Edge effect during microwave plasma chemical vapor deposition diamond-film:Multiphysics simulation and experimental verification

This study focused on the investigation of the edge effect of diamond films deposited by microwave plasma chemical vapor de-position.Substrate bulge height△h is a factor that affects the edge effect,and it was used to simulate plasma and guide the diamond-film deposition experiments.Finite-element software COMSOL Multiphysics was used to construct a multiphysics(electromagnetic,plasma,and fluid heat transfer fields)coupling model based on electron collision reaction.Raman spectroscopy and scanning electron microscopy were performed to characterize the experimental growth and validate the model.The simulation results reflected the experimental trends observed.Plasma discharge at the edge of the substrate accelerated due to the increase in△h(△h=0-3 mm),and the values of electron density(n_(c)),molar concentration of H(C_(H)),and molar concentration of CH_(3)(C_(CH_(3)))doubled at the edge(for the special concave sample with△h=−1 mm,the active chemical groups exhibited a decreased molar concentration at the edge of the substrate).At=0-3 mm,a high diamond growth rate and a large diamond grain size were observed at the edge of the substrate,and their values increased with.The uniformity of film thickness decreased with.The Raman spectra of all samples revealed the first-order characteristic peak of dia-mond near 1332 cm^(−1).When△h=−1 mm,tensile stress occurred in all regions of the film.When△h=1-3 mm,all areas in the film ex-hibited compressive stress.

Evaluation on residual stresses of silicon-doped CVD diamond films using X-ray diffraction and Raman spectroscopy

The effect of silicon doping on the residual stress of CVD diamond films is examined using both X-ray diffraction (XRD) analysis and Raman spectroscopy measurements. The examined Si-doped diamond films are deposited on WC-Co substrates in a home-made bias-enhanced HFCVD apparatus. Ethyl silicate (Si(OC2H5)4) is dissolved in acetone to obtain various Si/C mole ratio ranging from 0.1% to 1.4% in the reaction gas. Characterizations with SEM and XRD indicate increasing silicon concentration may result in grain size decreasing and diamond [110] texture becoming dominant. The residual stress values of as-deposited Si-doped diamond films are evaluated by both sin2ψ method, which measures the (220) diamond Bragg diffraction peaks using XRD, with ψ-values ranging from 0° to 45°, and Raman spectroscopy, which detects the diamond Raman peak shift from the natural diamond line at 1332 cm-1. The residual stress evolution on the silicon doping level estimated from the above two methods presents rather good agreements, exhibiting that all deposited Si-doped diamond films present compressive stress and the sample with Si/C mole ratio of 0.1% possesses the largest residual stress of ~1.75 GPa (Raman) or ~2.3 GPa (XRD). As the silicon doping level is up further, the residual stress reduces to a relative stable value around 1.3 GPa.

Effect of deposition parameters on micro-and nano-crystalline diamond films growth on WC-Co substrates by HFCVD

The characteristics of hot filament chemical vapor deposition（HFCVD） diamond films are significantly influenced by the deposition parameters, such as the substrate temperature, total pressure and carbon concentration. Orthogonal experiments were introduced to study the comprehensive effects of such three parameters on diamond films deposited on WC-Co substrates. Field emission scanning electron microscopy, atomic force microscopy and Raman spectrum were employed to analyze the morphology, growth rate and composition of as-deposited diamond films. The morphology varies from pyramidal to cluster features with temperature decreasing. It is found that the low total pressure is suitable for nano-crystalline diamond films growth. Moreover, the substrate temperature and total pressure have combined influence on the growth rate of the diamond films.

Enhancement of nucleation of diamond films deposited on copper substrate by nickel modification layer

A Ni layer with a thickness of about 100 nm was sputtered on Cu substrates,followed by an ultrasonic seeding with nanodiamond suspension.High-quality diamond film with its crystalline grains close to thermal equilibrium shape was deposited on Cu substrates by hot-filament chemical vapor deposition（HF-CVD）,and the sp2 carbon content was less than 5.56%.The nucleation and growth of diamond film were investigated by micro-Raman spectroscopy,scanning electron microscopy,and X-ray diffraction.The results show that the nucleation density of diamond on the Ni-modified Cu substrates is 10 times higher than that on blank Cu substrates.The enhancement mechanism of the nucleation kinetics by Ni modification layer results from two effects：namely,the nanometer rough Ni-modified surface shows an improved absorption of nanodiamond particles that act as starting points for the diamond nucleation during HF-CVD process;the strong catalytic effect of the Ni-modified surface causes the formation of graphite layer that acts as an intermediate to facilitate diamond nucleation quickly.

Effects of deposition parameters on HFCVD diamond films growth on inner hole surfaces of WC-Co substrates

Deposition parameters that have great influences on hot filament chemical vapor deposition (HFCVD) diamond films growth on inner hole surfaces of WC?Co substrates mainly include the substrate temperature (t), carbon content (φ), total pressure (p) and total mass flow (F). Taguchi method was used for the experimental design in order to study the combined effects of the four parameters on the properties of as-deposited diamond films. A new figure-of-merit (FOM) was defined to assess their comprehensive performance. It is clarified thatt,φandp all have significant and complicated effects on the performance of the diamond film and the FOM, which also present some differences as compared with the previous studies on CVD diamond films growth on plane or external surfaces. Aiming to deposit HFCVD diamond films with the best comprehensive performance, the key deposition parameters were finally optimized as:t=830 °C,φ=4.5%,p=4000 Pa,F=800 mL/min.

DIAMOND FILMS DEPOSITED AT LOW TEMPERATURES MICROWAVE PLASMA-ASSISTED CVD METHOD

Low-temperature deposition of diamond thin films in the range of 280￣445℃ has been successfully carried out by microwave plasma-assisted CVD method.At lower deposition temperatures (280￣445℃),the large increase in the nucleation density and great improvement in the average surfae roughness of the diamond were observed. Results of low temperature deposition and characterization of diamond thin films obtained are presented.

Preparation, characterization and electrochemical properties of boron-doped diamond films on Nb substrates

A series of boron-doped polycrystalline diamond films were prepared by hot filament （HF） chemical vapor deposition on Nb substrates. The effects of B/C ratio of reaction gas on film morphology, growth rate, chemical bonding states, phase composition and electrochemical properties of each deposited sample were studied by scanning electron microscopy, Raman spectra, X-ray diffraction, microhardness indentation, and electrochemical analysis. Results show that the average grain size of diamond and the growth rate decrease with increasing the B/C ratio. The diamond films exhibit excellent adhesion under Vickers microhardness testing （9.8 N load）. The sample with 2% B/C ratio has a wider potential window and a lower background current as well as a faster redox reaction rate in H2SO4 solution and KFe（CN）6 redox system compared with other doping level electrodes.

EFFECT OF GRID BIAS ON DEPOSITION OF NANOCRYSTALLINE DIAMOND FILMS

A positive grid bias and a negative substrate bias voltages are applied to the self-made hot filament chemical vapor deposited （HFCVD） system. The high quality nanocrystalline diamond （NCD） film is successfully deposited by double bias voltage nucleation and grid bias voltage growth. The Micro-Raman XRD SEM and AFM are used to investigate the diamond grain size, microstructure, surface morphology, and nucleation density. Results show that the obtained NCD has grain size of about 20 nm. The effect of grid bias voltage on the nucleation and the diamond growth is studied. Experimental results and theoretical analysis show that the positive grid bias increases the plasma density near the hot filaments, enhances the diamond nucleation, keeps the nanometer size of the diamond grains, and improves the quality of diamond film.

Amorphous SiO_2 interlayers for deposition of adherent diamond films onto WC-Co inserts

Amorphous Si O2（a-Si O2） films were synthesized on WC-Co substrates with H2 and tetraethoxysilane（TEOS） via pyrolysis of molecular precursor.X-ray diffraction（XRD） pattern shows that silicon-cobalt compounds form at the interface between a-Si O2 films and WC-Co substrates.Moreover,it is observed by transmission electron microscope（TEM） that the a-Si O2 films are composed of hollow mirco-spheroid a-Si O2 particles.Subsequently,the a-Si O2 films are used as intermediate films and chemical vapor deposition（CVD） diamond films are deposited on them.Indentation tests were performed to evaluate the adhesion of bi-layer（a-Si O2 ＋ diamond） films on cemented carbide substrates.And the cutting performance of bi-layer（a-Si O2 ＋ diamond） coated inserts was evaluated by machining the glass fiber reinforced plastic（GFRP）.The results show that a-Si O2 interlayers can greatly improve the adhesive strength of diamond films on cemented carbide inserts;furthermore,thickness of the a-Si O2 interlayers plays a significant role in their effectiveness on adhesion enhancement of diamond films.

Si-doped diamond films prepared by chemical vapour deposition

The effects of Si doping on morphology, components and structure characteristics of CVD diamond films were studied. Si-doped CVD diamond films were deposited on Si substrate by adding tetraethoxysilane （TEOS） into acetone as source of reactant gas. The morphology and microstructure of diamond films were characterized by scanning electron microcopy （SEM）. The crystalline quality of diamond films was studied by Raman spectroscopy and X-ray diffractometry （XRD）. The surface roughness of the films was evaluated with surface profilometer. The results suggest that Si doping tends to reduce the crystallite size, enhance grain refinement and inhibit the appearance of （11 I） facets. Raman spectra indicate that Si doping can enhance the formation of sp2 phase in diamond films. Moreover, Raman signal of SiC was detected, which suggests the existence of Si in the diamond films. Smooth fine-grained diamond （SFGD） film was synthesized at Si to C ratio of 1%.

Microscopic mechanical characteristics analysis of ultranano-crystalline diamond films

The microscopic mechanical characteristics of ultranano-crystalline diamond films which were prepared in four different atmospheres were investigated for the applications in microelectron-mechanical system（MEMS）.The loading-unloading curves and the change of modulus and hardness of samples along with depth were achieved through nanoindenter.The results show that the films which are made in atmosphere without Ar have the highest recovery of elasticity,hardness（72.9 GPa） and elastic modulus（693.7 GPa） among the samples.Meanwhile,samples fabricated at a low Ar content have higher hardness and modulus.All the results above demonstrate that atmosphere without Ar or low Ar content leads to better mechanical properties of nanodiamond films that are the candidates for applications in MEMS.

Simulations of the Dependence of Gas Physical Parameters on Deposition Variables during HFCVD Diamond Films

During the growth of the hot filament chemical vapor deposition （HFCVD） diamond films, numerical simulations in a 2-D mathematical model were employed to investigate the influence of various deposition parameters on the gas physical parameters, including the temperature, velocity and volume density of gas. It was found that, even in the case of optimized deposition parameters, the space distributions of gas parameters were heterogeneous due primarily to the thermal blockage come from the hot filaments and cryogenic pump effect arisen from the cold reactor wall. The distribution of volume density agreed well with the thermal round-flow phenomenon, one of the key obstacles to obtaining high growth rate in HFCVD process. In virtue of isothermal boundary with high temperature or adiabatic boundary condition of reactor wall, however, the thermal roundflow was profoundly reduced and as a consequence, the uniformity of gas physical parameters was considerably improved, as identified by the experimental films growth.

Effect of deposition temperature on properties of boron-doped diamond films on tungsten carbide substrate

Boron-doped diamond(BDD)films were deposited on the tungsten carbide substrates at different substrate temperatures ranging from 450 to 850°C by hot filament chemical vapor deposition(HFCVD)method.The effect of deposition temperature on the properties of the boron-doped diamond films on tungsten carbide substrate was investigated.It is found that boron doping obviously enhances the growth rate of diamond films.A relatively high growth rate of 544 nm/h was obtained for the BDD film deposited on the tungsten carbide at 650°C.The added boron-containing precursor gas apparently reduced activation energy of film growth to be 53.1 kJ/mol,thus accelerated the rate of deposition chemical reaction.Moreover,Raman and XRD analysis showed that heavy boron doping(750 and 850°C)deteriorated the diamond crystallinity and produced a high defect density in the BDD films.Overall,600-700°C is found to be an optimum substrate temperature range for depositing BDD films on tungsten carbide substrate.

Microwave Plasma Chemical Vapor Deposition of Diamond Films on Silicon From Ethanol and Hydrogen

Diamond films with very smooth surface and good optical quality have been deposited onto silicon substrate using microwave plasma chemical vapor deposition (MPCVD) from a gas mixture of ethanol and hydrogen at a low substrate temperature of 450 ℃. The effects of the substrate temperature on the diamond nucleation and the morphology of the diamond film have been investigated and observed with scanning electron microscopy (SEM). The microstructure and the phase of the film have been characterized using Raman spectroscopy and X-ray diffraction (XRD). The diamond nucleation density significantly decreases with the increasing of the substrate temperature. There are only sparse nuclei when the substrate temperature is higher than 800 ℃ although the ethanol concentration in hydrogen is very high. That the characteristic diamond peak in the Raman spectrum of a diamond film prepared at a low substrate temperature of 450 ℃ extends into broadband indicates that the film is of nanophase. No graphite peak appeared in the XRD pattern confirms that the film is mainly composed of SP3 carbon. The diamond peak in the XRD pattern also broadens due to the nanocrystalline of the film.

Effects of Alcohol Addition on the Deposition of Diamond Thick Films by dc Plasma Chemical Vapor Deposition Method

Diamond films have been deposited by dc plasma chemical vapor deposition method.The addition of alcohol in the resource gas largely increases the deposition rate.The effects of alcohol addition on deposition rate and film quality are analyzed by scanning electron microscopy and Raman spectrometry.The mechanism of experimental phenomena is discussed.

Deposition of crackless freestanding diamond films on Mo substrates with Zr interlayer

The Mo substrate with Zr interlayer,namely composite substrate,was employed to solve the problem of crack formation in the freestanding diamond film deposition.Freestanding diamond films deposited on the composite substrates by the direct current arc plasma jet chemical vapor deposition（CVD） method were investigated with scanning electron microscopy（SEM）,X-ray photoelectron spectroscopy （XPS）,X-ray diffraction（XRD）,and Raman spectroscopy.In addition,the stress distribution during the large area freestanding diamond film deposition on the composite substrate was analyzed based on the finite element model ANSYS.The results reveal that Zr interlayer can be easily destroyed during the post-deposition cooling process,which is helpful for stress release and crack avoiding in diamond films.

A novel approach of deposition for uniform diamond films on circular saw blades

Uniform diamond films are highly desirable for cutting industries, due to their high performance and long lifetime used on cutting tools. Nevertheless, they are difficult to obtain on cutting tools with complicated shapes, greatly limiting the applications of diamond films. In this study, a novel approach of deposition for uniform diamond films is proposed, on circular saw blades made of cemented carbide using reflectors of brass sheets. Diamond films are deposited using hot filament chemical vapor deposition（HFCVD）. A novel concave structure of brass sheets is designed and fabricated, improving the distribution of temperature field, and overcoming the disadvantages of the conventional HFCVD systems. This increases the energy efficiency of use without changing the structure and increasing the cost of HFCVD. The grains are refined and the intensities of diamond peaks are strengthened obviously, which is confirmed by scanning electron microscopy and Raman spectra respectively.

OES study of the gas phase during diamond films deposition in high power DC arc plasma jet CVD system

This paper used optical emission spectroscopy （OES） to study the gas phase in high power DC arc plasma jet chemical vapour deposition （CVD） during diamond films growth processes. The results show that all the deposition parameters （methane concentration, substrate temperature, gas flow rate and ratio of H2/Ar） could strongly influence the gas phase. C2 is found to be the most sensitive radical to deposition parameters among the radicals in gas phase. Spatially resolved OES implies that a relative high concentration of atomic H exists near the substrate surface, which is beneficial for diamond film growth. The relatively high concentrations of C2 and CH are correlated with high deposition rate of diamond. In our high deposition rate system, C2 is presumed to be the main growth radical, and CH is also believed to contribute the diamond deposition.

Blue-Green Electroluminescence of Free-Standing Diamond Thin Films

Blue-green electroluminescence has been observed in free-standing diamond films which were deposited by microwave plasma assisted CVD on silicon substrates.The electroluminescence device is driven by a 60 Hz power supply.The threshold voltage was about 112 V peak-to-peak.The electroluminescence spectrum at room temperature,showed a blue-green band with the peak centered at 485nm suggesting band A type emission.Electroluminescence was also observed at 77K.

Mechanism and prediction of failure of diamond films deposited on various substrates by HFCVD

Diamond films were deposited on the WC-Co cemented carbide and Si3N4 ceramic cutting tool substrates by hot-filament-assisted chemical vapour deposition. The adherence property of diamond films was estimated using the critical load (Pcr) in the indentation test. The adhesive strength of diamond films is related to the intermediate layer between the film and the substrate. Poor adhesion of diamond films to polished cemented carbide substrate is owing to the formation of graphite phase in the interface. The adhesion of diamond films deposited on acid etched cemented carbide substrate is improved, and the peeling-off of the films often happens in the loosen layer of WC particles where the cobalt element is nearly removed. The diamond films' adhesion to cemented carbide substrate whose surface layer is decarbonizated is strengthened dramatically because WC phase forms by reaction between the deposited carbon and tungsten in the surface layer of substrates during the deposition of diamond, which results in chemical combination in the film-substrate interface. The adhesion of diamond films to silicon nitride substrate is the firmest due to the formation of chemical combination of the SiC intermediate layer in the interfaces. In the piston-turning application, the diamond-coated Si3N4 ceramic and the cemented carbide cutting tools usually fail in the form of collapsing of edge and cracking or flaking respectively. They have no built-up edge(BUE) as long as coating is intact.As it wears through, BUE develops and the cutting force on it increases 1 - 3 times than that prior to failure. This can predict the failure of diamond-coated cutting tools.