Fe_(3)O_(4)and Cu_(2)O were successively immobilized on alkali-treated straw,and the magnetically separable straw@Fe_(3)O_(4)/Cu_(2)O composite was obtained.The straw@Fe_(3)O_(4)/Cu_(2)O was characterized by Fourier t...Fe_(3)O_(4)and Cu_(2)O were successively immobilized on alkali-treated straw,and the magnetically separable straw@Fe_(3)O_(4)/Cu_(2)O composite was obtained.The straw@Fe_(3)O_(4)/Cu_(2)O was characterized by Fourier transform infrared spectroscopy,X-ray diffraction,scanning electron microscopy,X-ray photoelectron spectroscopy and vibrating sample magnetometry,respectively.Photocatalytic performance of the straw@Fe_(3)O_(4)/Cu_(2)O was evaluated by measuring the degradation of methyl orange(MO)under irradiation of visible light.The introduction of Fe3O4 not only endowed the straw@Fe_(3)O_(4)/Cu_(2)O with magnetic separation feature but also significantly enhanced photocatalytic activity because Fe3O4 could prevent recombination of hole-electron pairs.The active species capture experiment showed that holes(h+),hydroxyl(∙OH)and superoxide(∙O2ˉ)radicals all took part in the MO degradation.In addition,the photocatalytic mechanism of straw@Fe_(3)O_(4)/Cu_(2)O was proposed based on the experimental results.After five cycles for the photodegradation of MO,the straw@Fe_(3)O_(4)/Cu_(2)O still displayed good photocatalytic activity,suggesting that the as-prepared composite had great potential for practical use in wastewater treatment.展开更多
Aluminium matrix composite reinforced by Al2O3 particles was produced by adding NH4AlO（OH）HCO3 into molten aluminum.The mechanical properties and wear behavior of the as-fabricated composites were studied.The result...Aluminium matrix composite reinforced by Al2O3 particles was produced by adding NH4AlO（OH）HCO3 into molten aluminum.The mechanical properties and wear behavior of the as-fabricated composites were studied.The results show that during stirring γ-Al2O3 particles were formed via decomposition reaction of NH4AlO（OH）HCO3,and the distribution of Al2O3 particles is more uniform in the matrix aluminum than directly added Al2O3 into molten aluminum.The density and the hardness values of the as-fabricated composites increase with increasing the particle volume fraction,while the tensile strength of the composites decreases with increasing the volume fraction of the Al2O3 particles.The wear rate of the composites decreases with increasing the volume fraction of the particle and loading.The in situ formed Al2O3/Al composite by adding NH4AlO（OH）HCO3 shows more superior mechanical and wear behaviors than that prepared by directly adding Al2O3 particles.展开更多
基金Science and Technology Project from Ministry of Housing and Urban-Rural Development of the People’s Republic of China(No.2014-K7-007)。
文摘Fe_(3)O_(4)and Cu_(2)O were successively immobilized on alkali-treated straw,and the magnetically separable straw@Fe_(3)O_(4)/Cu_(2)O composite was obtained.The straw@Fe_(3)O_(4)/Cu_(2)O was characterized by Fourier transform infrared spectroscopy,X-ray diffraction,scanning electron microscopy,X-ray photoelectron spectroscopy and vibrating sample magnetometry,respectively.Photocatalytic performance of the straw@Fe_(3)O_(4)/Cu_(2)O was evaluated by measuring the degradation of methyl orange(MO)under irradiation of visible light.The introduction of Fe3O4 not only endowed the straw@Fe_(3)O_(4)/Cu_(2)O with magnetic separation feature but also significantly enhanced photocatalytic activity because Fe3O4 could prevent recombination of hole-electron pairs.The active species capture experiment showed that holes(h+),hydroxyl(∙OH)and superoxide(∙O2ˉ)radicals all took part in the MO degradation.In addition,the photocatalytic mechanism of straw@Fe_(3)O_(4)/Cu_(2)O was proposed based on the experimental results.After five cycles for the photodegradation of MO,the straw@Fe_(3)O_(4)/Cu_(2)O still displayed good photocatalytic activity,suggesting that the as-prepared composite had great potential for practical use in wastewater treatment.
基金Project(2009BAE80B01)supported by the Ministry of Science and Technology,China
文摘Aluminium matrix composite reinforced by Al2O3 particles was produced by adding NH4AlO（OH）HCO3 into molten aluminum.The mechanical properties and wear behavior of the as-fabricated composites were studied.The results show that during stirring γ-Al2O3 particles were formed via decomposition reaction of NH4AlO（OH）HCO3,and the distribution of Al2O3 particles is more uniform in the matrix aluminum than directly added Al2O3 into molten aluminum.The density and the hardness values of the as-fabricated composites increase with increasing the particle volume fraction,while the tensile strength of the composites decreases with increasing the volume fraction of the Al2O3 particles.The wear rate of the composites decreases with increasing the volume fraction of the particle and loading.The in situ formed Al2O3/Al composite by adding NH4AlO（OH）HCO3 shows more superior mechanical and wear behaviors than that prepared by directly adding Al2O3 particles.