The electrochemical coupling of biomass oxidation and nitrogen conversion presents a potential strategy for high value-added chemicals and nitrogen cycling.Herein,in this work,CuO/Co_(3)O_(4)with heterogeneous interfa...The electrochemical coupling of biomass oxidation and nitrogen conversion presents a potential strategy for high value-added chemicals and nitrogen cycling.Herein,in this work,CuO/Co_(3)O_(4)with heterogeneous interface is successfully constructed as a bifunctional catalyst for the electrooxidation of 5-hydroxymethylfurfural to 2,5-furandicarboxylic acid and the electroreduction of nitrate to ammonia(NH_(3)).The open-circuit potential spontaneous experiment shows that more 5-hydroxymethylfurfural molecules are adsorbed in the Helmholtz layer of the CuO/Co_(3)O_(4)composite,which certifies that the CuO/Co_(3)O_(4)heterostructure is conducive to the kinetic adsorption of 5-hydroxymethylfurfural.In situ electrochemical impedance spectroscopy further shows that CuO/Co_(3)O_(4)has faster reaction kinetics and lower reaction potential in oxygen evolution reaction and 5-hydroxymethylfurfural electrocatalytic oxidation.Moreover,CuO/Co_(3)O_(4)also has a good reduction effect on NO_(3)^(-).The ex-situ Raman spectroscopy shows that under the reduction potential,the metal oxide is reduced,and the generated Cu_(2)O can be used as a new active site for the reaction to promote the electrocatalytic conversion of NO_(3)^(-)to NH_(3) synthesis.This work provides valuable guidance for the synthesis of value-added chemicals by 5-hydroxymethylfurfural electrocatalytic oxidation coupled with NO_(3)^(-)while efficiently producing NH_(3).展开更多
采用沉淀法-水热法合成了电催化Bi_(2)O_(3)-CuO复合材料.利用X-射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线光电子能谱(XPS)等方法对样品的结构和形貌进行了研究.用电化学测试方法对材料电催化性能进行研究,用...采用沉淀法-水热法合成了电催化Bi_(2)O_(3)-CuO复合材料.利用X-射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线光电子能谱(XPS)等方法对样品的结构和形貌进行了研究.用电化学测试方法对材料电催化性能进行研究,用气相色谱和核磁共振氢谱对产物进行分析.电催化实验结果表明,Bi_(2)O_(3)-CuO复合材料的电催化性能及对甲酸盐的选择性远高于Bi_(2)O_(3)和CuO.其中比例为1∶1的Bi_(2)O_(3)-CuO复合材料性能最好,在-1.2 V vs.RHE的电位下,甲酸盐的法拉第效率为90.3%,电流密度为20 mA/cm^(2),测试10 h保持稳定.展开更多
基金the support received from the National Natural Science Foundation of China(Grant No.22372012,22261160640,and 22002009)the Natural Science Foundation of Hunan Province(Grant No.2023JJ20037 and 2021JJ40565)the Scientific Research Project of Hunan Provincial Department of Education(Grant No.22B0293)
文摘The electrochemical coupling of biomass oxidation and nitrogen conversion presents a potential strategy for high value-added chemicals and nitrogen cycling.Herein,in this work,CuO/Co_(3)O_(4)with heterogeneous interface is successfully constructed as a bifunctional catalyst for the electrooxidation of 5-hydroxymethylfurfural to 2,5-furandicarboxylic acid and the electroreduction of nitrate to ammonia(NH_(3)).The open-circuit potential spontaneous experiment shows that more 5-hydroxymethylfurfural molecules are adsorbed in the Helmholtz layer of the CuO/Co_(3)O_(4)composite,which certifies that the CuO/Co_(3)O_(4)heterostructure is conducive to the kinetic adsorption of 5-hydroxymethylfurfural.In situ electrochemical impedance spectroscopy further shows that CuO/Co_(3)O_(4)has faster reaction kinetics and lower reaction potential in oxygen evolution reaction and 5-hydroxymethylfurfural electrocatalytic oxidation.Moreover,CuO/Co_(3)O_(4)also has a good reduction effect on NO_(3)^(-).The ex-situ Raman spectroscopy shows that under the reduction potential,the metal oxide is reduced,and the generated Cu_(2)O can be used as a new active site for the reaction to promote the electrocatalytic conversion of NO_(3)^(-)to NH_(3) synthesis.This work provides valuable guidance for the synthesis of value-added chemicals by 5-hydroxymethylfurfural electrocatalytic oxidation coupled with NO_(3)^(-)while efficiently producing NH_(3).
文摘采用沉淀法-水热法合成了电催化Bi_(2)O_(3)-CuO复合材料.利用X-射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线光电子能谱(XPS)等方法对样品的结构和形貌进行了研究.用电化学测试方法对材料电催化性能进行研究,用气相色谱和核磁共振氢谱对产物进行分析.电催化实验结果表明,Bi_(2)O_(3)-CuO复合材料的电催化性能及对甲酸盐的选择性远高于Bi_(2)O_(3)和CuO.其中比例为1∶1的Bi_(2)O_(3)-CuO复合材料性能最好,在-1.2 V vs.RHE的电位下,甲酸盐的法拉第效率为90.3%,电流密度为20 mA/cm^(2),测试10 h保持稳定.
