Stabilized cobalt-free lithium-rich cathode materials with an artificial lithium fluoride coating

Iron-substituted cobalt-free lithium-rich manganese-based materials,with advantages of high specific capacity,high safety,and low cost,have been considered as the potential cathodes for lithium ion batteries.However,challenges,such as poor cycle stability and fast voltage fade during cycling under high potential,hinder these materials from commercialization.Here,we developed a method to directly coat LiF on the particle surface of Li_(1.2)Ni_(0.15)Fe_(0.1)Mn_(0.55O2).A uniform and flat film was successfully formed with a thickness about 3 nm,which can effect-ively protect the cathode material from irreversible phase transition during the deintercalation of Li^(+).After surface coating with 0.5wt%LiF,the cycling stability of Li_(1.2)Ni_(0.15)Fe_(0.1)Mn_(0.55O2) cycled at high potential was significantly improved and the voltage fade was largely suppressed.

Dual modification of LiNi_(0.83)Co_(0.11)Mn_(0.06)O_(2) cathode materials by K^(+) doping and Li_(3)PO_(4) coating for lithium ions batteries

Li_(3)PO_(4)@Li_(0.99)K_(0.01)Ni_(0.83)Co_(0.11)Mn_(O.06)O_(2)(NCM-KP) cathode powders are synthesized via K^(+)doping in calcination processes and H_3PO_4 coating in sol-gel processes.K^(+) precisely enters into the lattice to widen the(003) plane to 0.4746 nm with a lower cationic disordered degree of 1.87%.Moreover,the surface residual lithium salts are treated by H_3PO_4 to generate a uniform Li_(3)PO_(4) coating layer of approximately 11.41 nm,which completely covers on the surface of secondary spherical particles to improve the interfacial stability.At 25℃,the NCM-KP electrode delivers a discharge specific capacity of 148.9 mAh·g^(-1) with a remarkable capacity retention ratio of 84.1% after 200 cycles at 1.0C and retains a high reversible specific capacity of 154.4 mAh·g^(-1) at 5.0C.Even at 1.0C and 60℃,it can maintain a reversible discharge specific capacity of 114.6 mAh·g^(-1) with 0.21% of capacity decay per cycle after 200 cycles,which is significantly lower than 0.40% for the pristine NCM powders.Importantly,the charge transfer resistance of 238.89 Ω for the NCM-KP electrode is significantly lower than 947.41 Ω for the pristine NCM one by restricting the interfacial side reactions.Therefore,combining K+doping and Li_(3)PO_(4) coating is an effective strategy to enable the significant improvement of the electrochemical property of high-nickel cathode materials,which may be mainly attributed to the widened diffusion pathway and the formed Li_(3)PO_(4) protective layer,thus promoting Li~+diffusion rate and preventing the erosion of HF.