grows bigger and bigger,entrance and exit tear firstly decreases,and then increases.Finally,the models of tear and delamination during CPOD of CFRP were established,the formation mechanisms of entrance and exit defects were revealed,and the control strategies were accordingly put forward.
文摘Compression tests on twenty unidirectional(UD) carbon fibre reinforced plastic(CFRP) specimens are conducted, the statistics on the measured compressive strength is calculated, and the fracture surface is characterized. Two types of different fracture surface are experimentally observed, and they are corresponding to very different values on the compressive strength. A finite element(FE) analysis is conducted to investigate the influence of random fibre packing on the compressive strength. And a riks method(provided in ABAQUS software) is applied in FE model to analyze fibre buckling behaviour in the vicinity of compressive failure. The FE analysis agrees well with the experimental observation on the two types of buckling modes and also the partition of compressive strength. It is clearly shown that the random fibre packing lays a significant influence on the random variability of compressive strength of CFRP.
基金The Cultural Ministry Foundation of China(No.17-2009)the Research Foundation of Palace Museum(No.2007-4)
文摘In order to well protect Chinese ancient buildings, aseismic behaviors of Chinese ancient tenon-mortise joints strengthened by carbon fibre reinforced plastic （CFRP） are studied by experiments. Based on the actual size of an ancient building, a wooden frame model with a scale of 1 ： 8 of the prototype structure is built considering the swallow-tail type of tenon-mortise connections. Low cyclic reversed loading tests are carried out including three groups of unstrengthened structures and two groups of structures strengthened with CFRP. Based on experimental data, moment-rotation angle hysteretic curves and skeleton curves for each joint are obtained. The energy dissipation capability, stiffness degradation and deformation performance of the joints before and after being strengthened are also analyzed. Results show that after being strengthened with CFRP, the tenon value pulled out of the mortise is reduced; the bending strength and the energy dissipation capabilities of the joint are enhanced; stiffness degradation of the joint is not obvious; and the deformation performance of the joint remains good. Thus, the CFRP has good effects on strengthening the tenon-mortise joints of Chinese ancient buildings.