The rupture behavior of a cast Ni-base superalloy M963 at high temperature has been investi- gated. The microstructure examination shows that there exists a large amount of the carbide and γ-γ' eutectic, which i...The rupture behavior of a cast Ni-base superalloy M963 at high temperature has been investi- gated. The microstructure examination shows that there exists a large amount of the carbide and γ-γ' eutectic, which is very harmful to the mechanical properties of M963 superalloy. The tensile strength of M963 superalloy both at room temperature and at high temperatures is higher than that of K17G alloy, but the tensile ductility of the former is much lower than that of the latter. In tensile fracture process with the high strain rate, the open carbides are the initiation site and the carbide/matrix interface is the propagation path of cracks. But in fracture process with the low strain rate, the carbide/matrix interface and cast microvoids are the initiation sites, and the carbide/matrix interface is the propagation path of cracks. The effective ways to improve ductility of M963 superalloy are also suggested.展开更多
A kind of diamond grinding wheel bonded by short cast iron fibres has been developed. ln comparison with high quality bronze bonded diamond grinding wheel. the new wheel was more suitable to grind hard and brittle mat...A kind of diamond grinding wheel bonded by short cast iron fibres has been developed. ln comparison with high quality bronze bonded diamond grinding wheel. the new wheel was more suitable to grind hard and brittle materials like ceramics. For Si3N4, the grinding efficiency has been raised two times and the grinding ratio five times展开更多
The effects of Cr content and annealing temperature on abrasive wear characteristics of cast ausferrite nodular iron were investigated with Suga type abrasive wear tester. The surface morphology and Vickers hardness o...The effects of Cr content and annealing temperature on abrasive wear characteristics of cast ausferrite nodular iron were investigated with Suga type abrasive wear tester. The surface morphology and Vickers hardness of the tested samples were analyzed by scanning electron microscopy（SEM）, digital microscope and Vickers hardness tester. The results show that the cast ausferrite nodular iron could be obtained by alloying with Cr in the as-cast ductile cast iron and permanent mold casting, and the bainite content in the matrix increased with increasing Cr content. However, the decomposition of bainite took place during annealing at 500 °C to 800 °C; especially, at 800 °C, the bainite transformed into a mixture of fine lamellar pearlite and ferrite matrix structure. The wear loss of specimens was reduced with increasing Cr content in the cast ausferrite nodular iron. The wear loss of the sample cast ausferrite nodular iron with 0.4mass% Cr is the least. The wear loss began to increase while the Cr content is 0.6mass%. The wear loss of annealed ductile irons at different annealing temperatures was higher than that of as-cast samples. During the abrasive wear, the shear stress transformed austenite to martensite, and the hardness of specimens increased and the wear resistance of as-cast ductile cast iron was improved.展开更多
基金supported by the Postdoctoral Science Foundation of China
文摘The rupture behavior of a cast Ni-base superalloy M963 at high temperature has been investi- gated. The microstructure examination shows that there exists a large amount of the carbide and γ-γ' eutectic, which is very harmful to the mechanical properties of M963 superalloy. The tensile strength of M963 superalloy both at room temperature and at high temperatures is higher than that of K17G alloy, but the tensile ductility of the former is much lower than that of the latter. In tensile fracture process with the high strain rate, the open carbides are the initiation site and the carbide/matrix interface is the propagation path of cracks. But in fracture process with the low strain rate, the carbide/matrix interface and cast microvoids are the initiation sites, and the carbide/matrix interface is the propagation path of cracks. The effective ways to improve ductility of M963 superalloy are also suggested.
文摘A kind of diamond grinding wheel bonded by short cast iron fibres has been developed. ln comparison with high quality bronze bonded diamond grinding wheel. the new wheel was more suitable to grind hard and brittle materials like ceramics. For Si3N4, the grinding efficiency has been raised two times and the grinding ratio five times
基金Item Sponsored by Important National Science and Technology Specific Project of China(2012ZX04010-031)
文摘The effects of Cr content and annealing temperature on abrasive wear characteristics of cast ausferrite nodular iron were investigated with Suga type abrasive wear tester. The surface morphology and Vickers hardness of the tested samples were analyzed by scanning electron microscopy（SEM）, digital microscope and Vickers hardness tester. The results show that the cast ausferrite nodular iron could be obtained by alloying with Cr in the as-cast ductile cast iron and permanent mold casting, and the bainite content in the matrix increased with increasing Cr content. However, the decomposition of bainite took place during annealing at 500 °C to 800 °C; especially, at 800 °C, the bainite transformed into a mixture of fine lamellar pearlite and ferrite matrix structure. The wear loss of specimens was reduced with increasing Cr content in the cast ausferrite nodular iron. The wear loss of the sample cast ausferrite nodular iron with 0.4mass% Cr is the least. The wear loss began to increase while the Cr content is 0.6mass%. The wear loss of annealed ductile irons at different annealing temperatures was higher than that of as-cast samples. During the abrasive wear, the shear stress transformed austenite to martensite, and the hardness of specimens increased and the wear resistance of as-cast ductile cast iron was improved.