Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxida...Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.展开更多
The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel...The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel 45 was used as a reference material. Experimentalresults showed that the abrasive wear resistance of Al_2O_3/PA1010 composite coatings has a goodlinear relationship with the volume fraction of Al_2O_3 particles in Al_2O_3/PA1010 compositecoatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, thesize of Al_2O_3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance ofAl_2O_3/PA1010 composite coatings. By treating the surface of Al_2O_3 particles with a suitablebonding agent, the distribution of Al_2O_3 particles in matrix PA1010 is more homogeneous and thebonding state between Al_2O_3 particles and matrix PA1010 is better. Therefore, the Al_2O_3particles in Al_2O_3/PA1010 composite coatings make the Al_2O_3/PA1010 composite coatings havebetter abrasive wear resistance than PA1010 coatings. The wear resistance of Al_2O_3/PA1010composite coatings is about 45% compared with that of steel 45.展开更多
文摘Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.
基金the financial support from the National Natural Science Foundation of China(Nos.52172067,92160202)Natural Science Foundation of Guangdong Province,China(Nos.2021B1515020038,2020B1515020036)+1 种基金Guangdong Special Support Program,China(No.2019BT02C629)Guangdong Academy of Sciences Program,China(No.2020GDASYL20200104030)。
文摘The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel 45 was used as a reference material. Experimentalresults showed that the abrasive wear resistance of Al_2O_3/PA1010 composite coatings has a goodlinear relationship with the volume fraction of Al_2O_3 particles in Al_2O_3/PA1010 compositecoatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, thesize of Al_2O_3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance ofAl_2O_3/PA1010 composite coatings. By treating the surface of Al_2O_3 particles with a suitablebonding agent, the distribution of Al_2O_3 particles in matrix PA1010 is more homogeneous and thebonding state between Al_2O_3 particles and matrix PA1010 is better. Therefore, the Al_2O_3particles in Al_2O_3/PA1010 composite coatings make the Al_2O_3/PA1010 composite coatings havebetter abrasive wear resistance than PA1010 coatings. The wear resistance of Al_2O_3/PA1010composite coatings is about 45% compared with that of steel 45.