The solid structures and thermostabilities of Cu-Fe-O and Cu-Fe-Ce-O supported on alumina were studied by XRD, ESR, Mossbauer and TPR techniques. The studies indicate that there are Fe2CuO4, CuO and alpha-Fe2O3 phases...The solid structures and thermostabilities of Cu-Fe-O and Cu-Fe-Ce-O supported on alumina were studied by XRD, ESR, Mossbauer and TPR techniques. The studies indicate that there are Fe2CuO4, CuO and alpha-Fe2O3 phases in Cu-Fe-O with the granula of less than 13 nm. With the catalyst pretreatment temperature rising, the crystallite of Fe2CuO4 in the catalysts grows up and that of CuO disappears gradually. The presence of Ce leads to the increase of Cu2+ concentration, inhibits the crystal growth of CuO and Fe2CuO4 in the catalyst except that of Fe2O3, and eliminates the difference for reductive reaction of oxygen in Fe-O and Cu-O. At 800 degrees C, the crystal growth of Fe2O3 in Cu-Fe-Ce-O is slower than that in Cu-Fe-O, i.e., CeO2 in Cu-Fe-Ce-O inhibits the growth of Fe2O3 phase effectively, and enhances the thermostability of catalysts so as to avoid the sintering of active elements in catalysts. CeO2 promotes the reducibility of catalysts at lower temperature.展开更多
According to the chemical and phase composition of the nickel-copper-iron matte containing precious metals and the progress in enrichment of precious metals from the nickel-copper-iron matte containing precious metals...According to the chemical and phase composition of the nickel-copper-iron matte containing precious metals and the progress in enrichment of precious metals from the nickel-copper-iron matte containing precious metals at home and abroad, this paper put forward the process route of enrichment of precious metals and selectively leaching of base metals from the nickel-copper-iron matte by sulfuric acid and sodium hypochlorite. The effects of particle size, leaching temperature, leaching time, amount of sulfuric acid and sodium hypochlorite on the leaching rate of nickel, cobalt, copper and iron are mainly discussed. The results show that raw material particle size has significantly effects on the leaching rate of base metals, high leaching rate of base metals and enrichment of precious metals are obtained with the suitable particle size. Through the experiments, the reasonable experiment parameters and conditions were determined as fellows: particle size of-200 to +250 mesh, leaching temperature 95℃ , leaching time 5 h, sulfuric acid concentration 30%, adding amount of sodium hypochlorite 3 times of matte weight. Under these experiment parameters and conditions, the leaching rate of nickel, cobalt, copper and iron were 97.39%, 96.24%, 98.30% and 99.01%, respectively. The content of nickel, cobalt, copper, iron in the leaching residues was 8.15%, 0.23%, 1.40% and 0.24%, respectively. The content of Pt, Pd, Au, Ag and Rh in the leaching residues was 247 g/t, 521 g/t, 112 g/t, 494 g/t and 24 g/t, respectively. The content of Pt, Pd, Au, Ag and Rh in the leaching solution was <0.0005 g/L, 0.0023 g/L, 0.0007 g/L, <0.0005 g/L and 0.00017 g/L, respectively. This process has advantages as follows: a small investment, simple technology, high enrichment efficiency.展开更多
采用种子生长法制备金纳米棒(AuNRs)以构建光学传感器,用于Fe^(3+)和Cu^(2+)的高选择性快速可视化检测。在酸性环境中,Fe^(3+)和Cu^(2+)通过与KI溶液反应,将I-氧化成I2。I2刻蚀AuNRs,导致其纵向表面等离子体共振(LSPR)吸收峰蓝移,从而...采用种子生长法制备金纳米棒(AuNRs)以构建光学传感器,用于Fe^(3+)和Cu^(2+)的高选择性快速可视化检测。在酸性环境中,Fe^(3+)和Cu^(2+)通过与KI溶液反应,将I-氧化成I2。I2刻蚀AuNRs,导致其纵向表面等离子体共振(LSPR)吸收峰蓝移,从而实现对Fe^(3+)和Cu^(2+)的检测。结果表明,反应温度为50℃时,添加0.8 mL 0.1 mol·L^(-1)HCl、2 mL AuNRs生长液和20 mmol·L^(-1)KI溶液,与2 mL 500μmol·L^(-1)Fe^(3+)或30μmol·L^(-1)Cu^(2+)反应25或90 min,可将AuNRs刻蚀至LSPR吸收峰消失。该方法对Fe^(3+)和Cu^(2+)检测具有高选择性和准确性,对于Fe^(3+)、Cu^(2+)共存体系的检测,可通过加入适量F-与Fe^(3+)生成配合物[FeF_(6)]^(3-)完成对Fe^(3+)的化学掩蔽,消除Fe^(3+)的干扰,实现共存体系中Cu^(2+)的准确检测。展开更多
文摘The solid structures and thermostabilities of Cu-Fe-O and Cu-Fe-Ce-O supported on alumina were studied by XRD, ESR, Mossbauer and TPR techniques. The studies indicate that there are Fe2CuO4, CuO and alpha-Fe2O3 phases in Cu-Fe-O with the granula of less than 13 nm. With the catalyst pretreatment temperature rising, the crystallite of Fe2CuO4 in the catalysts grows up and that of CuO disappears gradually. The presence of Ce leads to the increase of Cu2+ concentration, inhibits the crystal growth of CuO and Fe2CuO4 in the catalyst except that of Fe2O3, and eliminates the difference for reductive reaction of oxygen in Fe-O and Cu-O. At 800 degrees C, the crystal growth of Fe2O3 in Cu-Fe-Ce-O is slower than that in Cu-Fe-O, i.e., CeO2 in Cu-Fe-Ce-O inhibits the growth of Fe2O3 phase effectively, and enhances the thermostability of catalysts so as to avoid the sintering of active elements in catalysts. CeO2 promotes the reducibility of catalysts at lower temperature.
基金The National Basic Research Program (973 Plan)of China (2012CB724201)
文摘According to the chemical and phase composition of the nickel-copper-iron matte containing precious metals and the progress in enrichment of precious metals from the nickel-copper-iron matte containing precious metals at home and abroad, this paper put forward the process route of enrichment of precious metals and selectively leaching of base metals from the nickel-copper-iron matte by sulfuric acid and sodium hypochlorite. The effects of particle size, leaching temperature, leaching time, amount of sulfuric acid and sodium hypochlorite on the leaching rate of nickel, cobalt, copper and iron are mainly discussed. The results show that raw material particle size has significantly effects on the leaching rate of base metals, high leaching rate of base metals and enrichment of precious metals are obtained with the suitable particle size. Through the experiments, the reasonable experiment parameters and conditions were determined as fellows: particle size of-200 to +250 mesh, leaching temperature 95℃ , leaching time 5 h, sulfuric acid concentration 30%, adding amount of sodium hypochlorite 3 times of matte weight. Under these experiment parameters and conditions, the leaching rate of nickel, cobalt, copper and iron were 97.39%, 96.24%, 98.30% and 99.01%, respectively. The content of nickel, cobalt, copper, iron in the leaching residues was 8.15%, 0.23%, 1.40% and 0.24%, respectively. The content of Pt, Pd, Au, Ag and Rh in the leaching residues was 247 g/t, 521 g/t, 112 g/t, 494 g/t and 24 g/t, respectively. The content of Pt, Pd, Au, Ag and Rh in the leaching solution was <0.0005 g/L, 0.0023 g/L, 0.0007 g/L, <0.0005 g/L and 0.00017 g/L, respectively. This process has advantages as follows: a small investment, simple technology, high enrichment efficiency.
文摘采用种子生长法制备金纳米棒(AuNRs)以构建光学传感器,用于Fe^(3+)和Cu^(2+)的高选择性快速可视化检测。在酸性环境中,Fe^(3+)和Cu^(2+)通过与KI溶液反应,将I-氧化成I2。I2刻蚀AuNRs,导致其纵向表面等离子体共振(LSPR)吸收峰蓝移,从而实现对Fe^(3+)和Cu^(2+)的检测。结果表明,反应温度为50℃时,添加0.8 mL 0.1 mol·L^(-1)HCl、2 mL AuNRs生长液和20 mmol·L^(-1)KI溶液,与2 mL 500μmol·L^(-1)Fe^(3+)或30μmol·L^(-1)Cu^(2+)反应25或90 min,可将AuNRs刻蚀至LSPR吸收峰消失。该方法对Fe^(3+)和Cu^(2+)检测具有高选择性和准确性,对于Fe^(3+)、Cu^(2+)共存体系的检测,可通过加入适量F-与Fe^(3+)生成配合物[FeF_(6)]^(3-)完成对Fe^(3+)的化学掩蔽,消除Fe^(3+)的干扰,实现共存体系中Cu^(2+)的准确检测。