In order to study themechanical properties of Z-pins reinforced laminated composite single-lap adhesively bonded joint under un-directional static tensile load,damage failure analysis of the joint was carried out byme...In order to study themechanical properties of Z-pins reinforced laminated composite single-lap adhesively bonded joint under un-directional static tensile load,damage failure analysis of the joint was carried out bymeans of test and numerical simulation.The failure mode and mechanism of the joint were analyzed by tensile failure experiments.According to the experimental results,the joint exhibits mixed failure,and the ultimate failure is Z-pins pulling out of the adherend.In order to study the failure mechanism of the joint,the finite element method is used to predict the failure strength.The numerical results are in good agreement with the experimental results,and the error is 6.0%,which proves the validity of the numerical model.Through progressive damage failure analysis,it is found that matrix tensile failure of laminate at the edge of Z-pins occurs first,then adhesive layer failure-proceeds at the edge of Z-pins,and finally matrix-fiber shear failure of the laminate takes place.With the increase of load,the matrix-fiber shear failure expands gradually in the X direction,and at the same time,the matrix tensile failure at the hole edge gradually extends in different directions,which is consistent with the experimental results.展开更多
With the use of Ti/Ni/Cu/Ni multiple foils as interlayer,carbon/carbon（C/C） composite was bonded to Nibased superalloy GH3044 by partial transient liquid-phase bonding technique.The effect of bonding temperature on ...With the use of Ti/Ni/Cu/Ni multiple foils as interlayer,carbon/carbon（C/C） composite was bonded to Nibased superalloy GH3044 by partial transient liquid-phase bonding technique.The effect of bonding temperature on the microstructures and strengths of the joints was investigated.The results showed that gradient structural multiple interlayers composed of ‘‘C–Ti reaction layer/Ti–Ni intermetallic compound layer/Ni–Cu sosoloid/residual Cu layer/Ni-GH3044 diffusion layer＇＇ were formed between C/C composite and GH3044.The shear strength of the C/C composite/GH3044 joint reached the highest value of 26.1 MPa when the bonding temperature was 1,030 °C.In addition,the fracture morphology showed that the fracture mode changed with the increase of bonding temperature.展开更多
基金supported by Natural Science Talents Program of Lingnan Normal University(No.ZL2021011).
文摘In order to study themechanical properties of Z-pins reinforced laminated composite single-lap adhesively bonded joint under un-directional static tensile load,damage failure analysis of the joint was carried out bymeans of test and numerical simulation.The failure mode and mechanism of the joint were analyzed by tensile failure experiments.According to the experimental results,the joint exhibits mixed failure,and the ultimate failure is Z-pins pulling out of the adherend.In order to study the failure mechanism of the joint,the finite element method is used to predict the failure strength.The numerical results are in good agreement with the experimental results,and the error is 6.0%,which proves the validity of the numerical model.Through progressive damage failure analysis,it is found that matrix tensile failure of laminate at the edge of Z-pins occurs first,then adhesive layer failure-proceeds at the edge of Z-pins,and finally matrix-fiber shear failure of the laminate takes place.With the increase of load,the matrix-fiber shear failure expands gradually in the X direction,and at the same time,the matrix tensile failure at the hole edge gradually extends in different directions,which is consistent with the experimental results.
基金financially supported by the National Natural Science Foundation of China(Nos.51202193 and 51221001)the Fundamental Research Foundation of Northwestern Polytechnical University(No.GBKY1021)the‘‘111’’Project(No.08040)
文摘With the use of Ti/Ni/Cu/Ni multiple foils as interlayer,carbon/carbon（C/C） composite was bonded to Nibased superalloy GH3044 by partial transient liquid-phase bonding technique.The effect of bonding temperature on the microstructures and strengths of the joints was investigated.The results showed that gradient structural multiple interlayers composed of ‘‘C–Ti reaction layer/Ti–Ni intermetallic compound layer/Ni–Cu sosoloid/residual Cu layer/Ni-GH3044 diffusion layer＇＇ were formed between C/C composite and GH3044.The shear strength of the C/C composite/GH3044 joint reached the highest value of 26.1 MPa when the bonding temperature was 1,030 °C.In addition,the fracture morphology showed that the fracture mode changed with the increase of bonding temperature.