A wear resistant （Cr, Fe）7C3/γ-Fe ceramalcomposite coating wasfabricatedon substrate of a 0.45% C carbon steel by plasma transferred arc （PTA） cladding process using the Fe-Cr-C elemental powder blends. The micro...A wear resistant （Cr, Fe）7C3/γ-Fe ceramalcomposite coating wasfabricatedon substrate of a 0.45% C carbon steel by plasma transferred arc （PTA） cladding process using the Fe-Cr-C elemental powder blends. The microstructure, microhardness and dry sliding wear resistance of the coating were evaluated. Results indicate that the plasma transferred arc clad ceramal composite coating has a rapidly solidified microstructure consisting of blocky primary （Cr, Fe）7C3 and the interblocky （ Cr, Fe）7C3/γ-Fe eutectics and is metallurgically bonded to the 0.45%C carbon steel substrate. The ceramal composite coating has high hardness and excellent wear resistance under dry sliding wear test condition.展开更多
A wear-resistant （Cr, Fe）7C3/γ-Fe in situ ceramal composite coating was fabricated on the substrate of 0.45wt%C carbon steel by a plasma-transferred arc cladding process using the Fe-Cr-C elemental powder blends. T...A wear-resistant （Cr, Fe）7C3/γ-Fe in situ ceramal composite coating was fabricated on the substrate of 0.45wt%C carbon steel by a plasma-transferred arc cladding process using the Fe-Cr-C elemental powder blends. The microstructure, microhardness, and dry-sliding wear resistance of the coating were evaluated. The results indicate that the microstructure of the coating, which was composed of （Cr, Fe）7C3 primary phase uniformly distributed in the γ-Fe, and the （Cr, Fe）7C3 eutectic matrix was metallurgically bonded to the 0.45wt%C carbon steel substrate. From substrate to coating, the microstructure of the coating exhibited an evident epitaxial growth character. The coating, indehiscent and tack-free, had high hardness and appropriate gradient. It had excellent wear resistance under the dry sliding wear test condition.展开更多
文摘A wear resistant （Cr, Fe）7C3/γ-Fe ceramalcomposite coating wasfabricatedon substrate of a 0.45% C carbon steel by plasma transferred arc （PTA） cladding process using the Fe-Cr-C elemental powder blends. The microstructure, microhardness and dry sliding wear resistance of the coating were evaluated. Results indicate that the plasma transferred arc clad ceramal composite coating has a rapidly solidified microstructure consisting of blocky primary （Cr, Fe）7C3 and the interblocky （ Cr, Fe）7C3/γ-Fe eutectics and is metallurgically bonded to the 0.45%C carbon steel substrate. The ceramal composite coating has high hardness and excellent wear resistance under dry sliding wear test condition.
文摘A wear-resistant （Cr, Fe）7C3/γ-Fe in situ ceramal composite coating was fabricated on the substrate of 0.45wt%C carbon steel by a plasma-transferred arc cladding process using the Fe-Cr-C elemental powder blends. The microstructure, microhardness, and dry-sliding wear resistance of the coating were evaluated. The results indicate that the microstructure of the coating, which was composed of （Cr, Fe）7C3 primary phase uniformly distributed in the γ-Fe, and the （Cr, Fe）7C3 eutectic matrix was metallurgically bonded to the 0.45wt%C carbon steel substrate. From substrate to coating, the microstructure of the coating exhibited an evident epitaxial growth character. The coating, indehiscent and tack-free, had high hardness and appropriate gradient. It had excellent wear resistance under the dry sliding wear test condition.
