Dependence of Thermal Annealing on Transparent Conducting Properties of HoF_3-Doped ZnO Thin Films
1
作者 Jin-Song Luo Jie Lin +2 位作者 Li-Gong Zhang Xiao-Yang Guo Yong-Fu Zhu 《Chinese Physics Letters》 SCIE CAS CSCD 2019年第5期75-78,共4页
A kind of n-type HoF_3-doped zinc oxide-based transparent conductive film has been developed by electron beam evaporation and studied under thermal annealing in air and vacuum at temperatures 100–500℃.Effective subs... A kind of n-type HoF_3-doped zinc oxide-based transparent conductive film has been developed by electron beam evaporation and studied under thermal annealing in air and vacuum at temperatures 100–500℃.Effective substitutional dopings of F to O and Ho to Zn are realized for the films with smooth surface morphology and average grain size of about 50 nm.The hall mobility,electron concentration,resistivity and work function for the asdeposited films are 47.89 cm^2/Vs,1.39×10^(20)cm^(-3),9.37×10^(-4)Ω·cm and 5.069 eV,respectively.In addition,the average transmittance in the visible region(400–700 nm)approximates to 87%.The HoF_3:ZnO films annealed in air and vacuum can retain good optoelectronic properties under 300℃,thereinto,more stable electrical properties can be found in the air-annealed films than in the vacuum-annealed films,which is assumed to be a result of improved nano-crystalline lattice quality.The optimized films for most parameters can be obtained at 200℃ for the air-annealing case and at room temperature for the vacuum annealing case.The advisable optoelectronic properties imply that HoF_3:ZnO can facilitate carrier injection and has promising applications in energy and light sources as transparent electrodes. 展开更多
关键词 zno Ho DEPENDENce of Thermal ANNEALING on TRANSPARENT CONDUCTING Properties of HoF3-doped zno Thin films
下载PDF
退火温度对Ce掺杂ZnO薄膜光学特性影响的研究
2
作者 崔舒 王超 孟庆杰 《通化师范学院学报》 2012年第10期16-17,37,共3页
采用溶胶凝胶(sol-gel)法,在普通载玻片和Si-SiO2衬底上成功制备Ce掺杂ZnO薄膜.利用X射线衍射仪(XRD)、原子力显微镜(AFM)及光致荧光光谱(PL)对样品的结构、形貌和光学特性进行表征.XRD谱表明大部分样品都有较好的c轴择优取向,而且随着... 采用溶胶凝胶(sol-gel)法,在普通载玻片和Si-SiO2衬底上成功制备Ce掺杂ZnO薄膜.利用X射线衍射仪(XRD)、原子力显微镜(AFM)及光致荧光光谱(PL)对样品的结构、形貌和光学特性进行表征.XRD谱表明大部分样品都有较好的c轴择优取向,而且随着退火温度的升高择优取向明显改善.PL谱中在390nm附近可观察到明显发光峰,退火温度升高能够提高本征发光峰强度,抑制可见光区发光强度.用AFM观察到的样品表面形貌表明,退火温度提高使样品表面更加平整,同时粒径变大. 展开更多
关键词 ce掺杂zno薄膜 退火温度 光学特性
下载PDF
Preparation,characterization and infrared emissivity study of Ce-doped ZnO films 被引量:10
3
作者 杜芳黎 王宁 +1 位作者 张冬梅 沈应中 《Journal of Rare Earths》 SCIE EI CAS CSCD 2010年第3期391-395,共5页
Ce-doped ZnO films were prepared by the sol-gel method with spin coating onto glass substrates.Zinc acetate dihydrate,ethanol,diethanolamine and cerium nitrate hexahydrate were used as starting material,solvent,stabil... Ce-doped ZnO films were prepared by the sol-gel method with spin coating onto glass substrates.Zinc acetate dihydrate,ethanol,diethanolamine and cerium nitrate hexahydrate were used as starting material,solvent,stabilizer and dopant source,respectively.Structure and microstructure of the films were characterized with X-ray diffraction(XRD),field emission-scanning electron microscopy(FE-SEM) and the energy dispersive X-ray spectrometry(EDS).The infrared properties were also investigated.It was found that Ce-... 展开更多
关键词 ce-doped zno film SOL-GEL infrared properties rare earths
原文传递
纳米Ce-ZnO催化降解酸性染料条件优化及回收利用 被引量:1
4
作者 于占云 陈宇伦 +3 位作者 戴宇斌 袁馨怡 倪韦韦 宋茹 《现代纺织技术》 2019年第6期74-78,共5页
掺杂稀土元素Ce制备纳米Ce-ZnO催化剂,以甲基橙溶液为酸性染料代表,对纳米Ce-ZnO催化降解甲基橙条件进行优化,并对催化剂的回收循环使用效果进行研究。在催化时间为3 h条件下,通过正交试验确定纳米Ce-ZnO催化降解甲基橙溶液的最佳条件... 掺杂稀土元素Ce制备纳米Ce-ZnO催化剂,以甲基橙溶液为酸性染料代表,对纳米Ce-ZnO催化降解甲基橙条件进行优化,并对催化剂的回收循环使用效果进行研究。在催化时间为3 h条件下,通过正交试验确定纳米Ce-ZnO催化降解甲基橙溶液的最佳条件为催化温度25℃,甲基橙溶液pH 2,催化剂添加量1.0 g/L。在最优催化条件下,纳米Ce-ZnO对3×10^-5 mol/L甲基橙溶液的降解率达到90%左右,对不同浓度(1×10^-5、3×10^-5 mol/L和5×10^-5 mol/L)甲基橙溶液的降解均符合一级动力学方程。以聚偏二氯乙烯(PVDC)膜为载体,键合Ce-ZnO制备的Ce-ZnO/PVDC膜材料对3×10^-5 mol/L甲基橙溶液的降解率提高到95%以上,且循环3次使用后对甲基橙溶液的催化降解率保持在70%左右。因此,纳米Ce-ZnO催化剂及其PVDC膜材料在降解酸性染料方面有进一步开发应用前景。 展开更多
关键词 纳米zno 稀土元素ce 甲基橙溶液 降解 PVDC膜
下载PDF
Ce-ZnO@TiO_(2)纳米薄膜的制备及其光催化性能研究
5
作者 竹秋妮 张帅 武军 《广州化工》 CAS 2021年第8期34-37,共4页
将低温常压水热法制备的ZnO纳米花通过稀土Ce掺杂和TiO_(2)纳米纤维原位固定,自组装形成ZnO@TiO_(2)和Ce-ZnO@TiO_(2)宏观薄膜,以罗丹明B和甲基橙为降解底物,搭建循环光催化反应装置,研究薄膜材料的光催化活性。实验结果表明,Ce-ZnO,ZnO... 将低温常压水热法制备的ZnO纳米花通过稀土Ce掺杂和TiO_(2)纳米纤维原位固定,自组装形成ZnO@TiO_(2)和Ce-ZnO@TiO_(2)宏观薄膜,以罗丹明B和甲基橙为降解底物,搭建循环光催化反应装置,研究薄膜材料的光催化活性。实验结果表明,Ce-ZnO,ZnO@TiO_(2)和Ce-ZnO@TiO_(2)复合物的光催化活性分别是单纯ZnO的1.6倍,1.4倍和1.9倍。由此可见,Ce的掺杂和ZnO/TiO_(2)异质结的形成,都将提高材料的光催化活性,而且产品的宏观膜形态便于回收重复利用。 展开更多
关键词 zno TiO_(2) ce-zno@TiO_(2)膜 复合 光催化
下载PDF
旋涂法制备铈掺杂氧化锌薄膜的特性分析研究 被引量:1
6
作者 解旭东 《无机盐工业》 CAS CSCD 北大核心 2019年第1期33-38,共6页
以旋涂法制备铈掺杂氧化锌薄膜,利用XRD、Uv-vis光谱、PL光谱、四点探针及磁性测试系统等手段分析铈掺杂与退火处理对薄膜的晶体结构、表面形貌、光学透射率、发光特性及电磁特性的影响。研究结果表明:所有薄膜皆为纤锌矿结构,具有很高... 以旋涂法制备铈掺杂氧化锌薄膜,利用XRD、Uv-vis光谱、PL光谱、四点探针及磁性测试系统等手段分析铈掺杂与退火处理对薄膜的晶体结构、表面形貌、光学透射率、发光特性及电磁特性的影响。研究结果表明:所有薄膜皆为纤锌矿结构,具有很高的c轴取向性,无杂相产生,但铈掺杂会影响其结晶状况。所有薄膜表面皆呈多孔性纳米晶形态,掺铈后其表面则会出现五边形或六边形链状纹路,且具有很高的再现性。所有薄膜在可见光范围内的透射率皆可达80%以上,其能隙值则随铈掺杂量增加而减小。所有薄膜在紫外光区皆有一明显发射峰,但其强度随铈掺杂量增加而减弱;掺铈后的薄膜在绿光区与黄光区各有一明显发射峰,其强度则随铈掺杂量增加而增强。室温下薄膜的电传导机制为热激活型,而低温下则为变程跳跃型;所有薄膜皆具磁性,且其饱和磁矩随铈掺杂量增加而变大。 展开更多