The magnetic and electrical transport properties of the colossal magnetoresistance material La_(2/3)Ca_(1/3)MnO_3 were studied. It is found that the insulator-metal transition is well consistent with the paramagnetic-...The magnetic and electrical transport properties of the colossal magnetoresistance material La_(2/3)Ca_(1/3)MnO_3 were studied. It is found that the insulator-metal transition is well consistent with the paramagnetic-ferromagnetic transition,and shifts to higher temperature with increasing applied magnetic field. These results suggest that the transport properties are triggered by the magnetic structure transition and consequently result in a CMR near T _C.展开更多
The infrared spectra of La_(0.65)Ba_xMnO_(3-|?￡(c) (x = 0.35, 0.33 and 0.30) were investigated experimentally. The result shows that the sample La_(0.65)Ba_xMnO_(3-|?￡(c) has the largest Curie temperature and the sm...The infrared spectra of La_(0.65)Ba_xMnO_(3-|?￡(c) (x = 0.35, 0.33 and 0.30) were investigated experimentally. The result shows that the sample La_(0.65)Ba_xMnO_(3-|?￡(c) has the largest Curie temperature and the smallest resistivity and wave number of the stretching vibration mode of MnO_6 octaheUron at 300 K among the investigated samples. However, the absorption strength for the stretching vibration mode of Mn0_6 octahedron in La_(0.65)Ba_xMnO_(3-|?￡(c) is stronger for parainagnetic phase than that for ferromagnelic phase, which may be connected with the reducing of the dynamic in- coherent Jahn-Teller distortion below Curie temperature. In addition, the large shift of wave number for the stretching mode at the temperatures from 293 to 423 K has been observed in La_(0.65)Ba_xMnO_(3-|?￡(c), which may be due to the in- crease of the Mn-O bond length with temperature increasing.展开更多
The magnetic behavior and the transport behavior of La0.67-x Smx Sr0.33 MnO3 （x = 0. 00, 0. 10, 0. 20, 0. 30, 0. 40, 0. 50 and 0. 60 ） systems were studied through measuring the M-T curves, electron spin resonance ...The magnetic behavior and the transport behavior of La0.67-x Smx Sr0.33 MnO3 （x = 0. 00, 0. 10, 0. 20, 0. 30, 0. 40, 0. 50 and 0. 60 ） systems were studied through measuring the M-T curves, electron spin resonance （ ESR ） curves and ρ-T curves. The samples exhibit a long-range ferromagnetic order when x = 0. 00, 0. 10, a cluster-spin glass state when x = 0. 20 and 0. 30, and an anti-ferromagnetic state at low temperatures when x = 0. 40, 0. 50 and 0. 60. The samples of x = 0. 30 and 0.40 show phase separation at temperatures above Te. The transport behavior of the sample of x = 0. 60 becomes abnormal when the doping is high, and an insulator-metal transition occurs near To and then a metal-insulator transition occurs, which rarely appears in an ABO3 structure. It is concluded that the magnetic and electric behavior changes of the systems depend on the extra magnetism and lattice distortion effect induced by Sm doping.展开更多
Epitaxial La2/3Ca1/3 MnO3 thin films were prepared on NdGaO3(110) substrates by d. c. magnetron sputtering method. The measurements of magnetoresistance ρ(H) upon magnetic field at different temperatures were carried...Epitaxial La2/3Ca1/3 MnO3 thin films were prepared on NdGaO3(110) substrates by d. c. magnetron sputtering method. The measurements of magnetoresistance ρ(H) upon magnetic field at different temperatures were carried out in the field range of 0 - 8 T. It is found that p(H) obeys the following relations: when the temperature(T) is higher than the Curie temperature Tc, ρ ( H ) =1/α(T)+β(T)H2; below Tc, ρ ( H ) = ρ0 ( T ) 1/A(T)+B(T)exp(H/C(Y)),and ρ(H) =1/κa(T)+γ(T)H when T is far below TC. It is Suggested that the negative magnetoresistive effect is mainly due to enhancement of the magnetoconductance.展开更多
The influence of Gd doping at La-site on the electrical transport properties and the colossal magnetoresistance of La0.7-xGdxSr0.3MnO3 (x = 0.00, 0.10, 0.15, 0.20, 0.30, 0.40, 0.50, 0.60, and 0.70) is studied. The exp...The influence of Gd doping at La-site on the electrical transport properties and the colossal magnetoresistance of La0.7-xGdxSr0.3MnO3 (x = 0.00, 0.10, 0.15, 0.20, 0.30, 0.40, 0.50, 0.60, and 0.70) is studied. The experimental results indicate that the transport properties exhibit abnormal behavior under high doping condition. For x = 0.50, we find that a transition from metal to insulator occurs after the occurrence of insulator-metal transition near Tc, which seldom occurs in ABO3 structure. For samples x = 0.60 and 0.70, it exhibits insulator behavior far above Tc. These abnormal behaviors are attributed to different magnetic background, i.e. the system undergoes a transition from long range ferromagnetic order to the cluster-spin glass state and further to antiferromagnetic order.展开更多
文摘The magnetic and electrical transport properties of the colossal magnetoresistance material La_(2/3)Ca_(1/3)MnO_3 were studied. It is found that the insulator-metal transition is well consistent with the paramagnetic-ferromagnetic transition,and shifts to higher temperature with increasing applied magnetic field. These results suggest that the transport properties are triggered by the magnetic structure transition and consequently result in a CMR near T _C.
基金This work was financially supported by the Trans-Century Foundation of the Educational Ministry of China and by the National Nat
文摘The infrared spectra of La_(0.65)Ba_xMnO_(3-|?￡(c) (x = 0.35, 0.33 and 0.30) were investigated experimentally. The result shows that the sample La_(0.65)Ba_xMnO_(3-|?￡(c) has the largest Curie temperature and the smallest resistivity and wave number of the stretching vibration mode of MnO_6 octaheUron at 300 K among the investigated samples. However, the absorption strength for the stretching vibration mode of Mn0_6 octahedron in La_(0.65)Ba_xMnO_(3-|?￡(c) is stronger for parainagnetic phase than that for ferromagnelic phase, which may be connected with the reducing of the dynamic in- coherent Jahn-Teller distortion below Curie temperature. In addition, the large shift of wave number for the stretching mode at the temperatures from 293 to 423 K has been observed in La_(0.65)Ba_xMnO_(3-|?￡(c), which may be due to the in- crease of the Mn-O bond length with temperature increasing.
文摘The magnetic behavior and the transport behavior of La0.67-x Smx Sr0.33 MnO3 （x = 0. 00, 0. 10, 0. 20, 0. 30, 0. 40, 0. 50 and 0. 60 ） systems were studied through measuring the M-T curves, electron spin resonance （ ESR ） curves and ρ-T curves. The samples exhibit a long-range ferromagnetic order when x = 0. 00, 0. 10, a cluster-spin glass state when x = 0. 20 and 0. 30, and an anti-ferromagnetic state at low temperatures when x = 0. 40, 0. 50 and 0. 60. The samples of x = 0. 30 and 0.40 show phase separation at temperatures above Te. The transport behavior of the sample of x = 0. 60 becomes abnormal when the doping is high, and an insulator-metal transition occurs near To and then a metal-insulator transition occurs, which rarely appears in an ABO3 structure. It is concluded that the magnetic and electric behavior changes of the systems depend on the extra magnetism and lattice distortion effect induced by Sm doping.
基金Project supported by the National Natural Science Foundation of China (Grant No. 19504012) the Chinese Academy of Sciences
文摘Epitaxial La2/3Ca1/3 MnO3 thin films were prepared on NdGaO3(110) substrates by d. c. magnetron sputtering method. The measurements of magnetoresistance ρ(H) upon magnetic field at different temperatures were carried out in the field range of 0 - 8 T. It is found that p(H) obeys the following relations: when the temperature(T) is higher than the Curie temperature Tc, ρ ( H ) =1/α(T)+β(T)H2; below Tc, ρ ( H ) = ρ0 ( T ) 1/A(T)+B(T)exp(H/C(Y)),and ρ(H) =1/κa(T)+γ(T)H when T is far below TC. It is Suggested that the negative magnetoresistive effect is mainly due to enhancement of the magnetoconductance.
基金the National Natural Science Foundation of China(Grant No.19934003)the Research Fund for the Doctoral Program of Higher Education
文摘The influence of Gd doping at La-site on the electrical transport properties and the colossal magnetoresistance of La0.7-xGdxSr0.3MnO3 (x = 0.00, 0.10, 0.15, 0.20, 0.30, 0.40, 0.50, 0.60, and 0.70) is studied. The experimental results indicate that the transport properties exhibit abnormal behavior under high doping condition. For x = 0.50, we find that a transition from metal to insulator occurs after the occurrence of insulator-metal transition near Tc, which seldom occurs in ABO3 structure. For samples x = 0.60 and 0.70, it exhibits insulator behavior far above Tc. These abnormal behaviors are attributed to different magnetic background, i.e. the system undergoes a transition from long range ferromagnetic order to the cluster-spin glass state and further to antiferromagnetic order.