Based on the damage analysis of elliptical aperture,the mechanism of coal damagein the developing process of coal and gas outburst was researched.The results show thatthe damage to coal by gas is mainly caused by the ...Based on the damage analysis of elliptical aperture,the mechanism of coal damagein the developing process of coal and gas outburst was researched.The results show thatthe damage to coal by gas is mainly caused by the concentrated tensile stress appearing nearthe endpoint of the pores.Fractures in coal,gas pressure,ground stress and the tensilestrength of the coal matrix are the major controlling factors of this kind of damage.When theground stress releases abruptly and the gas pressure is high,tensile failure will occur aroundthe endpoint of the small pores due to gas pressure,and the coal may be broken up like powder;this is called pulverization.Otherwise,when the gas pressure is low,the tensile stress canonly occur around the endpoint of the large pores and fractures due to gas pressure,the fracturesin coal extend and link together,the fracture extension direction is statistically perpendicularto the direction of the minor principal stress.This kind of damage is shown as the stratifiedspall around the outburst hole.展开更多
In order to study the hypotonic and rheological particularity of “three soft” coal seam in west Henan, China, this paper explored the stress and damage characteristics of crack in coal under condition of water injec...In order to study the hypotonic and rheological particularity of “three soft” coal seam in west Henan, China, this paper explored the stress and damage characteristics of crack in coal under condition of water injection fracturing based on ABAQUS platform;The cohesive element in T-P damage evolution criterion was used to describe the approximately linear relationship between crack width and extending distance in soft coal. The simulation results show that stress evolution and crack damage in soft coal is a gradually developing process under condition of water injection fracturing. When the static pressure is 4 - 10 MPa, and the injection time is about 1 - 2 hours, the damage range of crack in soft coal can basically reach an ideal data of 80 - 100 m, and then greatly improve the hypotonic performance of “three soft” coal seam.展开更多
In this paper, simulated experiment device of coal and gas outburst was employed to perform the experiment on gas-containing coal extrusion. In the experiment, coal surface cracks were observed with a high-speed camer...In this paper, simulated experiment device of coal and gas outburst was employed to perform the experiment on gas-containing coal extrusion. In the experiment, coal surface cracks were observed with a high-speed camera and then the images were processed by sketch. Based on the above description, the paper studied the fractal dimension values from different positions of coal surface as well as their changing laws with time. The results show that there is a growing parabola trend of crack dimension value in the process of coal extrusion. Accordingly, we drew the conclusion that extruded coal crack evolution is a process of fractal dimension value increase. On the basis of fractal dimension values taken from different parts of coal masses, a fractal dimension of the contour map was drawn. Thus, it is clear that the contour map involves different crack fractal dimension values from different positions. To be specific, where there are complicated force and violent movement in coal mass, there are higher fractal dimension values, i.e., the further the middle of observation surface is from the exit of coal mass, and the lower the fractal dimension value is. In line with fractal geometry and energy theory of coal and gas outburst, this study presents the relation between fractal dimension and energy in the process of extruding. In conclusion, the evolution of crack fractal dimension value can signify that of energy, which has laid a solid foundation for the quantification research on the mechanism of gas-containing coal extrusion.展开更多
基金Supported by the National Basic Research Program(973)of China(2005CB221503)the Key Project of Natural Science Foundation of China(50534080)
文摘Based on the damage analysis of elliptical aperture,the mechanism of coal damagein the developing process of coal and gas outburst was researched.The results show thatthe damage to coal by gas is mainly caused by the concentrated tensile stress appearing nearthe endpoint of the pores.Fractures in coal,gas pressure,ground stress and the tensilestrength of the coal matrix are the major controlling factors of this kind of damage.When theground stress releases abruptly and the gas pressure is high,tensile failure will occur aroundthe endpoint of the small pores due to gas pressure,and the coal may be broken up like powder;this is called pulverization.Otherwise,when the gas pressure is low,the tensile stress canonly occur around the endpoint of the large pores and fractures due to gas pressure,the fracturesin coal extend and link together,the fracture extension direction is statistically perpendicularto the direction of the minor principal stress.This kind of damage is shown as the stratifiedspall around the outburst hole.
文摘In order to study the hypotonic and rheological particularity of “three soft” coal seam in west Henan, China, this paper explored the stress and damage characteristics of crack in coal under condition of water injection fracturing based on ABAQUS platform;The cohesive element in T-P damage evolution criterion was used to describe the approximately linear relationship between crack width and extending distance in soft coal. The simulation results show that stress evolution and crack damage in soft coal is a gradually developing process under condition of water injection fracturing. When the static pressure is 4 - 10 MPa, and the injection time is about 1 - 2 hours, the damage range of crack in soft coal can basically reach an ideal data of 80 - 100 m, and then greatly improve the hypotonic performance of “three soft” coal seam.
基金the National Natural Science Foundation of China (Nos. 50904067 and 51104156)the New Century Excellent Talents in University (No. NCET-10-0768) for their support of this project
文摘In this paper, simulated experiment device of coal and gas outburst was employed to perform the experiment on gas-containing coal extrusion. In the experiment, coal surface cracks were observed with a high-speed camera and then the images were processed by sketch. Based on the above description, the paper studied the fractal dimension values from different positions of coal surface as well as their changing laws with time. The results show that there is a growing parabola trend of crack dimension value in the process of coal extrusion. Accordingly, we drew the conclusion that extruded coal crack evolution is a process of fractal dimension value increase. On the basis of fractal dimension values taken from different parts of coal masses, a fractal dimension of the contour map was drawn. Thus, it is clear that the contour map involves different crack fractal dimension values from different positions. To be specific, where there are complicated force and violent movement in coal mass, there are higher fractal dimension values, i.e., the further the middle of observation surface is from the exit of coal mass, and the lower the fractal dimension value is. In line with fractal geometry and energy theory of coal and gas outburst, this study presents the relation between fractal dimension and energy in the process of extruding. In conclusion, the evolution of crack fractal dimension value can signify that of energy, which has laid a solid foundation for the quantification research on the mechanism of gas-containing coal extrusion.