A series of CexPr1-xO2-δ mixed oxides were synthesized by sol-gel met hod and characterized by Raman and XRD techniques. When x value was changed from 1.0 to 0.5, only a cubic phase CeO2 was observed. The samples wer...A series of CexPr1-xO2-δ mixed oxides were synthesized by sol-gel met hod and characterized by Raman and XRD techniques. When x value was changed from 1.0 to 0.5, only a cubic phase CeO2 was observed. The samples were very well cr ystallized on decreasing x from 0.50 to 0.99. For CexPr1-xO2-δ samples 465 cm-1 and 1 150 cm-1 Raman peaks are attributed to the Raman active F2g mode of CeO2. The broad peak at about 570 cm-1 in the region of 0.3 ≤ x ≤ 0.99 can be linke d to lattice defects resulting in oxygen vacancies. The new band at about 195 cm -1 may be attributed to the asymmetric vibration caused by the formation of oxyg en vacancies. Calcination temperatures had great effect on the peak intensity fo r CeO2 but less effect on Ce0.8Pr0.2O2-δ in Raman spectra. It might be due to t he transformation of the colors for the mixed oxides, the insertion of Pr atom i nto the ceria lattice could enhance the sintering resistance and thermal stabili ty of the mixed oxides.展开更多
In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of t...In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of the high Tc superconductors Gd1Ba2Cu3O7−δ phase with Sr substitution has been synthesized, i.e. Gd1(Ba2−xSrx)Cu3O7−δ compound. The sample was synthesized by using a solid-state reaction method with a wet mixing, sintered for 12 hours at temperature 900°C. The synthesis results are characterized by using XRD. The results of Match-3 software analysis showed high (higher 85%) Gd1Ba2Cu3O7−δ phase was formed. The Sr substitution causes changes to the structure, i.e. the lattice parameters a, b and c, where the orthorhombicity tends to decrease with increasing Sr content. Refinement results show that based on the oxygen occupancy, the total oxygen content tends to increase.展开更多
文摘A series of CexPr1-xO2-δ mixed oxides were synthesized by sol-gel met hod and characterized by Raman and XRD techniques. When x value was changed from 1.0 to 0.5, only a cubic phase CeO2 was observed. The samples were very well cr ystallized on decreasing x from 0.50 to 0.99. For CexPr1-xO2-δ samples 465 cm-1 and 1 150 cm-1 Raman peaks are attributed to the Raman active F2g mode of CeO2. The broad peak at about 570 cm-1 in the region of 0.3 ≤ x ≤ 0.99 can be linke d to lattice defects resulting in oxygen vacancies. The new band at about 195 cm -1 may be attributed to the asymmetric vibration caused by the formation of oxyg en vacancies. Calcination temperatures had great effect on the peak intensity fo r CeO2 but less effect on Ce0.8Pr0.2O2-δ in Raman spectra. It might be due to t he transformation of the colors for the mixed oxides, the insertion of Pr atom i nto the ceria lattice could enhance the sintering resistance and thermal stabili ty of the mixed oxides.
基金This report is part of the fundamental research report with contract No.486 127/UN14.2/PNL.01.03.00/2016.
文摘In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of the high Tc superconductors Gd1Ba2Cu3O7−δ phase with Sr substitution has been synthesized, i.e. Gd1(Ba2−xSrx)Cu3O7−δ compound. The sample was synthesized by using a solid-state reaction method with a wet mixing, sintered for 12 hours at temperature 900°C. The synthesis results are characterized by using XRD. The results of Match-3 software analysis showed high (higher 85%) Gd1Ba2Cu3O7−δ phase was formed. The Sr substitution causes changes to the structure, i.e. the lattice parameters a, b and c, where the orthorhombicity tends to decrease with increasing Sr content. Refinement results show that based on the oxygen occupancy, the total oxygen content tends to increase.