Phase analysis of Al metal in complex deoxidizer

Complex deoxidizer is an important supplementary material for steelmaking,which can not only absorb liquid steel inclusions and improve the quality of molten steel,but also enhance deoxidation,desulfurization, dephosphorization,to prevent the molten steel suction and reduce the molten steel temperature loss.Currently,the complex deoxidizer all contain a certain amount of metal aluminium.The metal aluminium can not be determined for the steel.The entire aluminium contents were regarded as the content of approximate metal aluminium,that often bring great economic losses.Because A1,0,price is cheaper than metal aluminite powder,suppliers added a certain amount of Al_2O_3 in complex deoxidizer,pretend to be the metal aluminium to reap huge profits.This paper put forward a kind of method for determining aluminum,which would reduce loss of the enterprise.Research and put forward an iron triehloride,which extracted from Al metal from complex deoxidizer.Meantime,using orthogonal design of the experiment has been optimized for working conditions.The RSD of the samples are I. 07%-1.94%,the recoveries of the experiment results are 97.0%-110.0%,which expressed the precision and accuracy of the experiment are good.The establishment of the iron triehloride as a extractor,which is rapid and accurate for determination of Al metal in complex deoxidizer.

Mathematical Simulation of Flow Phenomena in CAS-OB Refining Ladle

The deoxidation behaviors of alloys bearing barium in pipe steel were researched with MgO crucible under argon atmosphere in MoSi 2 furnace at 1 873 K. The total oxygen contents of molten steel, the distribution, size and morphology of deoxidation products in the steel were surveyed. The metamorphic mechanism for deoxidation products of alloy bearing barium was also discussed. The results show that applying alloy bearing barium to the pipe steel, very low total oxygen contents can be obtained, and deoxidation products, which easily float up from molten steel, can be changed into globular shape and uniformly distributed in steel. The equilibrium time of total oxygen is about 25 min, and the terminal total oxygen contents range from 0 002 0 % to 0 002 2 % after treating with SiCa wire. The best deoxidizers are SiAlBaCa and SiAlBaCaSr.

Deoxidation Behavior of Alloys Bearing Barium in Molten Steel

The deoxidation behaviors of alloys bearing barium in pipe steel were researched with MgO crucible under argon atmosphere in MoSi2 furnace at 1 873 K.The total oxygen contents of molten steel,the distribution,size and morphology of deoxidation products in the steel were surveyed.The metamorphic mechanism for deoxidation products of alloy bearing barium was also discussed.The results show that applying alloy bearing barium to the pipe steel,very low total oxygen contents can be obtained,and deoxidation products,which easily float up from molten steel,can be changed into globular shape and uniformly distributed in steel.The equilibrium time of total oxygen is about 25 min,and the terminal total oxygen contents range from 0.002 0%to 0.002 2% after treating with SiCa wire.The best deoxidizers are SiAlBaCa and SiAlBaCaSr.

A deoxidation thermodynamic model for 304 stainless steel considering multiple-components coupled reactions

A thermodynamic model for predicting the equilibrium oxygens of 304 stainless steel was developed based on the theory of slag-steel equilibrium,the law of mass conservation,and the ion and molecule coexistence theory.In the developed model,the Fe-Cr-Mn-Si-Al-S-O-melts reaction system and CaO-MgO-CaF_(2)-FeO-MnO-Al_(2)O_(3)-SiO_(2)-Cr2O_(3)slags were considered.The oxygen contents calculated by the model are in good agreement with experimental results and reference data.The equilibrium oxygen contents in 304 stainless steel mainly decrease with increasing binary basicity(w(CaO)/w(SiO_(2)),where w(i)is the mass percentage of component i)and decreasing temperature.Controlling binary basicity at 2.0 while maintaining temperatures lower than 1823 K will keep the oxygen contents in the 304 stainless steel lower than 15×10^(-6).The equilibrium oxygen contents may also be decreased with increasing content of MgO in slags,which is more significant at lower binary basicity.Besides,a small amount of FeO,MnO,and Al_(2)O_(3)(about 0-2.5 wt.%)in slags has little effect on equilibrium oxygen contents.Furthermore,it is found that the[C]-[O]reaction may occur during refining process but will not significantly affect the equilibrium oxygen contents.