Magneto-dielectric properties of Co_(2)Z ferrite materials are tuned via Gd doping for applications in high-frequency antennas and filters in the present work.Ba_(3)Co_(2)Fe_(24-x)Gd_(x)O_(41)(x=0.00,0.05,0.10,0.15,an...Magneto-dielectric properties of Co_(2)Z ferrite materials are tuned via Gd doping for applications in high-frequency antennas and filters in the present work.Ba_(3)Co_(2)Fe_(24-x)Gd_(x)O_(41)(x=0.00,0.05,0.10,0.15,and 0.20)materials are successfully prepared by using solid-state method at 925℃for 4 h with 2.5-wt%Bi_(2)O_(3)sintering aids.The content of Gd^(3+)ion can affect micromorphology,grain size,bulk density,and magneto-dielectric properties of the ferrite.With Gd^(3+)ion content increasing,saturation magnetization(Ms)first increases and then decreases.The maximum value of Ms is 44.86 emu/g at x=0.15.Additionally,sites occupied by Gd^(3+)ions can change magnetic anisotropy constant of the ferrite.Magnetocrystalline anisotropy constant(K_1)is derived from initial magnetization curve,and found to be related to spin-orbit coupling and intersublattice interactions between metal ions.The real part of magnetic permeability(μ′)and real part of dielectric permittivity(ε′)are measured in a frequency range of 10 MHz-1 GHz.When x=0.15,material has excellent magneto-dielectric properties(μ′≈12.2 andε′≈17.61),low magnetic loss(tanδμ≈0.03 at 500 MHz),and dielectric loss(tanδε≈0.04 at 500 MHz).The results show that Gd-doped Co_(2)Z ferrite has broad application prospects in multilayer filters and high-frequency antennas.展开更多
Stro ntium-doped lanthanum ferrite(LSF)is a potential ceramic cathode for direct CO_(2) electrolysis in solid oxide electrolysis cells(SOECs),but its application is limited by insufficient catalytic activity and stabi...Stro ntium-doped lanthanum ferrite(LSF)is a potential ceramic cathode for direct CO_(2) electrolysis in solid oxide electrolysis cells(SOECs),but its application is limited by insufficient catalytic activity and stability in CO_(2)-containing atmospheres.Herein,a novel strategy is proposed to enhance the electrolytic performance as well as chemical stability,achieved by doping F into the O-site of the perovskite LSF.Doping F does not change the phase structure but reduces the cell volume and improves the chemical stability in a CO_(2)-rich atmosphere.Importantly,F doping favors oxygen vacancy formation,increases oxygen vacancy concentration,and enhances the CO_(2) adsorption capability.Meanwhile,doping with F greatly improves the kinetics of the CO_(2) reduction reaction.For example,kchem increases by 78%from3.49×10^(-4) cm s^(-1) to 6.24×10^(-4) cm s^(-1),and Dchem doubles from 4.68×10^(-5) cm^(2) s^(-1) to 9.45×10^(-5)cm^(2) s^(-1).Consequently,doping F significantly increases the electrochemical performance,such as reducing R_(p) by 52.2%from 0.226Ωcm^(2) to 0.108Ωcm^(2) at 800℃.As a result,the single cell with the Fcontaining cathode exhibits an extremely high current density of 2.58 A cm^(-2) at 800℃and 1.5 V,as well as excellent durability over 200 h for direct CO_(2) electrolysis in SOECs.展开更多
Layered cathode materials have been successfully commercialized and applied to electric vehicles.To further improve improve the energy density of these marterials is still the main efforts in the market.Therefore,deve...Layered cathode materials have been successfully commercialized and applied to electric vehicles.To further improve improve the energy density of these marterials is still the main efforts in the market.Therefore,developing high-voltage LiNi_(x)Co_(y)Mn_(z)O_(2)(x+y+z=1,NCM)to achieve high energy density is particularly important.However,under high voltage cycling,NCM often exhibits rapid capacity degradation,which can be attributed to oxygen release,structural phase transition and particle cracking.In this work,the representative single-crystal LiNi_(0.5)Co_(0.2)Mn_(0.3)O_(2)(NCM523)was studied under various high charge cut-off voltages.Analysis by x-ray diffraction(XRD),transmission electron microscope(TEM)and electron back scatter diffraction(EBSD)measurements indicated that the rock-salt phase is formed on the surface of the particles after high voltage cycling,which is responsible for the increase of impedance and the rapid decay of capacity.Therefore,inhibiting the formation of rock-salt phase is believed an effective strategy to address the failure of NCM under high voltages.These findings provide effective guidance for the development of high-voltage NCM.展开更多
基金the National Key Research and Development Program of China(Grant No.2022YFB3504800)the National Natural Science Foundation of China(Grant Nos.61901142,52003256,and 51902037)the Natural Science Foundation of Shanxi Province,China(Grant No.201901D211259)。
文摘Magneto-dielectric properties of Co_(2)Z ferrite materials are tuned via Gd doping for applications in high-frequency antennas and filters in the present work.Ba_(3)Co_(2)Fe_(24-x)Gd_(x)O_(41)(x=0.00,0.05,0.10,0.15,and 0.20)materials are successfully prepared by using solid-state method at 925℃for 4 h with 2.5-wt%Bi_(2)O_(3)sintering aids.The content of Gd^(3+)ion can affect micromorphology,grain size,bulk density,and magneto-dielectric properties of the ferrite.With Gd^(3+)ion content increasing,saturation magnetization(Ms)first increases and then decreases.The maximum value of Ms is 44.86 emu/g at x=0.15.Additionally,sites occupied by Gd^(3+)ions can change magnetic anisotropy constant of the ferrite.Magnetocrystalline anisotropy constant(K_1)is derived from initial magnetization curve,and found to be related to spin-orbit coupling and intersublattice interactions between metal ions.The real part of magnetic permeability(μ′)and real part of dielectric permittivity(ε′)are measured in a frequency range of 10 MHz-1 GHz.When x=0.15,material has excellent magneto-dielectric properties(μ′≈12.2 andε′≈17.61),low magnetic loss(tanδμ≈0.03 at 500 MHz),and dielectric loss(tanδε≈0.04 at 500 MHz).The results show that Gd-doped Co_(2)Z ferrite has broad application prospects in multilayer filters and high-frequency antennas.
基金supported by the National Key R&D Program of China(2021YFB4001401)the National Natural Science Foundation of China(51972298)。
文摘Stro ntium-doped lanthanum ferrite(LSF)is a potential ceramic cathode for direct CO_(2) electrolysis in solid oxide electrolysis cells(SOECs),but its application is limited by insufficient catalytic activity and stability in CO_(2)-containing atmospheres.Herein,a novel strategy is proposed to enhance the electrolytic performance as well as chemical stability,achieved by doping F into the O-site of the perovskite LSF.Doping F does not change the phase structure but reduces the cell volume and improves the chemical stability in a CO_(2)-rich atmosphere.Importantly,F doping favors oxygen vacancy formation,increases oxygen vacancy concentration,and enhances the CO_(2) adsorption capability.Meanwhile,doping with F greatly improves the kinetics of the CO_(2) reduction reaction.For example,kchem increases by 78%from3.49×10^(-4) cm s^(-1) to 6.24×10^(-4) cm s^(-1),and Dchem doubles from 4.68×10^(-5) cm^(2) s^(-1) to 9.45×10^(-5)cm^(2) s^(-1).Consequently,doping F significantly increases the electrochemical performance,such as reducing R_(p) by 52.2%from 0.226Ωcm^(2) to 0.108Ωcm^(2) at 800℃.As a result,the single cell with the Fcontaining cathode exhibits an extremely high current density of 2.58 A cm^(-2) at 800℃and 1.5 V,as well as excellent durability over 200 h for direct CO_(2) electrolysis in SOECs.
文摘Layered cathode materials have been successfully commercialized and applied to electric vehicles.To further improve improve the energy density of these marterials is still the main efforts in the market.Therefore,developing high-voltage LiNi_(x)Co_(y)Mn_(z)O_(2)(x+y+z=1,NCM)to achieve high energy density is particularly important.However,under high voltage cycling,NCM often exhibits rapid capacity degradation,which can be attributed to oxygen release,structural phase transition and particle cracking.In this work,the representative single-crystal LiNi_(0.5)Co_(0.2)Mn_(0.3)O_(2)(NCM523)was studied under various high charge cut-off voltages.Analysis by x-ray diffraction(XRD),transmission electron microscope(TEM)and electron back scatter diffraction(EBSD)measurements indicated that the rock-salt phase is formed on the surface of the particles after high voltage cycling,which is responsible for the increase of impedance and the rapid decay of capacity.Therefore,inhibiting the formation of rock-salt phase is believed an effective strategy to address the failure of NCM under high voltages.These findings provide effective guidance for the development of high-voltage NCM.
基金supported by the National Key R&D Program of China(2022YFA1503003)the National Natural Science Foundation of China(U20A20250,21801069 and 91961111)+2 种基金the Natural Science Foundation of Heilongjiang Province(YQ2021B008)the Basic Research Fund of Heilongjiang University in Heilongjiang Province(2022-KYYWF-1036 and 2021-KYYWF-0039)Heilongjiang University Excellent Youth Foundation.