Effect of Heat Treatment on Mechanical Property of High Cr-W Cast Iron

The microstructure of high Cr-W cast iron after heat treatment were analyzed, and the effect of various heat treatment temperature and time on mechanical properties of high Cr-W cast iron were studied, and the best process parameter of heat treatment was provided in this paper. The results show that the heat treatment can improve the mechanical property of high Cr-W cast iron, and higher synthetic mechanical property of high Cr-W cast iron can be obtained when treated with normalization at 980 ℃ for 2 h and tempered at 400 ℃ for 2 h.

W对铸态高铬铸铁组织和性能的影响

采用金相显微镜、扫描电镜观察显微组织,X射线衍射分析相组成,并测定洛氏硬度、冲击韧度及耐磨性,研究了w(W)量对高铬铸铁组织及性能的影响。结果表明:含钨高铬铸铁的铸态组织为马氏体+奥氏体+碳化物;W在碳化物和基体中均匀分布,w(W)量为1%时,高铬铸铁硬度为58.75HRC,冲击韧度为11.18J/cm^2;w(W)量达到3%时,高铬铸铁冲击韧度明显下降;w(W)量在0~3%范围内渐增时,随着w(W)量的增加,耐磨性不断提高。

单辊破碎机耐磨技术研究概况

简要介绍了单辊破碎机的工作环境和使用情况。为了提高单辊破碎机的使用寿命 ,科研人员作了很多研究 ,主要有两方面 :一方面是在单辊破碎机的星轮表面堆焊抗高温耐磨材料 ;另一方面是改进单辊破碎机的星轮材料。我们根据单辊破碎机的工作环境、使用情况及磨损机理研制出了一种新型铬锰钨铸铁 ,通过手工焊接在邯钢一烧 40 0m2 烧结机单辊星轮上 ,运行两个月后 ,磨损还不到 5mm 。

含钨钒高铬白口铸铁退火工艺的研究

研究了退火工艺对含钨钒高铬白口铸铁组织和硬度的影响。结果表明,采用1050℃保温4h,随后于720℃保温10h的退火工艺,硬度最低,为36HRC,机加工性能最好。

热处理对高铬钨铸铁性能的影响

研究了热处理对高铬钨铸铁力学性能的影响,结果表明,高铬钨铸铁经980℃×2h空冷+400℃×2h回火处理可获得较高的力学性能。

高铬钨铸铁的软化退火工艺

针对高铬钨铸铁硬度高这一问题,对其软化退化工艺进行试验,并对高铬钨铸铁退火过程中组织转变进行分析。在此基础上,提出了合理的软化退火工艺。

钨铬合金白口铸铁的外约束型热疲劳特性

为开发钨铬合金白口铸铁轧辊的新型材料，对在外约束条件下的热疲劳行为进行了研究．结果表明，影响其外约束热疲劳抗力的主要因素是屈服温度和强度，屈服温度越高，屈服强度越大，热疲劳抗力越大；随着循环上限温度的升高，产生的塑性变形越大，随着拉应力达到循环稳定所需次数的增多，热疲劳抗力下降，且钨铬合金的热疲劳断口呈解理断裂特征．

价值工程理论在九轴筛改造成蓖条筛设计中的应用

运用价值工程理论将九轴筛改造成篦条筛，在功能分析的基础上确定了铬钨白口铸铁与碳钢复今筛条结构。经装机考核，其使用寿命由原４５ｄ延长为３６０ｄ功能价值系数由０．０３５增加到１０收到了显著的经济效益和社会效益。