A thermal fatigue behaviour of Co-based alloy coating obtained by laser surface meltcasting on the high temperature alloy GH33 was studied.The results show that after each time of thermal cycling,the final residual st...A thermal fatigue behaviour of Co-based alloy coating obtained by laser surface meltcasting on the high temperature alloy GH33 was studied.The results show that after each time of thermal cycling,the final residual stress was formed in the melt-casting layer which is attributed to the thermal stress and structural stress.Through the first 50 times of thermal cycling,the morphology of coating still inherits the laser casting one,but the dendrites get bigger;After the second 50 times of thermal cycling,corrosion pits emerge from coating,and mostly in the places where coating and substrate meet.The fatigue damage type of coating belongs to stress corrosion.展开更多
基金Project Sponsored by Committee on Science and Technology of Guizhou Province(943068)
文摘A thermal fatigue behaviour of Co-based alloy coating obtained by laser surface meltcasting on the high temperature alloy GH33 was studied.The results show that after each time of thermal cycling,the final residual stress was formed in the melt-casting layer which is attributed to the thermal stress and structural stress.Through the first 50 times of thermal cycling,the morphology of coating still inherits the laser casting one,but the dendrites get bigger;After the second 50 times of thermal cycling,corrosion pits emerge from coating,and mostly in the places where coating and substrate meet.The fatigue damage type of coating belongs to stress corrosion.