To explore the iron coke application in hydrogen-rich blast furnace,which is an effective method to achieve the purpose of low carbon emissions,the initial gasification temperature of iron coke in CO_(2) and H_(2)O at...To explore the iron coke application in hydrogen-rich blast furnace,which is an effective method to achieve the purpose of low carbon emissions,the initial gasification temperature of iron coke in CO_(2) and H_(2)O atmosphere and its cogasification reaction mechanism with coke were systematically studied.Iron coke was prepared under laboratory conditions,with a 0-7wt%iron ore powder addition.The properties of iron cokes were tested by coke reactivity index(CRI)and coke strength after reaction(CSR),and their phases and morphology were evolution discussed by scanning electron microscopy and X-ray diffraction analysis.The results indicated that the initial gasification temperature of iron coke decreased with the increase in the iron ore powder content under the CO_(2) and H_(2)O_((g))atmosphere.In the 40vol%H_(2)O+60vol%CO_(2) atmosphere,CRI of iron coke with the addition of 3wt%iron ore powder reached 58.7%,and its CSR reached 56.5%.Because of the catalytic action of iron,the reaction capacity of iron coke was greater than that of coke.As iron coke was preferentially gasified,the CRI and CSR of coke were reduced and increased,respectively,when iron coke and coke were cogasified.The results showed that the skeleton function of the coke can be protected by iron coke.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51576164)the Joint Research Fund of China Bao-Wu Iron and Steel Group Company Limited(Nos.U1860108 and U1860203)Science and Technology Commission of Shanghai Municipality,China(Nos.21DZ1208900 and 19DZ2270200)。
文摘To explore the iron coke application in hydrogen-rich blast furnace,which is an effective method to achieve the purpose of low carbon emissions,the initial gasification temperature of iron coke in CO_(2) and H_(2)O atmosphere and its cogasification reaction mechanism with coke were systematically studied.Iron coke was prepared under laboratory conditions,with a 0-7wt%iron ore powder addition.The properties of iron cokes were tested by coke reactivity index(CRI)and coke strength after reaction(CSR),and their phases and morphology were evolution discussed by scanning electron microscopy and X-ray diffraction analysis.The results indicated that the initial gasification temperature of iron coke decreased with the increase in the iron ore powder content under the CO_(2) and H_(2)O_((g))atmosphere.In the 40vol%H_(2)O+60vol%CO_(2) atmosphere,CRI of iron coke with the addition of 3wt%iron ore powder reached 58.7%,and its CSR reached 56.5%.Because of the catalytic action of iron,the reaction capacity of iron coke was greater than that of coke.As iron coke was preferentially gasified,the CRI and CSR of coke were reduced and increased,respectively,when iron coke and coke were cogasified.The results showed that the skeleton function of the coke can be protected by iron coke.