The activity and thermal stability of Pd/Al2O3 and Pd/（Al2O3＋MOx） （M=Ca, La, Ce） palladium catalysts in the reaction of complete oxidation of methane are presented in this study. The catalyst supports were prepar...The activity and thermal stability of Pd/Al2O3 and Pd/（Al2O3＋MOx） （M=Ca, La, Ce） palladium catalysts in the reaction of complete oxidation of methane are presented in this study. The catalyst supports were prepared by sol-gel method and they were dried either conventionally or with supercritical carbon dioxide. Then they were impregnated with palladium nitrate solution. The catalysts with unmodified alumina had a high surface area. The activity and thermal stability of the aluminasupported catalyst was also very high. The introduction of calcium, lanthanum, or cerium oxide into alumina support caused a decrease of the surface area in the way dependent on the support precursor drying method. These modifiers decreased the activity of palladium catalysts, and they required higher temperatures for the complete oxidation of methane than unmodified Pd/Al2O3. The improvement of the palladium activity by lanthanum and cerium support modifier was observed only at low temperatures of the reaction.展开更多
The compound nano-ZnO modified with Ce was prepared by homogeneous precipitation.IR,XRD and dynamic experiments show that the crystal size of nano-ZnO desulfurizer is decreased after being modified with Ce and its des...The compound nano-ZnO modified with Ce was prepared by homogeneous precipitation.IR,XRD and dynamic experiments show that the crystal size of nano-ZnO desulfurizer is decreased after being modified with Ce and its desulfurization activities are improved greatly.When calcined at 270 ℃,Ce distributes evenly on the ZnO particle surface as amorphous state oxides,and the amorphous ZnO·H2O also exists;when the calcining temperature is 570 ℃,the crystal CeO2 separates out and the amorphous structure of zinc oxide disappears,at the same time,the crystal is perfect and its size increases,but the desulfurization activities decrease.The desulfurization product of nano-ZnO modified with Ce was analyzed with XPS.The results show that the adsorption compound of HS,S and ZnS exists on the surface of the desulfurizer.展开更多
文摘The activity and thermal stability of Pd/Al2O3 and Pd/（Al2O3＋MOx） （M=Ca, La, Ce） palladium catalysts in the reaction of complete oxidation of methane are presented in this study. The catalyst supports were prepared by sol-gel method and they were dried either conventionally or with supercritical carbon dioxide. Then they were impregnated with palladium nitrate solution. The catalysts with unmodified alumina had a high surface area. The activity and thermal stability of the aluminasupported catalyst was also very high. The introduction of calcium, lanthanum, or cerium oxide into alumina support caused a decrease of the surface area in the way dependent on the support precursor drying method. These modifiers decreased the activity of palladium catalysts, and they required higher temperatures for the complete oxidation of methane than unmodified Pd/Al2O3. The improvement of the palladium activity by lanthanum and cerium support modifier was observed only at low temperatures of the reaction.
基金the National Natural Science Foundation of China(Grant No.50478026)the Science Foundation for Young Scientists of Harbin University of Science and Technology(Grant No.2008XQJZ039)
文摘The compound nano-ZnO modified with Ce was prepared by homogeneous precipitation.IR,XRD and dynamic experiments show that the crystal size of nano-ZnO desulfurizer is decreased after being modified with Ce and its desulfurization activities are improved greatly.When calcined at 270 ℃,Ce distributes evenly on the ZnO particle surface as amorphous state oxides,and the amorphous ZnO·H2O also exists;when the calcining temperature is 570 ℃,the crystal CeO2 separates out and the amorphous structure of zinc oxide disappears,at the same time,the crystal is perfect and its size increases,but the desulfurization activities decrease.The desulfurization product of nano-ZnO modified with Ce was analyzed with XPS.The results show that the adsorption compound of HS,S and ZnS exists on the surface of the desulfurizer.