The effects of yttrium and cerium on the compression properties of Ni_3Al-base alloys have been investigated.The results reveal that the addition of about 0.1 wt% Y to Ni_3Al-B alloy is effective for improving the duc...The effects of yttrium and cerium on the compression properties of Ni_3Al-base alloys have been investigated.The results reveal that the addition of about 0.1 wt% Y to Ni_3Al-B alloy is effective for improving the ductility at 1100℃.A ductility increase of about 100% is observed for this Y doped alloy.The yttrium re- fines grains of the alloy.An YNi_5 phase is found to be precipitated on the grain boundaries in the alloy con- taining 0.3 wt% Yor more.Adding about 0.1 wt% Ce to Ni_3Al-B-Cr-Zr alloy obviously improves the ductility of the alloy at 1100℃.A ductility increase of about 50% is obtained for this alloy.The added cerium also pre- vents the formation of γ+γ' eutectic and refines it.The bulk phase of CeNi_4 appeares at the front of the eutectic in the alloys containing 0.1 wt% Ce or more.展开更多
文摘The effects of yttrium and cerium on the compression properties of Ni_3Al-base alloys have been investigated.The results reveal that the addition of about 0.1 wt% Y to Ni_3Al-B alloy is effective for improving the ductility at 1100℃.A ductility increase of about 100% is observed for this Y doped alloy.The yttrium re- fines grains of the alloy.An YNi_5 phase is found to be precipitated on the grain boundaries in the alloy con- taining 0.3 wt% Yor more.Adding about 0.1 wt% Ce to Ni_3Al-B-Cr-Zr alloy obviously improves the ductility of the alloy at 1100℃.A ductility increase of about 50% is obtained for this alloy.The added cerium also pre- vents the formation of γ+γ' eutectic and refines it.The bulk phase of CeNi_4 appeares at the front of the eutectic in the alloys containing 0.1 wt% Ce or more.