The composites were prepared by ball-milling ZrO_2(3%Y_2O_3) and γ-Al_2O_3 nanoparticles, pressing unidirectionally, cold-pressing isostatically and pressurelessly sintering in air. The phases of ZrO_2 in composites ...The composites were prepared by ball-milling ZrO_2(3%Y_2O_3) and γ-Al_2O_3 nanoparticles, pressing unidirectionally, cold-pressing isostatically and pressurelessly sintering in air. The phases of ZrO_2 in composites were examined by X-ray diffraction. The microstructure of Al_2O_3/3Y-TZP composites was observed by scanning electron microscope (SEM) and transmission electron microscopy (TEM) respectively. The X-ray analysis reveals that ZrO_2 of both surface and fracture surface is mainly t-ZrO_2. The SEM image shows that there are some intragranular particles in large granulars. The fracture toughness K_ 1c of Al_2O_3/70%ZrO_2(3%Y_2O_3(mole fraction)) composite tested by single-edge notched bending is 13.5 MPa·m 1/2. Being toughened by the ferroelastic domain switching and the intragranular microstructure explains high toughness of the composite.展开更多
The composition, microstructures and properties of SiC /Al-2O-3/Al-Si composites formed by reactive penetration of the molten aluminum into the preforms of SiO-2 and SiC were investigated. The composition of the compo...The composition, microstructures and properties of SiC /Al-2O-3/Al-Si composites formed by reactive penetration of the molten aluminum into the preforms of SiO-2 and SiC were investigated. The composition of the composites was measured by X-ray diffraction (XRD). The microstructures of the composites were also measured by scanning electron microscopy (SEM) and optical microscopy. In addition, the factors affecting the properties of the composites were discussed.The experiments show that the mechanical properties of the composites depend on their relative densities and the sizes of the fillers“SiC grains".The denser the SiC/Al-2O-3/Al-Si composites,the higher their bending strength.As the filler “SiC grains" become fine,the bending strength of the composites increases.展开更多
The potential difference between positive and negative ions was utilized to improve the homogenized dispersion of nanoscale Al_(2)O_(3) whiskers in Mg matrix composites.The Mg powders were decorated with sodium dodecy...The potential difference between positive and negative ions was utilized to improve the homogenized dispersion of nanoscale Al_(2)O_(3) whiskers in Mg matrix composites.The Mg powders were decorated with sodium dodecylbenzene sulfonate(C_(18)H_(29)NaO_(3)S,SDBS)and were introduced to the cathode group on their surface.The Al_(2)O_(3) whiskers were modified by the cetyl trimethyl ammonium bromide(C_(19)H_(42)BrN,CTAB)and were featured in the anode group.The suitable contents of CTAB and SDBS,the application atmosphere,and the type of solvents were investigated.Dispersion results showed that adding 2wt%SDBS into Mg powders and adding 2wt%CTAB into Al_(2)O_(3) whiskers pro-moted the formation of more uniformly mixed composite powders,compared to those of conventional ball milling via scanning electron micro-scopy(SEM)analysis.Meanwhile,the calculated results derived from first-principle calculations also demonstrated the stronger cohesion between Al_(2)O_(3) whisker reinforcements and Mg matrix than undecorated composite powders.After preparation by powder metallurgy,the mor-phology,grain size,hardness,and standard deviation coefficient of composites were analyzed to evaluate the dispersed efficiency.The results indicated that the modification of homogenized dispersed Al_(2)O_(3) whiskers in composites contributed to the refinement of 26%in grain size and the improvement of 20%in hardness compared with pure Mg,and the reduction of 32.5%in the standard deviation coefficient of hardness compared with the ball-milling sample.展开更多
A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties ...A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties of the composite, and the process flow weresystematically studied. It is confirmed that this new technique simplifies the process and improvesthe properties of the composite. X-ray analysis indicates that the alumina particles formed duringinternal oxidation consist of a large mount of gamma-Al_2O_3 and a certain amount of theta-Al_2O_3and alpha-Al_2O_3. TEM observation shows that the obtained gamma-Al_2O_3 nano-particles areuniformly distributed in the copper grains; their mean size and space between particles are 7 runand 30 nm, respectively. The main properties of the composite with 50 percent cold deformation areas follows: the electric conductivity is 51 MS/m (87 percent IACS), sigma_b = 628 MPa, and thehardness is HRB86. After annealing at 1273 K, all or most of the above properties remain, and themicrostructures are still dependent on elongated fiber-form grains.展开更多
The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel...The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel 45 was used as a reference material. Experimentalresults showed that the abrasive wear resistance of Al_2O_3/PA1010 composite coatings has a goodlinear relationship with the volume fraction of Al_2O_3 particles in Al_2O_3/PA1010 compositecoatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, thesize of Al_2O_3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance ofAl_2O_3/PA1010 composite coatings. By treating the surface of Al_2O_3 particles with a suitablebonding agent, the distribution of Al_2O_3 particles in matrix PA1010 is more homogeneous and thebonding state between Al_2O_3 particles and matrix PA1010 is better. Therefore, the Al_2O_3particles in Al_2O_3/PA1010 composite coatings make the Al_2O_3/PA1010 composite coatings havebetter abrasive wear resistance than PA1010 coatings. The wear resistance of Al_2O_3/PA1010composite coatings is about 45% compared with that of steel 45.展开更多
icrostructure and mechanical properties of Al_4C_3 and Al_2O_3 dispersion strengthened aluminum composite fabricated by mechanical attrition and hotpressing consolidation method were studied. It was shown that fine we...icrostructure and mechanical properties of Al_4C_3 and Al_2O_3 dispersion strengthened aluminum composite fabricated by mechanical attrition and hotpressing consolidation method were studied. It was shown that fine well developed Al_4C_3 stick and equiaxed γAl_2O_3 dispersoids with total content of about 6.6 v% uniformly distributed within the Al grains or along the grain boundaries. The Al/Al_4C_3 and Al/Al_2O_3 interfaces are very clean and well bonded at atomic level, but have no fixed orientation relationships between the dispersoids and the aluminum matrix exists. At ambient and especially elevated temperatures, strength and stiffness of the composite are much higher than that of P/M Al and even better than that of the 15 v% SiCw/Al composite.展开更多
The equilibrium phase and adiabatic temperature for combustion synthesis of Al_2O_3/B_4C employing Al, B_2O_3 and C as starting materials is analyzed by both conventional and CALPHAD method. The adiabatic temperature ...The equilibrium phase and adiabatic temperature for combustion synthesis of Al_2O_3/B_4C employing Al, B_2O_3 and C as starting materials is analyzed by both conventional and CALPHAD method. The adiabatic temperature calculed by CALPHAD method is significantly lower than that obtained by conventional method. The CALPHAD calculation also reveals that the equilibrium phases presented at the adiabatic temperature are different to the desired composites. The adiabatic temperature in this system can be lowered by introducing Al_2O_3 as diluents. The maximum amount of Al_2O_3 that can be added to the system while maintain a self-sustaining combusion mode is 1.3 mol.展开更多
Al_(2)O_(3) particles reinforced hypereutectic Al-Si composites were prepared by in situ Fe_(2)O_(3)/Al reaction system.The thermodynamic analysis and microstructure evolution were investigated by differential scannin...Al_(2)O_(3) particles reinforced hypereutectic Al-Si composites were prepared by in situ Fe_(2)O_(3)/Al reaction system.The thermodynamic analysis and microstructure evolution were investigated by differential scanning calorimetry,optical microscope,scanning electronic microscopy and transmission electron microscope.Results show that the reaction between Fe_(2)O_(3) and Al is spontaneous which can be separated into two steps at different temperatures.The in situ Al_(2)O_(3) particles in nano size distribute on the Al matrix accompanied with long needle-shapedβFe-rich intermetallic phase.With different content of Mn addition,βphase can be modified toα-Al15(Mn,Fe)3Si2 andδ-Al4(Fe,Mn)Si2.Both tensile strength and elongation results at room temperature and 300℃reveal that the optimal Fe-rich intermetallic phase is finer Chinese-script and polyhedralαphase with a Mn/Fe mass ratio 0.5 for the composites.Both in situ Al_(2)O_(3) particles andα-Fe phases contribute to the properties improvement of the composites。展开更多
文摘The composites were prepared by ball-milling ZrO_2(3%Y_2O_3) and γ-Al_2O_3 nanoparticles, pressing unidirectionally, cold-pressing isostatically and pressurelessly sintering in air. The phases of ZrO_2 in composites were examined by X-ray diffraction. The microstructure of Al_2O_3/3Y-TZP composites was observed by scanning electron microscope (SEM) and transmission electron microscopy (TEM) respectively. The X-ray analysis reveals that ZrO_2 of both surface and fracture surface is mainly t-ZrO_2. The SEM image shows that there are some intragranular particles in large granulars. The fracture toughness K_ 1c of Al_2O_3/70%ZrO_2(3%Y_2O_3(mole fraction)) composite tested by single-edge notched bending is 13.5 MPa·m 1/2. Being toughened by the ferroelastic domain switching and the intragranular microstructure explains high toughness of the composite.
文摘The composition, microstructures and properties of SiC /Al-2O-3/Al-Si composites formed by reactive penetration of the molten aluminum into the preforms of SiO-2 and SiC were investigated. The composition of the composites was measured by X-ray diffraction (XRD). The microstructures of the composites were also measured by scanning electron microscopy (SEM) and optical microscopy. In addition, the factors affecting the properties of the composites were discussed.The experiments show that the mechanical properties of the composites depend on their relative densities and the sizes of the fillers“SiC grains".The denser the SiC/Al-2O-3/Al-Si composites,the higher their bending strength.As the filler “SiC grains" become fine,the bending strength of the composites increases.
基金the Fundamental Research Funds for the National Natural Science Foundation of China (Nos. 52101123 and 52004227)the Fundamental Research Funds for the Central Universities-Interdisciplinary Research (No. 2682021ZTPY001)the Dongguan Scitech Commissioner (No. 20211800500102)
文摘The potential difference between positive and negative ions was utilized to improve the homogenized dispersion of nanoscale Al_(2)O_(3) whiskers in Mg matrix composites.The Mg powders were decorated with sodium dodecylbenzene sulfonate(C_(18)H_(29)NaO_(3)S,SDBS)and were introduced to the cathode group on their surface.The Al_(2)O_(3) whiskers were modified by the cetyl trimethyl ammonium bromide(C_(19)H_(42)BrN,CTAB)and were featured in the anode group.The suitable contents of CTAB and SDBS,the application atmosphere,and the type of solvents were investigated.Dispersion results showed that adding 2wt%SDBS into Mg powders and adding 2wt%CTAB into Al_(2)O_(3) whiskers pro-moted the formation of more uniformly mixed composite powders,compared to those of conventional ball milling via scanning electron micro-scopy(SEM)analysis.Meanwhile,the calculated results derived from first-principle calculations also demonstrated the stronger cohesion between Al_(2)O_(3) whisker reinforcements and Mg matrix than undecorated composite powders.After preparation by powder metallurgy,the mor-phology,grain size,hardness,and standard deviation coefficient of composites were analyzed to evaluate the dispersed efficiency.The results indicated that the modification of homogenized dispersed Al_(2)O_(3) whiskers in composites contributed to the refinement of 26%in grain size and the improvement of 20%in hardness compared with pure Mg,and the reduction of 32.5%in the standard deviation coefficient of hardness compared with the ball-milling sample.
文摘A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties of the composite, and the process flow weresystematically studied. It is confirmed that this new technique simplifies the process and improvesthe properties of the composite. X-ray analysis indicates that the alumina particles formed duringinternal oxidation consist of a large mount of gamma-Al_2O_3 and a certain amount of theta-Al_2O_3and alpha-Al_2O_3. TEM observation shows that the obtained gamma-Al_2O_3 nano-particles areuniformly distributed in the copper grains; their mean size and space between particles are 7 runand 30 nm, respectively. The main properties of the composite with 50 percent cold deformation areas follows: the electric conductivity is 51 MS/m (87 percent IACS), sigma_b = 628 MPa, and thehardness is HRB86. After annealing at 1273 K, all or most of the above properties remain, and themicrostructures are still dependent on elongated fiber-form grains.
文摘The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel 45 was used as a reference material. Experimentalresults showed that the abrasive wear resistance of Al_2O_3/PA1010 composite coatings has a goodlinear relationship with the volume fraction of Al_2O_3 particles in Al_2O_3/PA1010 compositecoatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, thesize of Al_2O_3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance ofAl_2O_3/PA1010 composite coatings. By treating the surface of Al_2O_3 particles with a suitablebonding agent, the distribution of Al_2O_3 particles in matrix PA1010 is more homogeneous and thebonding state between Al_2O_3 particles and matrix PA1010 is better. Therefore, the Al_2O_3particles in Al_2O_3/PA1010 composite coatings make the Al_2O_3/PA1010 composite coatings havebetter abrasive wear resistance than PA1010 coatings. The wear resistance of Al_2O_3/PA1010composite coatings is about 45% compared with that of steel 45.
文摘icrostructure and mechanical properties of Al_4C_3 and Al_2O_3 dispersion strengthened aluminum composite fabricated by mechanical attrition and hotpressing consolidation method were studied. It was shown that fine well developed Al_4C_3 stick and equiaxed γAl_2O_3 dispersoids with total content of about 6.6 v% uniformly distributed within the Al grains or along the grain boundaries. The Al/Al_4C_3 and Al/Al_2O_3 interfaces are very clean and well bonded at atomic level, but have no fixed orientation relationships between the dispersoids and the aluminum matrix exists. At ambient and especially elevated temperatures, strength and stiffness of the composite are much higher than that of P/M Al and even better than that of the 15 v% SiCw/Al composite.
文摘The equilibrium phase and adiabatic temperature for combustion synthesis of Al_2O_3/B_4C employing Al, B_2O_3 and C as starting materials is analyzed by both conventional and CALPHAD method. The adiabatic temperature calculed by CALPHAD method is significantly lower than that obtained by conventional method. The CALPHAD calculation also reveals that the equilibrium phases presented at the adiabatic temperature are different to the desired composites. The adiabatic temperature in this system can be lowered by introducing Al_2O_3 as diluents. The maximum amount of Al_2O_3 that can be added to the system while maintain a self-sustaining combusion mode is 1.3 mol.
基金Funded by the National Natural Science Foundation of China(No.51201071)the National Natural Science Foundation of Jiangsu Province(No.BK20161270)Jiangsu Overseas Visiting Scholar Program for University Prominent Young&Middle-aged Teachers and Presidents(2018)。
文摘Al_(2)O_(3) particles reinforced hypereutectic Al-Si composites were prepared by in situ Fe_(2)O_(3)/Al reaction system.The thermodynamic analysis and microstructure evolution were investigated by differential scanning calorimetry,optical microscope,scanning electronic microscopy and transmission electron microscope.Results show that the reaction between Fe_(2)O_(3) and Al is spontaneous which can be separated into two steps at different temperatures.The in situ Al_(2)O_(3) particles in nano size distribute on the Al matrix accompanied with long needle-shapedβFe-rich intermetallic phase.With different content of Mn addition,βphase can be modified toα-Al15(Mn,Fe)3Si2 andδ-Al4(Fe,Mn)Si2.Both tensile strength and elongation results at room temperature and 300℃reveal that the optimal Fe-rich intermetallic phase is finer Chinese-script and polyhedralαphase with a Mn/Fe mass ratio 0.5 for the composites.Both in situ Al_(2)O_(3) particles andα-Fe phases contribute to the properties improvement of the composites。