The effects of RE modification on structure and the properties of a new cast hot work die (CHD) steel were investigated. The grains of the CHD steel are refined by RE modification. With the increase of RE addition, b...The effects of RE modification on structure and the properties of a new cast hot work die (CHD) steel were investigated. The grains of the CHD steel are refined by RE modification. With the increase of RE addition, both grain size and inclusion amount are reduced. Appropriate amount of RE results in decrease in inclusion amount and formation of spheroidal inclusions uniformly-distributed in steel, so that the morphology and distribution of inclusions are improved. RE composite modification favors the formation of bainite, austenite and fine lath martensite with dense dislocation. When the residual RE content reaches 0.02%, no obvious changes in strength and hardness are found, while fracture toughness and threshold of fatigue crack growth are increased. The impact toughness, elongation and reduction of cross sectional area are increased by a factor of two, and thermal fatigue resistance is also improved.展开更多
The understanding of oxidation behaviors on H13 steel was helpful to improve the service life and performance of hot work moulds and dies. Thermal-Calc Software was performed to calculate the oxidation phases on H13 s...The understanding of oxidation behaviors on H13 steel was helpful to improve the service life and performance of hot work moulds and dies. Thermal-Calc Software was performed to calculate the oxidation phases on H13 steel along with different partial oxygen pressures in the interesting temperature range of 500-700 ℃. In this range H13 steel samples were treated respectively in different atmosphere including flowing water vapor （0.2 MPa）, normal pressure air （0.1 MPa） and low pressure air （0. 001 MPa）. The different oxidation films were detected with optical microscopy and X-ray diffraction. The microstructures and phase constitutions of the films formed in low pressure air were similar to those of the films formed in water vapor, and obviously different to those of the films formed in normal pressure air. The oxidation mechanisms of H13 steel in different atmosphere were also discussed.展开更多
文摘The effects of RE modification on structure and the properties of a new cast hot work die (CHD) steel were investigated. The grains of the CHD steel are refined by RE modification. With the increase of RE addition, both grain size and inclusion amount are reduced. Appropriate amount of RE results in decrease in inclusion amount and formation of spheroidal inclusions uniformly-distributed in steel, so that the morphology and distribution of inclusions are improved. RE composite modification favors the formation of bainite, austenite and fine lath martensite with dense dislocation. When the residual RE content reaches 0.02%, no obvious changes in strength and hardness are found, while fracture toughness and threshold of fatigue crack growth are increased. The impact toughness, elongation and reduction of cross sectional area are increased by a factor of two, and thermal fatigue resistance is also improved.
基金ItemSponsored by Science and Technology Development Fund of Shanghai Municipality (015211010)ASSABTooling Technology (Shanghai) Co Ltd
文摘The understanding of oxidation behaviors on H13 steel was helpful to improve the service life and performance of hot work moulds and dies. Thermal-Calc Software was performed to calculate the oxidation phases on H13 steel along with different partial oxygen pressures in the interesting temperature range of 500-700 ℃. In this range H13 steel samples were treated respectively in different atmosphere including flowing water vapor （0.2 MPa）, normal pressure air （0.1 MPa） and low pressure air （0. 001 MPa）. The different oxidation films were detected with optical microscopy and X-ray diffraction. The microstructures and phase constitutions of the films formed in low pressure air were similar to those of the films formed in water vapor, and obviously different to those of the films formed in normal pressure air. The oxidation mechanisms of H13 steel in different atmosphere were also discussed.