A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of app...A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of appropriate amounts of Ce into the catalyst was beneficial to the formation of sole tetragonal ZrO2 and effectively prevented from the formation of monoclinic ZrO〉 and restrained the loss of sulfated species. XRD revealed the presence of tetragonal Ce0.16Zr0.84O2phase in the case of S2O8^2-/ZrO2-CeO2 calcined above 500 ℃. Catalytic activities of S2O8^2-/ZrO2-CeO2 for the esterification of lactic acid with n-butanol was studied. The results showed that the optimum conditions were as follows： calcination temperature of the catalyst 600 ℃, n（lactic acid）：n（n-butyl alcohol）=1.0：3.0, w（S2O8^2-/ZrO2- CeO2）=12.0%, reaction temperature 145 ℃, and reaction time 2 h. The esterification efficiency of lactic acid was about 96.6%.展开更多
Diethylaminoethyl aryloxyacetates are prepared efficiently in 75~95% yields bycondensation of the corresponding aryloxyacetic acids with 2-diethylaminoethanol in the presenceof catalytic amount of solid superacid SO4 ...Diethylaminoethyl aryloxyacetates are prepared efficiently in 75~95% yields bycondensation of the corresponding aryloxyacetic acids with 2-diethylaminoethanol in the presenceof catalytic amount of solid superacid SO4 /Fe2O3. 2-展开更多
A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures an...A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures and acidities were determined by XRD and Hammett method, respectively. The activity of the catalyst was studied as function of Al 2O 3 content, calcination temperature and time in the esterification of acetic acid with butanol, and a conversion of 96 5% was obtained. The catalyst gave also higher yields in syntheses of ketals and acetals: cyclohexanone ethylene ketal(86 2%), acetophenone ethylene ketal(78 5%), acetylacetic ester ketal(88 5%), benzaldehyde glycol acetal(76 3%). The chemical structures of the products were confirmed by IR spectra.展开更多
Ethyl lactate was synthesized starting from lactic acid and ethanol over solid superacid SO2-4/ZrO2-La3+ catalyst.The influence factors were investigated.The results showed that the appropriate conditions were as foll...Ethyl lactate was synthesized starting from lactic acid and ethanol over solid superacid SO2-4/ZrO2-La3+ catalyst.The influence factors were investigated.The results showed that the appropriate conditions were as follows:SO2-4/ZrO2-La3+ was made by adding ZrO2 to 1.5 mol.L-1 H2SO4 and 0.1mol.l-1La3+,immersing 24 hours,baking 2 hour at 600℃.The molar ratio of ethanol to lactic acid was 1.5∶1,reaction time was 3 hours,weight of catalyst is 2.0% of lactic acid mass.The yield of ethyl lactate reached up to 51.4%.展开更多
基金supported by the Science and Technique Foundation of Shaaxi Province of China (2008K07-32)the Foundation of Shaanxi Educa- tional Committee of China (08JK228)the Graduate Innovation Fund of Shaanxi University of Science and Technology
文摘A novel solid superacid catalyst S2O8^2-/ZrO2-CeO2 was prepared by a coprecipitation method and characterized by means of XRD FTIR, BET, TEM and DSC/TG analysis methods. The results indicated that incorporation of appropriate amounts of Ce into the catalyst was beneficial to the formation of sole tetragonal ZrO2 and effectively prevented from the formation of monoclinic ZrO〉 and restrained the loss of sulfated species. XRD revealed the presence of tetragonal Ce0.16Zr0.84O2phase in the case of S2O8^2-/ZrO2-CeO2 calcined above 500 ℃. Catalytic activities of S2O8^2-/ZrO2-CeO2 for the esterification of lactic acid with n-butanol was studied. The results showed that the optimum conditions were as follows： calcination temperature of the catalyst 600 ℃, n（lactic acid）：n（n-butyl alcohol）=1.0：3.0, w（S2O8^2-/ZrO2- CeO2）=12.0%, reaction temperature 145 ℃, and reaction time 2 h. The esterification efficiency of lactic acid was about 96.6%.
文摘Diethylaminoethyl aryloxyacetates are prepared efficiently in 75~95% yields bycondensation of the corresponding aryloxyacetic acids with 2-diethylaminoethanol in the presenceof catalytic amount of solid superacid SO4 /Fe2O3. 2-
文摘A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures and acidities were determined by XRD and Hammett method, respectively. The activity of the catalyst was studied as function of Al 2O 3 content, calcination temperature and time in the esterification of acetic acid with butanol, and a conversion of 96 5% was obtained. The catalyst gave also higher yields in syntheses of ketals and acetals: cyclohexanone ethylene ketal(86 2%), acetophenone ethylene ketal(78 5%), acetylacetic ester ketal(88 5%), benzaldehyde glycol acetal(76 3%). The chemical structures of the products were confirmed by IR spectra.
文摘Ethyl lactate was synthesized starting from lactic acid and ethanol over solid superacid SO2-4/ZrO2-La3+ catalyst.The influence factors were investigated.The results showed that the appropriate conditions were as follows:SO2-4/ZrO2-La3+ was made by adding ZrO2 to 1.5 mol.L-1 H2SO4 and 0.1mol.l-1La3+,immersing 24 hours,baking 2 hour at 600℃.The molar ratio of ethanol to lactic acid was 1.5∶1,reaction time was 3 hours,weight of catalyst is 2.0% of lactic acid mass.The yield of ethyl lactate reached up to 51.4%.