Effects of slurry pack cementation temperature on microstructure and wear resistance of Ti-Al co-deposited coating on copper plated nickel layer

In order to improve the wear resistance properties of copper substrate, a layer of electroplated nickel was firstly deposited on copper substrate, subsequently these electroplated specimens were treated by slurry pack cementation process with a slurry pack cementation mixture composed of TiO2 as titanizing source, pure Al powder as aluminzing source and also a reducer for titanizing, an activator of NH4Cl and albumen （egg white） as cohesive agent. The Ti-Al coating was fabricated on the surface of electro-deposited nickel layer on copper matrix followed by the slurry pack cementation process. The effects of slurry pack cementation temperature on the microstructures and wear resistance of Ti-Al coating were studied. The results show that the microstructure of the coating changed from NiAl＋Ni3（Ti,Al） to NiAl ＋Ni3（Ti,Al）＋Ni4Ti3 to Ni4Ti3＋NiAl, and to NiAl＋Ni3（Ti,Al）＋NiTi with slurry pack cementation temperature ranging from 800 ℃ to 950 ℃ in 12 h. The friction coefficient of Ti-Al coating decreased and the hardness increased with increasing the slurry pack cementation temperature. The minimum friction coefficient was 1/3 and the minimum hardness was 5 times larger than that of pure copper.

Comparison of Temperature Field Distribution between Cement Preclinkering Technology and Cement Precalcining Technology

Through the comparison of calcination conditions between cement preclinkering technology and cement precalcining technology,we studied the characteristics of temperature field distribution of cement preclinkering technology systems including cyclone preheater,preclinkering furnace,and rotary kiln.We used numericalsimulation method to obtain data of temperature field distribution.Some results are found by system study.The ratio of tailcoalof cement preclinkering technology is about 70%,and raw mealtemperature can reach 1070 ℃.Shorter L/D kiln type of preclinkering technology can obtain more stable calcining zone temperature.The highest solid temperature of cement preclinkering technology is higher than 80 ℃,and high temperature region（〉1450 ℃）length is 2 times,which is beneficialfor calcining clinker and higher clinker quality.So cement preclinkering technology can obtain more performance temperature filed,which improves both the solid-phase reaction and liquid-phase reaction.