Many properties of polyester filaments such as heat shrinkage, tenacity, elongation at break and etc. are greatly influenced by drawing, so post-drawing is important in downstream processing. As more and more profile ...Many properties of polyester filaments such as heat shrinkage, tenacity, elongation at break and etc. are greatly influenced by drawing, so post-drawing is important in downstream processing. As more and more profile fibers and multi-variance fibers used in textile industry, the properties of above two kinds of differential polyester filaments after drawing in different heat conditions were studied. Finally following conclusions were obtained: Firstly, the tenacity and elongation at break decreases with the rise of Tp. Secondly, the tenacity rises but the elongation at break decreases with the increase of Tb. Then, when the Tb is low, both the shrinkage in boiling water and hi hot air decreases with the rise of Tp, while, when the Tb is high, both the shrinkage rises with the rise of Tp. The last, both the shrinkage decreases with the rise of Tb.展开更多
In this paper the influences of the drawing temperature on physical structures and properties of PET filaments have been studied. The results show that the temperatures of the first-stage drawing will have significant...In this paper the influences of the drawing temperature on physical structures and properties of PET filaments have been studied. The results show that the temperatures of the first-stage drawing will have significant effects on birefringence development of filaments during the second stage drawing, as well as the oriented amorphous filaments change to crystanine-oriented filaments after heat treatment. Increasing temperature of the second-stage drawing can be greatly increasing the crystallinity and decreasing the dry heat shrinkage of the filaments.展开更多
From the effects of the composition of the three kinds ofblended systems, the antistatic agent content and theblending methods on the spinnability, the antistatic prop-erty, and the wash fastness of PET filament, it i...From the effects of the composition of the three kinds ofblended systems, the antistatic agent content and theblending methods on the spinnability, the antistatic prop-erty, and the wash fastness of PET filament, it is foundthat the antistatic behavior of the (PET) - (PEG) -(SDBS) - stearate quaternary system is improved greatlydue to the synergefic effect of the combined antistaticagents and the volume resistivity of the fiber made.Thereof reaches 10~8 ～ 10~9Ω·cm after being washed 20 tines in saponaceous water at 40℃. Its spinnability anddrawing behavior are good. The effect of the antistaticagent content on the mechanical property of PET fila-ment is also studied.展开更多
文摘Many properties of polyester filaments such as heat shrinkage, tenacity, elongation at break and etc. are greatly influenced by drawing, so post-drawing is important in downstream processing. As more and more profile fibers and multi-variance fibers used in textile industry, the properties of above two kinds of differential polyester filaments after drawing in different heat conditions were studied. Finally following conclusions were obtained: Firstly, the tenacity and elongation at break decreases with the rise of Tp. Secondly, the tenacity rises but the elongation at break decreases with the increase of Tb. Then, when the Tb is low, both the shrinkage in boiling water and hi hot air decreases with the rise of Tp, while, when the Tb is high, both the shrinkage rises with the rise of Tp. The last, both the shrinkage decreases with the rise of Tb.
文摘In this paper the influences of the drawing temperature on physical structures and properties of PET filaments have been studied. The results show that the temperatures of the first-stage drawing will have significant effects on birefringence development of filaments during the second stage drawing, as well as the oriented amorphous filaments change to crystanine-oriented filaments after heat treatment. Increasing temperature of the second-stage drawing can be greatly increasing the crystallinity and decreasing the dry heat shrinkage of the filaments.
文摘From the effects of the composition of the three kinds ofblended systems, the antistatic agent content and theblending methods on the spinnability, the antistatic prop-erty, and the wash fastness of PET filament, it is foundthat the antistatic behavior of the (PET) - (PEG) -(SDBS) - stearate quaternary system is improved greatlydue to the synergefic effect of the combined antistaticagents and the volume resistivity of the fiber made.Thereof reaches 10~8 ～ 10~9Ω·cm after being washed 20 tines in saponaceous water at 40℃. Its spinnability anddrawing behavior are good. The effect of the antistaticagent content on the mechanical property of PET fila-ment is also studied.