A three-dimensional finite-element model of slab continuous casting mold was conducted to clarify the effect of cooling structure on thermal behavior of copper plates. The results show that temperature distribution of...A three-dimensional finite-element model of slab continuous casting mold was conducted to clarify the effect of cooling structure on thermal behavior of copper plates. The results show that temperature distribution of hot surface is mainly governed by cooling structure and heat-transfer conditions. For hot surface centricity, maximum surface temperature promotions are 30℃ and 15℃ with thickness increments of copper plates of 5 mm and nickel layers of 1 mm, respectively. The surface temperature without nickel layers is depressed by 10℃ when the depth increment of water slots is 2 mm and that with nickel layers adjacent to and away from mold outlet is depressed by 7℃ and 5℃, respectively. The specific trend of temperature distribution of transverse sections of copper plates is nearly free of cooling structure, but temperature is changed and its law is similar to the corresponding surface temperature.展开更多
A plate＇s internal quality is very critical, especially for boilers and high-pressure vessels. The ultrasonic test （UT） is the main type of non-destructive flaw detection for heavy plates, which is important becaus...A plate＇s internal quality is very critical, especially for boilers and high-pressure vessels. The ultrasonic test （UT） is the main type of non-destructive flaw detection for heavy plates, which is important because one of the main reasons for plate defects is ultrasonic flaws. This study, based on Baosteel＇ s practical experience in the manufacture of heavy plates, elucidates the cause of defect formation by analyzing ultrasonic flaw testing maps and using special equipment, such as the scanning electron microscope, electron probe and the optical microscope. The author puts forward the following improvement measures： ① Ultrasonic flaws are caused by central porosity and segregation,[H] bubbles and inclusion in slabs.②Ultrasonic flaws are more likely to occur in the bottom and top of slabs rather than the other positions in the casting sequence. It is clear that one-quarter of the inner camber＇ s thickness is accumulated inclusion.③It is clear that overheating in the tundish and the flow of the casting mould have an effect on ultrasonic flaws caused by inclusions.④Soft reduction improves central porosity and segregation,which decreases the number of ultrasonic flaws in the plate.展开更多
基金Project(51004031) supported by the National Natural Science Foundation of ChinaProject(50925415) supported by the National Outstanding Young Scientist Foundation of China+1 种基金Project(20100042120012) supported by the Special Research Fund for Doctoral Programs of Ministry of Education of ChinaProject(N090402022) supported by the Fundamental Research Funds for the Central Universities of China
文摘A three-dimensional finite-element model of slab continuous casting mold was conducted to clarify the effect of cooling structure on thermal behavior of copper plates. The results show that temperature distribution of hot surface is mainly governed by cooling structure and heat-transfer conditions. For hot surface centricity, maximum surface temperature promotions are 30℃ and 15℃ with thickness increments of copper plates of 5 mm and nickel layers of 1 mm, respectively. The surface temperature without nickel layers is depressed by 10℃ when the depth increment of water slots is 2 mm and that with nickel layers adjacent to and away from mold outlet is depressed by 7℃ and 5℃, respectively. The specific trend of temperature distribution of transverse sections of copper plates is nearly free of cooling structure, but temperature is changed and its law is similar to the corresponding surface temperature.
文摘A plate＇s internal quality is very critical, especially for boilers and high-pressure vessels. The ultrasonic test （UT） is the main type of non-destructive flaw detection for heavy plates, which is important because one of the main reasons for plate defects is ultrasonic flaws. This study, based on Baosteel＇ s practical experience in the manufacture of heavy plates, elucidates the cause of defect formation by analyzing ultrasonic flaw testing maps and using special equipment, such as the scanning electron microscope, electron probe and the optical microscope. The author puts forward the following improvement measures： ① Ultrasonic flaws are caused by central porosity and segregation,[H] bubbles and inclusion in slabs.②Ultrasonic flaws are more likely to occur in the bottom and top of slabs rather than the other positions in the casting sequence. It is clear that one-quarter of the inner camber＇ s thickness is accumulated inclusion.③It is clear that overheating in the tundish and the flow of the casting mould have an effect on ultrasonic flaws caused by inclusions.④Soft reduction improves central porosity and segregation,which decreases the number of ultrasonic flaws in the plate.