One Step Hydrothermal Synthesis of Flower-shaped CO3O4 Nanorods on Nickel Foam as Supercapacitor Materials and Their Excellent Electrochemical Performance
1
作者 WANG Chen MENG Yanshuang +2 位作者 WANG Lei ZHU Fuliang ZHANG Yue 《Chemical Research in Chinese Universities》 SCIE CAS CSCD 2018年第6期882-886,共5页
Flower-shaped Co3O4 nanorods directly grown on nickel foam(Co3O4/NF) were prepared by one step hy-drothermal method at low temperature. Co3O4 nanorods are directly connected with the nickel foam, and no binder is ne... Flower-shaped Co3O4 nanorods directly grown on nickel foam(Co3O4/NF) were prepared by one step hy-drothermal method at low temperature. Co3O4 nanorods are directly connected with the nickel foam, and no binder is needed as an additive, so the Co3O4NF electrode has good electrical conductivity. This flower-shaped structure makes larger surface area of Co3O4 nanorods that exposes to the electrolyte, thus promoting the redox reaction. The Co3O4/NF electrode shows a high specific capacitance of 2005.34 F/g at the current density of 0.5 A/g and a high capacitance retention of 98.0% after 5000 cycles. The high superior capacitive performance with high specific capacitance and the excellent cyclic performance indicate that the one step hydrothermal method has great potential application in supercapacitors. 展开更多
关键词 supercapacitor co3o4/NF hydrothermal Nanorod
原文传递
微波辅助水热法反应参数对NaYF_(4):Dy^(3+)晶相、形貌、发光性能的影响 被引量:1
2
作者 高端 程丽红 +5 位作者 陈宝玖 刘盛意 李香萍 孙佳石 徐赛 张金苏 《无机化学学报》 SCIE CAS CSCD 北大核心 2019年第9期1623-1634,共12页
采用微波辅助水热法快速制备了可重复性良好的NaYF4∶Dy^3+样品,研究了一系列反应参数对NaYF4∶Dy^3+晶相、形貌、发光性能的影响。结果表明微波水热反应时间长短并未对产物的晶相、形貌、光谱性能产生明显的影响。Dy^3+掺杂浓度的增加... 采用微波辅助水热法快速制备了可重复性良好的NaYF4∶Dy^3+样品,研究了一系列反应参数对NaYF4∶Dy^3+晶相、形貌、发光性能的影响。结果表明微波水热反应时间长短并未对产物的晶相、形貌、光谱性能产生明显的影响。Dy^3+掺杂浓度的增加并未改变样品晶相、形貌和尺寸,但发光强度发生改变,发光强度的变化趋势为先增大后减小,当Dy^3+掺杂浓度(物质的量分数)为1%时发光强度最强。根据具体的理论依据获得的电多极相互作用指数为6,表明Dy^3+之间的相互作用为电偶极-电偶极相互作用。研究了表面活性剂的种类与量对NaYF4∶Dy^3+晶相的影响。当使用柠檬酸钠和CTAB作为表面活性剂时,可制备得到六方相NaYF4∶Dy^3+。增加柠檬酸钠和CTAB的量,样品晶相未发生改变。使用EDTA-2Na作为表面活性剂时,随着EDTA-2Na量的不断增加发生从六方相到立方相晶相的转变。3种表面活性剂使用量不断增加后样品均出现尺寸减小现象。合成的一系列NaYF4∶Dy^3+荧光粉均在350nm紫外光激发下,出现Dy^3+特征峰。蓝光发射中心为479 nm,对应于Dy^3+的4F9/2→6H15/2跃迁;绿光发射中心为572 nm,对应于Dy3+的4F9/2→6H13/2跃迁,样品可实现蓝、绿发光。 展开更多
关键词 微波辅助水热法 反应时间 Dy^(3+)掺杂浓度 柠檬酸钠 CTAB EDTA-2Na