The different copper coatings with thickness varying from 0.3μm to 1.5μm were deposited on carbon fibers using either electroless plating or electroplating method. The coated fibers were chopped and composites were ...The different copper coatings with thickness varying from 0.3μm to 1.5μm were deposited on carbon fibers using either electroless plating or electroplating method. The coated fibers were chopped and composites were fabricated with melting aluminum at 700℃. The effect of the copper layer on the microstructure in the system was discussed. The results show that the copper layer has fully reacted with aluminum matrix, and the intermetallic compound CuAl2 forms through SEM observation and XRD, EDX analysis. The results of tensile tests indicate that composites fabricated using carbon fibers with 0.7-1.1μm copper coating perform best and the composites turn to more brittle as the thickness of copper coating increases. The fracture surface observation exhibits good interface bonding and ductility of the matrix alloy when the thickness of copper coating is about 0.7-1.1μm.展开更多
Preparing antioxidant coatings to address the inherent oxidation sensitivity of carbon fiber-reinforced carbon aerogel(C/CA)composites is a feasible way to promote their application in oxidizing environments as therma...Preparing antioxidant coatings to address the inherent oxidation sensitivity of carbon fiber-reinforced carbon aerogel(C/CA)composites is a feasible way to promote their application in oxidizing environments as thermal insulation materials.However,preparing the coatings with excellent oxidation and ablation resistance while avoiding evident damage to the C/CA substrate still remains a challenge.Herein,a SiC@SiO_(2)nanowire-toughened ZrB2–SiC/SiC bilayer coating with a large thickness of 500μm was prepared on C/CA using a one-step low-temperature reaction sintering method,which simultaneously formed a sintered outer layer with even-distributed nanowires and a siliconized gradient inner layer.By courtesy of the synergic thermal response of the layers and the crack deflection induced by the nanowires,the resulting coating has moderate residual compressive stress of 0.08–1.22 GPa in the interface,high interfacial bonding strength of 6.02 MPa,and good fracture toughness of 4.36 MPa·m^(1/2).Benefited from the optimum components and improved structure,the coating shows excellent cyclic ablation resistance with linear ablation rates of 0.1μm/s at 1650℃for 1500 s(300 s×5 cycles)and 0.4μm/s at 1850℃for 900 s(300 s×3 cycles).The one-step preparation strategy contributes to little damage to the substrate,thus showing the well-preserved mechanical and thermal insulation properties.展开更多
The effect of different regimes of heat treatment on the tensile strength of SiC coated composite of C fibers reinforced Al wires has been investigated.Their tensile strength may increase under treatment either at 500...The effect of different regimes of heat treatment on the tensile strength of SiC coated composite of C fibers reinforced Al wires has been investigated.Their tensile strength may increase under treatment either at 500℃ for 2h or 550℃ for 1h,but decrease over 600℃.After the strength tests of extracted fibers from composite wires,the SiC coating is an excellent protection to C fibers.EPMA and EDAX showed that the C/Al interface of the composite wires is stable under treatment below 600℃,but unstable at 650℃展开更多
基金Project(204AA335010) supported by the National High-Tech Research and Development Program of China
文摘The different copper coatings with thickness varying from 0.3μm to 1.5μm were deposited on carbon fibers using either electroless plating or electroplating method. The coated fibers were chopped and composites were fabricated with melting aluminum at 700℃. The effect of the copper layer on the microstructure in the system was discussed. The results show that the copper layer has fully reacted with aluminum matrix, and the intermetallic compound CuAl2 forms through SEM observation and XRD, EDX analysis. The results of tensile tests indicate that composites fabricated using carbon fibers with 0.7-1.1μm copper coating perform best and the composites turn to more brittle as the thickness of copper coating increases. The fracture surface observation exhibits good interface bonding and ductility of the matrix alloy when the thickness of copper coating is about 0.7-1.1μm.
基金the Defense Industrial Technology Development Program(No.JCKY2021130B007)the National Natural Science Foundation of China(Nos.52272075 and 52188101)+1 种基金the Research Fund of Youth Innovation Promotion Association of Chinese Academy of Sciences(No.2021190)the directional institutionalized scientific research platform relies on China Spallation Neutron Source of Chinese Academy of Sciences,and the National Key R&D Program of China(No.2021YFA1500804).
文摘Preparing antioxidant coatings to address the inherent oxidation sensitivity of carbon fiber-reinforced carbon aerogel(C/CA)composites is a feasible way to promote their application in oxidizing environments as thermal insulation materials.However,preparing the coatings with excellent oxidation and ablation resistance while avoiding evident damage to the C/CA substrate still remains a challenge.Herein,a SiC@SiO_(2)nanowire-toughened ZrB2–SiC/SiC bilayer coating with a large thickness of 500μm was prepared on C/CA using a one-step low-temperature reaction sintering method,which simultaneously formed a sintered outer layer with even-distributed nanowires and a siliconized gradient inner layer.By courtesy of the synergic thermal response of the layers and the crack deflection induced by the nanowires,the resulting coating has moderate residual compressive stress of 0.08–1.22 GPa in the interface,high interfacial bonding strength of 6.02 MPa,and good fracture toughness of 4.36 MPa·m^(1/2).Benefited from the optimum components and improved structure,the coating shows excellent cyclic ablation resistance with linear ablation rates of 0.1μm/s at 1650℃for 1500 s(300 s×5 cycles)and 0.4μm/s at 1850℃for 900 s(300 s×3 cycles).The one-step preparation strategy contributes to little damage to the substrate,thus showing the well-preserved mechanical and thermal insulation properties.
文摘The effect of different regimes of heat treatment on the tensile strength of SiC coated composite of C fibers reinforced Al wires has been investigated.Their tensile strength may increase under treatment either at 500℃ for 2h or 550℃ for 1h,but decrease over 600℃.After the strength tests of extracted fibers from composite wires,the SiC coating is an excellent protection to C fibers.EPMA and EDAX showed that the C/Al interface of the composite wires is stable under treatment below 600℃,but unstable at 650℃