A mixture of amorphous carbon and carbon nanotubes films was synthesized on stainless steel plates by a micro- wave plasma enhanced chemical vapor deposition system. The source gases were hydrogen and methane with flo...A mixture of amorphous carbon and carbon nanotubes films was synthesized on stainless steel plates by a micro- wave plasma enhanced chemical vapor deposition system. The source gases were hydrogen and methane with flow rates of 100 and 16sccm,respectively,with a total pressure of 5.0kPa. The surface morphology and the structure of the films were characterized by field emission scanning electron microscopy （SEM） and Raman scattering spectroscopy. Field emission properties of as-deposited film were measured in a vacuum room below 5 ×10^ 5 Pa. The experimental results show that the initial turn-on field is 0. 9V/μm; The current density is 4.0mA/cm2 and the emission sites are dense and uniform at an electric field of 3.7V/μm. These results indicate that such a mixture of amorphous carbon and carbon nanotubes films is a promising material for field emission applications.展开更多
A simple process to fabricate chain-like carbon nanotube （CNT） films by microwave plasma-enhanced chemical vapor deposition （MPCVD） was developed successfully. Prior to deposition, the Ti/Al2O3 substrates were gro...A simple process to fabricate chain-like carbon nanotube （CNT） films by microwave plasma-enhanced chemical vapor deposition （MPCVD） was developed successfully. Prior to deposition, the Ti/Al2O3 substrates were ground with Fe-doped SiO2 powder. The nano-structure of the deposited films was analyzed by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and Raman spectroscopy. The field electron emission characteristics of the chain-like carbon nanotube films were measured under the vacuum of 10-5 Pa. The low turn-on field of 0.80 V/μm and the emission current density of 8.5 mA/cm2 at the electric field of 3.0 V/μm are obtained. Based on the above results, chain-like carbon nanotube films probably have important applications in cold cathode materials and electrode materials.展开更多
A fringelike field emission with high-luminescence and stable emission current from screen-printed carbon nanotube mixed zinc oxide (CNT-ZnO) composite cathode was investigated. The luminescent patterns are significan...A fringelike field emission with high-luminescence and stable emission current from screen-printed carbon nanotube mixed zinc oxide (CNT-ZnO) composite cathode was investigated. The luminescent patterns are significantly different from those observed in the field emission measure of pure CNT cathode. SEM images reveal that the CNTs are perfectly matched with ZnO powders by filling the interspaces in CNT film. XRD analysis demonstrates that the CNTs and ZnO have a high degree of crystalline perfection. Field emission measurement exhibits that the turn-on field of CNT-ZnO cathode is 2.08 V/μm, lower than 2.46 V/μm for pure CNT cathode. The large fringelike emission current at the brims of CNT-ZnO cathode is attributed to a combination of the increased effective contact area of CNTs, which decrease the sheet resistance of cathode film, and the dangled CNT bundles at the brims of CNT-ZnO film cathode.展开更多
Amorphous carbon nanoparticles （a-CNPs） on a multi-walled carbon nanotube （MWCNT） film, deposited on a silicon substrate, were synthesized using an electrodeposition combination from a methanol suspension of polyd...Amorphous carbon nanoparticles （a-CNPs） on a multi-walled carbon nanotube （MWCNT） film, deposited on a silicon substrate, were synthesized using an electrodeposition combination from a methanol suspension of polydiallyldimethylammonium chloride-modified MWCNTs. A low-voltage electropho- retic deposition of the MWCNTs and a high-voltage electrochemical deposition of the a-CNPs were carried out to yield homogenously attached a-CNPs on the surfaces of the MWCNTs, and form a composite film with good adhesion to the substrate. This scalable technology can produce a large area of a-CNP/MWCNT film. And the field emission investigations show that the a-CNP/MWCNT film has turn- on electric field of 3.17 V μm- 1 （at 10 μA cm-2） and threshold field of 4.62 V μm-1 （at 1 mA cm-2）, which are lower than those of the MWCNT film. The a-CNP/MWCNT film can be deposited simply with large areas and may be a promising cathode material applied in field emission displays.展开更多
文摘A mixture of amorphous carbon and carbon nanotubes films was synthesized on stainless steel plates by a micro- wave plasma enhanced chemical vapor deposition system. The source gases were hydrogen and methane with flow rates of 100 and 16sccm,respectively,with a total pressure of 5.0kPa. The surface morphology and the structure of the films were characterized by field emission scanning electron microscopy （SEM） and Raman scattering spectroscopy. Field emission properties of as-deposited film were measured in a vacuum room below 5 ×10^ 5 Pa. The experimental results show that the initial turn-on field is 0. 9V/μm; The current density is 4.0mA/cm2 and the emission sites are dense and uniform at an electric field of 3.7V/μm. These results indicate that such a mixture of amorphous carbon and carbon nanotubes films is a promising material for field emission applications.
文摘A simple process to fabricate chain-like carbon nanotube （CNT） films by microwave plasma-enhanced chemical vapor deposition （MPCVD） was developed successfully. Prior to deposition, the Ti/Al2O3 substrates were ground with Fe-doped SiO2 powder. The nano-structure of the deposited films was analyzed by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and Raman spectroscopy. The field electron emission characteristics of the chain-like carbon nanotube films were measured under the vacuum of 10-5 Pa. The low turn-on field of 0.80 V/μm and the emission current density of 8.5 mA/cm2 at the electric field of 3.0 V/μm are obtained. Based on the above results, chain-like carbon nanotube films probably have important applications in cold cathode materials and electrode materials.
文摘A fringelike field emission with high-luminescence and stable emission current from screen-printed carbon nanotube mixed zinc oxide (CNT-ZnO) composite cathode was investigated. The luminescent patterns are significantly different from those observed in the field emission measure of pure CNT cathode. SEM images reveal that the CNTs are perfectly matched with ZnO powders by filling the interspaces in CNT film. XRD analysis demonstrates that the CNTs and ZnO have a high degree of crystalline perfection. Field emission measurement exhibits that the turn-on field of CNT-ZnO cathode is 2.08 V/μm, lower than 2.46 V/μm for pure CNT cathode. The large fringelike emission current at the brims of CNT-ZnO cathode is attributed to a combination of the increased effective contact area of CNTs, which decrease the sheet resistance of cathode film, and the dangled CNT bundles at the brims of CNT-ZnO film cathode.
基金support from the Top Hundred Talents Program of Chinese Academy of Sciencesthe National Nature Science Foundation of China(No.51002161)
文摘Amorphous carbon nanoparticles （a-CNPs） on a multi-walled carbon nanotube （MWCNT） film, deposited on a silicon substrate, were synthesized using an electrodeposition combination from a methanol suspension of polydiallyldimethylammonium chloride-modified MWCNTs. A low-voltage electropho- retic deposition of the MWCNTs and a high-voltage electrochemical deposition of the a-CNPs were carried out to yield homogenously attached a-CNPs on the surfaces of the MWCNTs, and form a composite film with good adhesion to the substrate. This scalable technology can produce a large area of a-CNP/MWCNT film. And the field emission investigations show that the a-CNP/MWCNT film has turn- on electric field of 3.17 V μm- 1 （at 10 μA cm-2） and threshold field of 4.62 V μm-1 （at 1 mA cm-2）, which are lower than those of the MWCNT film. The a-CNP/MWCNT film can be deposited simply with large areas and may be a promising cathode material applied in field emission displays.