In the ironmaking process,the addition of an organic binder to replace a portion of bentonite has the potential to improve the per-formance of pellets.The interaction between original bentonite(OB)and organic binder w...In the ironmaking process,the addition of an organic binder to replace a portion of bentonite has the potential to improve the per-formance of pellets.The interaction between original bentonite(OB)and organic binder was investigated.Results indicated that the micromor-phology of organic composite bentonite(OCB)became porous and the infrared difference spectrum exhibited a curved shape.In addition,the residual burning rates of OB and organic binder were determined to be 82.72%and 2.30%,respectively.Finally,the influence of OCB on the properties of pellets was investigated.The compressive strength of OCB-added green pellets(14.7 N per pellet)was better than that of OB-ad-ded pellets(10.3 N per pellet).Moreover,the range of melting temperature of OCB-added green pellets(173℃)was narrower than that of OB-added pellets(198℃).The compressive strength of OCB-added green pellets increased from 2156 to 3156 N per pellet with the increase in roasting temperature from 1200 to 1250℃.展开更多
基金This work was financially supported by the National Nat-ural Science Foundation of China(No.51874025)the Na-tional Key R&D Program of China(No.2017YFB0304302-01)the Fundamental Research Funds for the Central Universities,China(No.FRF-NP-19-004).
文摘In the ironmaking process,the addition of an organic binder to replace a portion of bentonite has the potential to improve the per-formance of pellets.The interaction between original bentonite(OB)and organic binder was investigated.Results indicated that the micromor-phology of organic composite bentonite(OCB)became porous and the infrared difference spectrum exhibited a curved shape.In addition,the residual burning rates of OB and organic binder were determined to be 82.72%and 2.30%,respectively.Finally,the influence of OCB on the properties of pellets was investigated.The compressive strength of OCB-added green pellets(14.7 N per pellet)was better than that of OB-ad-ded pellets(10.3 N per pellet).Moreover,the range of melting temperature of OCB-added green pellets(173℃)was narrower than that of OB-added pellets(198℃).The compressive strength of OCB-added green pellets increased from 2156 to 3156 N per pellet with the increase in roasting temperature from 1200 to 1250℃.