Thermal fatigue performance of copper/stainless steel explosive welding joint was investigated by using a highly effective thermal fatigue test device. The testing device adopted induction coil to heat and carry out t...Thermal fatigue performance of copper/stainless steel explosive welding joint was investigated by using a highly effective thermal fatigue test device. The testing device adopted induction coil to heat and carry out two groups of thermal fatigue test at the same time. Metallurgical microscope and scanning electron microscope were used to respectively measure the surface crack and cross-section crack propagation morphology of the explosive welding joint specimen that were conducted thermal cycling for different upper limit temperatures and different cycle time.Experimental results indicated that the cyclic thermal stress and oxidation corrosion was the major factors for fatigue damage behavior of explosive welding joints, where the oxidation corrosion of the interface has become more serious with the increasing the upper limit temperature or the number of cycles rising. Thermal fatigue cracks initiation was mainly beginning from the wavy interface between copper and stainless steel, the vortex-like cast microstructure formed by explosive welding can prevent the crack from propagating along the interface edge and change the direction of crack propagation.The initiation and expansionof thermal fatigue cracks were observed in the copper matrix.展开更多
Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimen...Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimental environmental issues.To prevent chromium pollution,the effects of iron oxide on crystallization behavior and spatial distribution of spinel were investigated in this work.The results revealed that FeO was more conducive to the growth of spinels compared with Fe2O3 and Fe3O4.Spinels were found to be mainly distrib-uted at the top and bottom of slag.The amount of spinel phase at the bottom decreased with the increasing FeO content,while that at the top increased.The average particle size of spinel in the slag with 18wt%FeO content was 12.8μm.Meanwhile,no notable structural changes were observed with a further increase in FeO content.In other words,the spatial distribution of spinel changed when the content of iron oxide varied in the range of 8wt%to 18wt%.Finally,less spinel was found at the bottom of slag with a FeO content of 23wt%.展开更多
Stainless steels are used in a wide range of complex environments due to their excellent corrosion resistance.Multiphase stainless steels can offer an excellent combination of strength,toughness and corrosion resistan...Stainless steels are used in a wide range of complex environments due to their excellent corrosion resistance.Multiphase stainless steels can offer an excellent combination of strength,toughness and corrosion resistance due to the coexistence of different microstructures.The microstructure and mechanical properties of a novel cast multiphase stainless steel,composed of martensite,ferrite,and austenite,were investigated following appropriate heat treatment processes:solution treatment at 1,050℃ for 0.5 h followed by water quenching to room temperature,and aging treatment at 500℃ for 4 h followed by water quenching to room temperature.Results show reversed austenite is formed by diffusion of Ni element during aging process,and the enrichment of Ni atoms directly determines the mechanical stability of austenite.The austenite with a lower Ni content undergoes a martensitic transformation during plastic deformation.The tensile strength of the specimen exceeds 1,100 MPa and the elongation exceeds 24%after solid solution,and further increases to 1,247 MPa and 25%after aging treatment.This enhancement is due to the TRIP effect of austenite and the precipitation of the nanoscale G-phase pinning dislocations in ferrite and martensite.展开更多
In the present work,plastic deformation mechanisms were initially tailored by adjusting the deformation temperature in the range of 0 to 200℃ in AISI 304L austenitic stainless steel,aiming to optimize the strength-du...In the present work,plastic deformation mechanisms were initially tailored by adjusting the deformation temperature in the range of 0 to 200℃ in AISI 304L austenitic stainless steel,aiming to optimize the strength-ductility synergy.It was shown that the combined twinning-induced plasticity(TWIP)/transformation-induced plasticity(TRIP)effects and a wider strain range for the TRIP effect up to higher strains by adjusting the deformation temperature are good strategies to improve the strength-ductility synergy of this metastable stainless steel.In this regard,by consideration of the observed temperature-dependency of plastic deformation,the controlled sequence of TWIP and TRIP effects for archiving superior strength-ductility trade-off was intended by the pre-designed temperature jump tensile tests.Accordingly,the optimum tensile toughness of 846 MJ/m^(3) and total elongation to 133% were obtained by this strategy via exploiting the advantages of the TWIP effect at 100℃ and the TRIP effect at 25℃ at the later stages of the straining.Consequently,a deformation-temperature-transformation(DTT)diagram was developed for this metastable alloy.Moreover,based on work-hardening analysis,it was found that the main phenomenon constraining further improvement in the ductility and strengthening was the yielding of the deformation-induced α′-martensite.展开更多
Non-penetration laser welding of lap joints in austenitic stainless steel sheets is commonly preferred in fields where the surface quality is of utmost importance.However,the application of non-penetration welded aust...Non-penetration laser welding of lap joints in austenitic stainless steel sheets is commonly preferred in fields where the surface quality is of utmost importance.However,the application of non-penetration welded austenitic stainless steel parts is limited owing to the micro bulging distortion that occurs on the back surface of the partial penetration side.In this paper,non-penetration lap laser welding experiments,were conducted on galvanized and SUS304 austenitic stainless steel plates using a fiber laser,to investigate the mechanism of bulging distortion.A comparative experiment of DC01 galvanized steel-Q235 carbon steel lap laser welding was carried out,and the deflection and distortion profile of partially penetrated side of the sheets were measured using a noncontact laser interferometer.In addition,the cold-rolled SUS304 was subjected to heat holding at different temperatures and water quenching after bending to characterize its microstructure under tensile and compressive stress.The results show that,during the heating stage of the thermal cycle of laser lap welding,the partial penetration side of the SUS304 steel sheet generates compressive stress,which extrudes the material in the heat-affected zone to the outside of the back of the SUS304 steel sheet,thereby forming a bulge.The findings of these experiments can be of great value for controlling the distortion of the partial penetrated side of austenitic stainless steel sheet during laser non-penetration lap welding.展开更多
Duplex stainless steels(DSSs)show better corrosion resistance with higher strength than traditional austenite stainless steels in many aggressive environments,and can be welded properly with almost every welding proce...Duplex stainless steels(DSSs)show better corrosion resistance with higher strength than traditional austenite stainless steels in many aggressive environments,and can be welded properly with almost every welding processes,if proper heat input is provided.Progresses of research works on weldability of DSSs in recent years are reviewed in this paper.Balance control of ferrite/austenite phases is most important for DSSs welding.The phases balance can be controlled with filler materials,nitrogen addition in shielding gas,heat input,post weld heat treatment,and alternating magnetic field.Too high cooling rate results in not only extra ferrite,but also chromium nitride precipitation.While too low cooling rate or heating repeatedly results in precipitation of secondary austenite and intermetallic compounds.In both situations,mechanical properties and corrosion resistance of the DSS joints deteriorate.Recommended upper and lower limits of heat input and maximum interpass temperature should be observed.展开更多
Excellent weldability substantially contributes to the intrinsic quality of steels,while appropriate chemical composition plays a primary role in the essential weldability of steels.The poor weldability of ferritic st...Excellent weldability substantially contributes to the intrinsic quality of steels,while appropriate chemical composition plays a primary role in the essential weldability of steels.The poor weldability of ferritic stainless steels could be improved through modification with minor alloy elements while minimally increasing the cost.Therefore,studying the effect of minor alloy elements on the weldability of steels is of considerable importance.In this study,several steels of middle-chromium hyperpure ferritic stainless 00Cr21Ti with different Ni content(0.3%,0.5%,0.8%,and 1.0%)were developed,and their weldabilities of butt joint samples welded using the metal inert gas welding process,including the influence of welded joints on the microstructure,tensile performance,corrosion resistance,and fatigue property,were investigated.Results show that the steels with w(Ni)≥0.8%exhibit excellent mechanical properties compared with those with low-Ni content steels,further,their impact toughness at normal atmospheric temperature meets the industrial application standard and the fatigue property is similar to that of 304 austenitic stainless steel.Moreover,results show that the corrosion resistance of all the samples is almost at the same level.The results acquired in this study are supposed to be useful for the optimization of the chemical composition of stainless steels aiming to improve weldability.展开更多
Starting from the corrosion mechanism,this paper analyzes the characteristics of various types of stainless steel and selects the best performance composite plate composite plate stainless steel.Analyze and select the...Starting from the corrosion mechanism,this paper analyzes the characteristics of various types of stainless steel and selects the best performance composite plate composite plate stainless steel.Analyze and select the most suitable corrosion detection method based on specific practical multi working conditions,discuss the interference factors that affect metal corrosion during experimental simulation,and the advantages of newly developed sheet metal.The new development of composite board panels,with the substrate and composite materials applying their respective capabilities for MED,will bring breakthrough progress to the scientific research and engineering applica-tion of composite boards.展开更多
The corrosion behavior of 304L stainless steel(SS)in 3.5wt%NaCl solution after different cavitation erosion(CE)times was mainly evaluated using electrochemical noise and potentiostatic polarization techniques.It was f...The corrosion behavior of 304L stainless steel(SS)in 3.5wt%NaCl solution after different cavitation erosion(CE)times was mainly evaluated using electrochemical noise and potentiostatic polarization techniques.It was found that the antagonism effect resulting in the passivation and depassivation of 304L SS had significant distinctions at different CE periods.The passive behavior was predominant during the incubation period of CE where the metastable pitting initiated at the surface of 304L SS.Over the rising period of CE,the 304L SS experienced a transition from passivation to depassivation,leading to the massive growth of metastable pitting and stable pitting.The depassivation of304L SS was found to be dominant at the stable period of CE where serious localized corrosion occurred.展开更多
The reliable welding of T91 heat-resistant steel to 316L stainless steel is a considerable issue for ensuring the safety in service of ultrasupercritical power generation unit and nuclear fusion reactor,but the high-q...The reliable welding of T91 heat-resistant steel to 316L stainless steel is a considerable issue for ensuring the safety in service of ultrasupercritical power generation unit and nuclear fusion reactor,but the high-quality dissimilar joint of these two steels was difficult to be obtained by traditional fusion welding methods.Here we improved the structure-property synergy in a dissimilar joint of T91 steel to 316L steel via friction stir welding.A defect-free joint with a large bonding interface was produced using a small-sized tool under a relatively high welding speed.The bonding interface was involved in a mixing zone with both mechanical mixing and metallurgical bonding.No obvious material softening was detected in the joint except a negligible hardness decline of only HV~10 in the heat-affected zone of the T91 steel side due to the formation of ferrite phase.The welded joint exhibited an excellent ultimate tensile strength as high as that of the 316L parent metal and a greatly enhanced yield strength on account of the dependable bonding and material renovation in the weld zone.This work recommends a promising technique for producing high-strength weldments of dissimilar nuclear steels.展开更多
A preliminary study was made on the antibacterial mechanism of copper-bearing antibacterial stainless steels against E.coli through experiments of microbiology such as EDTA (ethylenediaminetetraacetic acid) complexi...A preliminary study was made on the antibacterial mechanism of copper-bearing antibacterial stainless steels against E.coli through experiments of microbiology such as EDTA (ethylenediaminetetraacetic acid) complexing, DNA smearing and AFM (atomic force microscope) observation. It was measured that the antibacterial stainless steels showed excellent antibacterial functions with antibacterial rate to E.coli over 99.99%. The antibacterial rate was weak if the bacteria solution was complexed by EDTA, indicating that the copper ions play a dominant role in the antibacterial effect of the antibacterial stainless steels. The electrophoresis experiment did not show the phenomenon of DNA smearing for E.coli after contacting antibacterial stainless steels, which meant that DNA of E.coli was not obviously damaged. It was observed by AFM that the morphology of E.coli changed a lot after contacting antibacterial stainless steels, such as cell walls being seriously changed and lots of contents in the cells being leaked.展开更多
Dissimilar joints comprised of copper–nickel and steel alloys are a challenge for manufacturers in modern industries, as these metals are not thermomechanically or chemically well matched. The present study investiga...Dissimilar joints comprised of copper–nickel and steel alloys are a challenge for manufacturers in modern industries, as these metals are not thermomechanically or chemically well matched. The present study investigated the effects of tool rotational speed and linear speed on the microstructure and mechanical properties of friction stir-welded C71000 copper–nickel and 340 stainless steel alloys using a tungsten carbide tool with a cylindrical pin. The results indicated that a rotational-to-linear speed ratio of 12.5 r/mm did not cause any macro defects, whereas some tunneling defects and longitudinal cracks were found at other ratios that were lower and higher. Furthermore, chromium carbide was formed on the grain boundaries of the 304 stainless steel near the shoulder zone and inside the joint zone, directing carbon and chromium penetration toward the grain boundaries. Tensile strength and elongation percentages were 84% and 65% of the corresponding values in the copper–nickel base metal, respectively.展开更多
Copper ions were implanted into austenitic stainless steel (SS) by metal vapor vacuum arc with a energy of 100 keV and an ions dose range of (0.5-8.0)× 10^17 cm^-2. The Cu-implanted SS was annealed in an Ar a...Copper ions were implanted into austenitic stainless steel (SS) by metal vapor vacuum arc with a energy of 100 keV and an ions dose range of (0.5-8.0)× 10^17 cm^-2. The Cu-implanted SS was annealed in an Ar atmosphere furnace. Glancing X-ray diffraction (GXRD), transmission electron microscopy (TEM) and Auger electron spectroscopy (AES) were used to reveal the phase compositions, microstructures, and concentration profiles of copper ions in the implanted layer. The results show that the antibacterial property of Cu-implanted SS is attributed to Cu9.9Fe0.1, which precipitated as needles. The depth of copper in Cu-implanted SS with annealing treatment is greater than that in Cu-implanted SS without annealing treatment, which improves the antibacterial property against S. aureus. The salt wetting-drying combined cyclic test was used to evaluate the corrosion-resistance of antibacterial SS, and the results reveal that the antibacterial SS has a level of corrosion-resistance equivalent to that of un-implanted SS.展开更多
With CuMn alloy as interlayer, the transient liquid phase (TLP) diffusion bonding of Cu alloys (CuAlBe) to stainless steel (1Cr18Ni9Ti) was studied. The results show that the bonding pressure, time and temperature and...With CuMn alloy as interlayer, the transient liquid phase (TLP) diffusion bonding of Cu alloys (CuAlBe) to stainless steel (1Cr18Ni9Ti) was studied. The results show that the bonding pressure, time and temperature and the content of Mn in CuMn alloy have great effects on the strength of bonding interface; when they are 1 MPa, 40 min, 1 223 K and 30% respectively, the maximum joint strength of 487 MPa is attained. The fracture occurring at the bonding interface is a plastic one and the effect of Mn has been analyzed.展开更多
Austenite antibacterial stainless steels have been found to have wide applications in hospitals and food industries. In recent years epsilon copper precipitation in antibacterial stainless steels has obtained much res...Austenite antibacterial stainless steels have been found to have wide applications in hospitals and food industries. In recent years epsilon copper precipitation in antibacterial stainless steels has obtained much research interest due to its antibacterial action. The objective of this study was to determine the effects of nitrogen concentration on the precipitation of epsilon copper and antibacterial property. Two kinds of austenite antibacterial stainless steels containing copper and different nitrogen concentration (0.02 and 0.08 wt pct, respectively) were prepared and the microstructures were characterized by a combination of electron microscopy and thermodynamic analysis. A mathematical expression was deduced to predict the effect of nitrogen concentration on the activity coefficient of copper, In(fCu/f^0cu)=0.53524+4.11xN-0.48x^2N. Higher nitrogen was found to increase the free energy difference of copper concentration distribution between precipitation phase and austenite matrix, stimulate the aggregation of copper atoms from austenite, increase the precipitation amount and consequently enhance the antibacterial property of steel.展开更多
Silver or copper ions are often chosen as antibacterial agents. But a few reports are concerned with these two antibacterial agents for preparation of antibacterial stainless steel (SS). The antibacterial properties...Silver or copper ions are often chosen as antibacterial agents. But a few reports are concerned with these two antibacterial agents for preparation of antibacterial stainless steel (SS). The antibacterial properties and corrosion resistance of AISI 420 stainless steel implanted by silver and copper ions were investigated. Due to the cooperative antibacterial effect of silver and copper ions, the Ag/Cu implanted SS showed excellent antibacterial activities against both Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus) at a total implantation dose of 2~ 1017 ions/cm2. Electrochemical polarization curves revealed that the corrosion resistance of Ag/Cu implanted SS was slightly enhanced as compared with that of un-implanted SS, The implanted layer was characterized by X-ray photoelec- tron spectroscopy (XPS). Core level XPS spectra indicate that the implanted silver and copper ions exist in metallic state in the implanted layer.展开更多
The precipitation of epsilon copper at 1023 K ageing in ferrite antibacterial stainless steel was investigated by a combination of electron microscopy and micro-Vickers hardness measurement. The results show that epsi...The precipitation of epsilon copper at 1023 K ageing in ferrite antibacterial stainless steel was investigated by a combination of electron microscopy and micro-Vickers hardness measurement. The results show that epsilon copper precipitation occurs within 90 s, Complex multilayer structure confirmed as twins and stacking faults on {111}ε-Cu planes was observed in the precipitates. The precipitates grow by the lengthwise enlargement of a set of parallel layers, having [111]ε-Cu and [112]ε-Cu preferred growth orientations. The volume fraction of precipitates f formed within 120 min can be predicted by a modified Avrami equation (In1/1-f= kt + b). Simultaneously, substituent atom clusters with a size of 5-10 nm was found to occur in the solution and cause matrix strain. The precipitate morphology and distribution on the surface of ferrite antibacterial stainless steel are associated with surface crystallographic orientation of the matrix. The precipitates are predominantly located within the ferrite grains of 〈110〉 orientation. The precipitates located on {111}α-Fe surface planes have sphere or ellipse shape.展开更多
By using auger electron spectroscopy (AES) and diffusion theory to analyze the surface segregation of copper in antibacterial ferritic stainless steel, establishing a diffusion model, and calculating the activation ...By using auger electron spectroscopy (AES) and diffusion theory to analyze the surface segregation of copper in antibacterial ferritic stainless steel, establishing a diffusion model, and calculating the activation energy of diffusion of the copper in ferrite, the affect of surface segregation on the antibacterial capabilities were researched. The results show that the concentration of the copper surface at 973 K and 1 073 K could be expressed asln X^sCu/X^bCu = k0 √Dt/d(-△Hv^Cu+△Hf^tron+ △Hs^Cu)/3RT , with the parameters relating to the concentration of the diffusion layer, the coefficient of diffusion, the length of diffusion, the latent heat of evaporation and the latent heat of fusion. The activation energy of diffusion of copper in ferrite is approximately 221. 688 kJ/mol. The antibacterial property of the steel is improved as the surface segregation of the copper is increased. At 1 073 K for 60 min, the concentration of the surface copper is over three times higher than the basic concentration. The antibacterial property of the stainless steel can reach approximately 99.9%.展开更多
A continuous wave diode laser with an output power of 2.8 kW was used to join pure copper and 304 stainless steel with a thickness of 1 mm. The focused laser beam with a diameter of O. 8 mm was irradiated on the coppe...A continuous wave diode laser with an output power of 2.8 kW was used to join pure copper and 304 stainless steel with a thickness of 1 mm. The focused laser beam with a diameter of O. 8 mm was irradiated on the copper side of the butt joints. In process of laser welding, effects of processing primary parameters on tensile strength of the joints were investigated. The interfacial characterizations of the joints were investigated by metallographic microscope, scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDS). The results showed that the element diffusion and solution occur and metallurgical bonding was achieved between pure copper and 304 stainless steel. The maximum tensile strength of the joints was 209 MPa when the laser power of welding was 2. 4 kW and welding speed was 12 mm/s.展开更多
Antibacterial activity of AISI420 stainless steel (SS) implanted by copper was investigated. Ions extracted from a metal vapor vacuum arc (MEVVA) are sourced with 100keV energy and a dose range from 0.2×1017 to 2...Antibacterial activity of AISI420 stainless steel (SS) implanted by copper was investigated. Ions extracted from a metal vapor vacuum arc (MEVVA) are sourced with 100keV energy and a dose range from 0.2×1017 to 2.0×1017ions·cm-2. The saturation dose of Cu implantation in AISI420 SS and Cu surface concentration were calculated at the energy of 100keV. The effect of dose on the antibacterial activity was analyzed. Results of antibacterial test show that the saturation dose is the optimum implantation dose for best antibacterial activity, which is above 99% against both Escherichia coli and Staphylococcus aureus. Novel phases such as Fe4Cu3 and Cu9.9Fe0.1 were found in the implanted layer by glancing angle X-ray diffraction (GXRD). The antibacterial activity of AISI420 SS attributes to Cu-contained phase.展开更多
基金supported by the 2020 Ningbo“3315 Talent Introduction Plan”Innovative Team(C-Class)the major project of Ningbo“Scientific and Technological Innovation 2025”(Grant No.2020Z111)。
文摘Thermal fatigue performance of copper/stainless steel explosive welding joint was investigated by using a highly effective thermal fatigue test device. The testing device adopted induction coil to heat and carry out two groups of thermal fatigue test at the same time. Metallurgical microscope and scanning electron microscope were used to respectively measure the surface crack and cross-section crack propagation morphology of the explosive welding joint specimen that were conducted thermal cycling for different upper limit temperatures and different cycle time.Experimental results indicated that the cyclic thermal stress and oxidation corrosion was the major factors for fatigue damage behavior of explosive welding joints, where the oxidation corrosion of the interface has become more serious with the increasing the upper limit temperature or the number of cycles rising. Thermal fatigue cracks initiation was mainly beginning from the wavy interface between copper and stainless steel, the vortex-like cast microstructure formed by explosive welding can prevent the crack from propagating along the interface edge and change the direction of crack propagation.The initiation and expansionof thermal fatigue cracks were observed in the copper matrix.
基金the National Natural Science Foundation of China(Nos.52074078 and 52374327)the Applied Fundamental Research Program of Liaoning Province(No.2023JH2/101600002)+2 种基金the Shenyang Young Middle-Aged Scientific and Technological Innovation Talent Support Program(No.RC220491)the Liaoning Province Steel Industry-University-Research Innovation Alliance Cooperation Project of Bensteel Group(No.KJBLM202202)the Fundamental Research Funds for the Central Universities(Nos.N2201023 and N2325009).
文摘Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimental environmental issues.To prevent chromium pollution,the effects of iron oxide on crystallization behavior and spatial distribution of spinel were investigated in this work.The results revealed that FeO was more conducive to the growth of spinels compared with Fe2O3 and Fe3O4.Spinels were found to be mainly distrib-uted at the top and bottom of slag.The amount of spinel phase at the bottom decreased with the increasing FeO content,while that at the top increased.The average particle size of spinel in the slag with 18wt%FeO content was 12.8μm.Meanwhile,no notable structural changes were observed with a further increase in FeO content.In other words,the spatial distribution of spinel changed when the content of iron oxide varied in the range of 8wt%to 18wt%.Finally,less spinel was found at the bottom of slag with a FeO content of 23wt%.
基金supported by the Inner Mongolia Autonomous Region Science and Technology Major Special Project(Grant No.2021SZD0082).
文摘Stainless steels are used in a wide range of complex environments due to their excellent corrosion resistance.Multiphase stainless steels can offer an excellent combination of strength,toughness and corrosion resistance due to the coexistence of different microstructures.The microstructure and mechanical properties of a novel cast multiphase stainless steel,composed of martensite,ferrite,and austenite,were investigated following appropriate heat treatment processes:solution treatment at 1,050℃ for 0.5 h followed by water quenching to room temperature,and aging treatment at 500℃ for 4 h followed by water quenching to room temperature.Results show reversed austenite is formed by diffusion of Ni element during aging process,and the enrichment of Ni atoms directly determines the mechanical stability of austenite.The austenite with a lower Ni content undergoes a martensitic transformation during plastic deformation.The tensile strength of the specimen exceeds 1,100 MPa and the elongation exceeds 24%after solid solution,and further increases to 1,247 MPa and 25%after aging treatment.This enhancement is due to the TRIP effect of austenite and the precipitation of the nanoscale G-phase pinning dislocations in ferrite and martensite.
文摘In the present work,plastic deformation mechanisms were initially tailored by adjusting the deformation temperature in the range of 0 to 200℃ in AISI 304L austenitic stainless steel,aiming to optimize the strength-ductility synergy.It was shown that the combined twinning-induced plasticity(TWIP)/transformation-induced plasticity(TRIP)effects and a wider strain range for the TRIP effect up to higher strains by adjusting the deformation temperature are good strategies to improve the strength-ductility synergy of this metastable stainless steel.In this regard,by consideration of the observed temperature-dependency of plastic deformation,the controlled sequence of TWIP and TRIP effects for archiving superior strength-ductility trade-off was intended by the pre-designed temperature jump tensile tests.Accordingly,the optimum tensile toughness of 846 MJ/m^(3) and total elongation to 133% were obtained by this strategy via exploiting the advantages of the TWIP effect at 100℃ and the TRIP effect at 25℃ at the later stages of the straining.Consequently,a deformation-temperature-transformation(DTT)diagram was developed for this metastable alloy.Moreover,based on work-hardening analysis,it was found that the main phenomenon constraining further improvement in the ductility and strengthening was the yielding of the deformation-induced α′-martensite.
文摘Non-penetration laser welding of lap joints in austenitic stainless steel sheets is commonly preferred in fields where the surface quality is of utmost importance.However,the application of non-penetration welded austenitic stainless steel parts is limited owing to the micro bulging distortion that occurs on the back surface of the partial penetration side.In this paper,non-penetration lap laser welding experiments,were conducted on galvanized and SUS304 austenitic stainless steel plates using a fiber laser,to investigate the mechanism of bulging distortion.A comparative experiment of DC01 galvanized steel-Q235 carbon steel lap laser welding was carried out,and the deflection and distortion profile of partially penetrated side of the sheets were measured using a noncontact laser interferometer.In addition,the cold-rolled SUS304 was subjected to heat holding at different temperatures and water quenching after bending to characterize its microstructure under tensile and compressive stress.The results show that,during the heating stage of the thermal cycle of laser lap welding,the partial penetration side of the SUS304 steel sheet generates compressive stress,which extrudes the material in the heat-affected zone to the outside of the back of the SUS304 steel sheet,thereby forming a bulge.The findings of these experiments can be of great value for controlling the distortion of the partial penetrated side of austenitic stainless steel sheet during laser non-penetration lap welding.
文摘Duplex stainless steels(DSSs)show better corrosion resistance with higher strength than traditional austenite stainless steels in many aggressive environments,and can be welded properly with almost every welding processes,if proper heat input is provided.Progresses of research works on weldability of DSSs in recent years are reviewed in this paper.Balance control of ferrite/austenite phases is most important for DSSs welding.The phases balance can be controlled with filler materials,nitrogen addition in shielding gas,heat input,post weld heat treatment,and alternating magnetic field.Too high cooling rate results in not only extra ferrite,but also chromium nitride precipitation.While too low cooling rate or heating repeatedly results in precipitation of secondary austenite and intermetallic compounds.In both situations,mechanical properties and corrosion resistance of the DSS joints deteriorate.Recommended upper and lower limits of heat input and maximum interpass temperature should be observed.
文摘Excellent weldability substantially contributes to the intrinsic quality of steels,while appropriate chemical composition plays a primary role in the essential weldability of steels.The poor weldability of ferritic stainless steels could be improved through modification with minor alloy elements while minimally increasing the cost.Therefore,studying the effect of minor alloy elements on the weldability of steels is of considerable importance.In this study,several steels of middle-chromium hyperpure ferritic stainless 00Cr21Ti with different Ni content(0.3%,0.5%,0.8%,and 1.0%)were developed,and their weldabilities of butt joint samples welded using the metal inert gas welding process,including the influence of welded joints on the microstructure,tensile performance,corrosion resistance,and fatigue property,were investigated.Results show that the steels with w(Ni)≥0.8%exhibit excellent mechanical properties compared with those with low-Ni content steels,further,their impact toughness at normal atmospheric temperature meets the industrial application standard and the fatigue property is similar to that of 304 austenitic stainless steel.Moreover,results show that the corrosion resistance of all the samples is almost at the same level.The results acquired in this study are supposed to be useful for the optimization of the chemical composition of stainless steels aiming to improve weldability.
文摘Starting from the corrosion mechanism,this paper analyzes the characteristics of various types of stainless steel and selects the best performance composite plate composite plate stainless steel.Analyze and select the most suitable corrosion detection method based on specific practical multi working conditions,discuss the interference factors that affect metal corrosion during experimental simulation,and the advantages of newly developed sheet metal.The new development of composite board panels,with the substrate and composite materials applying their respective capabilities for MED,will bring breakthrough progress to the scientific research and engineering applica-tion of composite boards.
基金financially supported of the National Natural Science Foundation of China (Nos.52101105 and 51975263)。
文摘The corrosion behavior of 304L stainless steel(SS)in 3.5wt%NaCl solution after different cavitation erosion(CE)times was mainly evaluated using electrochemical noise and potentiostatic polarization techniques.It was found that the antagonism effect resulting in the passivation and depassivation of 304L SS had significant distinctions at different CE periods.The passive behavior was predominant during the incubation period of CE where the metastable pitting initiated at the surface of 304L SS.Over the rising period of CE,the 304L SS experienced a transition from passivation to depassivation,leading to the massive growth of metastable pitting and stable pitting.The depassivation of304L SS was found to be dominant at the stable period of CE where serious localized corrosion occurred.
基金financially supported by the National Natural Science Foundation of China (Nos. 52171057, 52034005, 51901225, and 12027813)the Liaoning Province Excellent Youth Foundation, China (No. 2021-YQ-01)the Youth Innovation Promotion Association of the Chinese Academy of Sciences (No. Y2021061)
文摘The reliable welding of T91 heat-resistant steel to 316L stainless steel is a considerable issue for ensuring the safety in service of ultrasupercritical power generation unit and nuclear fusion reactor,but the high-quality dissimilar joint of these two steels was difficult to be obtained by traditional fusion welding methods.Here we improved the structure-property synergy in a dissimilar joint of T91 steel to 316L steel via friction stir welding.A defect-free joint with a large bonding interface was produced using a small-sized tool under a relatively high welding speed.The bonding interface was involved in a mixing zone with both mechanical mixing and metallurgical bonding.No obvious material softening was detected in the joint except a negligible hardness decline of only HV~10 in the heat-affected zone of the T91 steel side due to the formation of ferrite phase.The welded joint exhibited an excellent ultimate tensile strength as high as that of the 316L parent metal and a greatly enhanced yield strength on account of the dependable bonding and material renovation in the weld zone.This work recommends a promising technique for producing high-strength weldments of dissimilar nuclear steels.
基金supported by the National Natural Science Foundation of China(Grant No.50671101).
文摘A preliminary study was made on the antibacterial mechanism of copper-bearing antibacterial stainless steels against E.coli through experiments of microbiology such as EDTA (ethylenediaminetetraacetic acid) complexing, DNA smearing and AFM (atomic force microscope) observation. It was measured that the antibacterial stainless steels showed excellent antibacterial functions with antibacterial rate to E.coli over 99.99%. The antibacterial rate was weak if the bacteria solution was complexed by EDTA, indicating that the copper ions play a dominant role in the antibacterial effect of the antibacterial stainless steels. The electrophoresis experiment did not show the phenomenon of DNA smearing for E.coli after contacting antibacterial stainless steels, which meant that DNA of E.coli was not obviously damaged. It was observed by AFM that the morphology of E.coli changed a lot after contacting antibacterial stainless steels, such as cell walls being seriously changed and lots of contents in the cells being leaked.
基金the funding support of Babol Noshirvani University of Technology (No. BNUT/370167/97)
文摘Dissimilar joints comprised of copper–nickel and steel alloys are a challenge for manufacturers in modern industries, as these metals are not thermomechanically or chemically well matched. The present study investigated the effects of tool rotational speed and linear speed on the microstructure and mechanical properties of friction stir-welded C71000 copper–nickel and 340 stainless steel alloys using a tungsten carbide tool with a cylindrical pin. The results indicated that a rotational-to-linear speed ratio of 12.5 r/mm did not cause any macro defects, whereas some tunneling defects and longitudinal cracks were found at other ratios that were lower and higher. Furthermore, chromium carbide was formed on the grain boundaries of the 304 stainless steel near the shoulder zone and inside the joint zone, directing carbon and chromium penetration toward the grain boundaries. Tensile strength and elongation percentages were 84% and 65% of the corresponding values in the copper–nickel base metal, respectively.
基金supported by the National Natural Science Foundation of China (No.50101009)
文摘Copper ions were implanted into austenitic stainless steel (SS) by metal vapor vacuum arc with a energy of 100 keV and an ions dose range of (0.5-8.0)× 10^17 cm^-2. The Cu-implanted SS was annealed in an Ar atmosphere furnace. Glancing X-ray diffraction (GXRD), transmission electron microscopy (TEM) and Auger electron spectroscopy (AES) were used to reveal the phase compositions, microstructures, and concentration profiles of copper ions in the implanted layer. The results show that the antibacterial property of Cu-implanted SS is attributed to Cu9.9Fe0.1, which precipitated as needles. The depth of copper in Cu-implanted SS with annealing treatment is greater than that in Cu-implanted SS without annealing treatment, which improves the antibacterial property against S. aureus. The salt wetting-drying combined cyclic test was used to evaluate the corrosion-resistance of antibacterial SS, and the results reveal that the antibacterial SS has a level of corrosion-resistance equivalent to that of un-implanted SS.
文摘With CuMn alloy as interlayer, the transient liquid phase (TLP) diffusion bonding of Cu alloys (CuAlBe) to stainless steel (1Cr18Ni9Ti) was studied. The results show that the bonding pressure, time and temperature and the content of Mn in CuMn alloy have great effects on the strength of bonding interface; when they are 1 MPa, 40 min, 1 223 K and 30% respectively, the maximum joint strength of 487 MPa is attained. The fracture occurring at the bonding interface is a plastic one and the effect of Mn has been analyzed.
文摘Austenite antibacterial stainless steels have been found to have wide applications in hospitals and food industries. In recent years epsilon copper precipitation in antibacterial stainless steels has obtained much research interest due to its antibacterial action. The objective of this study was to determine the effects of nitrogen concentration on the precipitation of epsilon copper and antibacterial property. Two kinds of austenite antibacterial stainless steels containing copper and different nitrogen concentration (0.02 and 0.08 wt pct, respectively) were prepared and the microstructures were characterized by a combination of electron microscopy and thermodynamic analysis. A mathematical expression was deduced to predict the effect of nitrogen concentration on the activity coefficient of copper, In(fCu/f^0cu)=0.53524+4.11xN-0.48x^2N. Higher nitrogen was found to increase the free energy difference of copper concentration distribution between precipitation phase and austenite matrix, stimulate the aggregation of copper atoms from austenite, increase the precipitation amount and consequently enhance the antibacterial property of steel.
基金supported by the National Natural Science Foundation of China (Nos. 50771075 and 51171133) the Program for New Century Excellent Talents in University of Ministries of the Education of China (No.NECT-07-0650)
文摘Silver or copper ions are often chosen as antibacterial agents. But a few reports are concerned with these two antibacterial agents for preparation of antibacterial stainless steel (SS). The antibacterial properties and corrosion resistance of AISI 420 stainless steel implanted by silver and copper ions were investigated. Due to the cooperative antibacterial effect of silver and copper ions, the Ag/Cu implanted SS showed excellent antibacterial activities against both Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus) at a total implantation dose of 2~ 1017 ions/cm2. Electrochemical polarization curves revealed that the corrosion resistance of Ag/Cu implanted SS was slightly enhanced as compared with that of un-implanted SS, The implanted layer was characterized by X-ray photoelec- tron spectroscopy (XPS). Core level XPS spectra indicate that the implanted silver and copper ions exist in metallic state in the implanted layer.
文摘The precipitation of epsilon copper at 1023 K ageing in ferrite antibacterial stainless steel was investigated by a combination of electron microscopy and micro-Vickers hardness measurement. The results show that epsilon copper precipitation occurs within 90 s, Complex multilayer structure confirmed as twins and stacking faults on {111}ε-Cu planes was observed in the precipitates. The precipitates grow by the lengthwise enlargement of a set of parallel layers, having [111]ε-Cu and [112]ε-Cu preferred growth orientations. The volume fraction of precipitates f formed within 120 min can be predicted by a modified Avrami equation (In1/1-f= kt + b). Simultaneously, substituent atom clusters with a size of 5-10 nm was found to occur in the solution and cause matrix strain. The precipitate morphology and distribution on the surface of ferrite antibacterial stainless steel are associated with surface crystallographic orientation of the matrix. The precipitates are predominantly located within the ferrite grains of 〈110〉 orientation. The precipitates located on {111}α-Fe surface planes have sphere or ellipse shape.
文摘By using auger electron spectroscopy (AES) and diffusion theory to analyze the surface segregation of copper in antibacterial ferritic stainless steel, establishing a diffusion model, and calculating the activation energy of diffusion of the copper in ferrite, the affect of surface segregation on the antibacterial capabilities were researched. The results show that the concentration of the copper surface at 973 K and 1 073 K could be expressed asln X^sCu/X^bCu = k0 √Dt/d(-△Hv^Cu+△Hf^tron+ △Hs^Cu)/3RT , with the parameters relating to the concentration of the diffusion layer, the coefficient of diffusion, the length of diffusion, the latent heat of evaporation and the latent heat of fusion. The activation energy of diffusion of copper in ferrite is approximately 221. 688 kJ/mol. The antibacterial property of the steel is improved as the surface segregation of the copper is increased. At 1 073 K for 60 min, the concentration of the surface copper is over three times higher than the basic concentration. The antibacterial property of the stainless steel can reach approximately 99.9%.
文摘A continuous wave diode laser with an output power of 2.8 kW was used to join pure copper and 304 stainless steel with a thickness of 1 mm. The focused laser beam with a diameter of O. 8 mm was irradiated on the copper side of the butt joints. In process of laser welding, effects of processing primary parameters on tensile strength of the joints were investigated. The interfacial characterizations of the joints were investigated by metallographic microscope, scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDS). The results showed that the element diffusion and solution occur and metallurgical bonding was achieved between pure copper and 304 stainless steel. The maximum tensile strength of the joints was 209 MPa when the laser power of welding was 2. 4 kW and welding speed was 12 mm/s.
基金This work was supported by the National Natural Science Foundation of China(No.50101009)
文摘Antibacterial activity of AISI420 stainless steel (SS) implanted by copper was investigated. Ions extracted from a metal vapor vacuum arc (MEVVA) are sourced with 100keV energy and a dose range from 0.2×1017 to 2.0×1017ions·cm-2. The saturation dose of Cu implantation in AISI420 SS and Cu surface concentration were calculated at the energy of 100keV. The effect of dose on the antibacterial activity was analyzed. Results of antibacterial test show that the saturation dose is the optimum implantation dose for best antibacterial activity, which is above 99% against both Escherichia coli and Staphylococcus aureus. Novel phases such as Fe4Cu3 and Cu9.9Fe0.1 were found in the implanted layer by glancing angle X-ray diffraction (GXRD). The antibacterial activity of AISI420 SS attributes to Cu-contained phase.