Deactivation mechanism of Cr-Al2O3catalyst and the interaction of Cr-A1 in the dehydrogenation of isobutane, as well as the nature of the catalytic active center, were studied using XRD, SEM, XPS, H2-TPR, isobutane-TP...Deactivation mechanism of Cr-Al2O3catalyst and the interaction of Cr-A1 in the dehydrogenation of isobutane, as well as the nature of the catalytic active center, were studied using XRD, SEM, XPS, H2-TPR, isobutane-TPR and TPO techniques. The results revealed that the deactivation of Cr-Al2O3 catalyst was mainly caused by carbon deposition on its surface. The Cr3＋ ion could not be reduced by hydrogen but could be reduced to Cr2＋ by hydrocarbons and monoxide carbon. The active center for isobutane dehydrogenation could be Cr2＋/Cr3＋ produced from Cr6＋ by the on line reduction of hydrocarbon and carbon monoxide. The binding energy of Al3＋ was strongly affected by the state of chromium cations in the catalysts.展开更多
Alumina supports modified by lanthanum （La） and barium （Ba） were prepared by peptization. Catalysts with different KOH contents supported on modified alumina were prepared by impregnation method. Various technique...Alumina supports modified by lanthanum （La） and barium （Ba） were prepared by peptization. Catalysts with different KOH contents supported on modified alumina were prepared by impregnation method. Various techniques, including N2 adsorption-desorption （Brunauer-Emmet-Teller method, BET）, X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and fourier transform infrared absorption spectroscopy （FT-IR）. Catalytic activity for microalgae oil conversion to methyl ester via transesterification was evaluated and analyzed by GC-MS and GC. BET results showed that the support possessed high specific surface area, suitable pore volume and pore size distribution. Activity results indicated that the catalyst with 25 wt% KOH showed the best activity for microalgae oil conversion. XRD and SEM results revealed that Al-O-K compound was the active phase for microalgae oil conversion. The agglomeration and changing of pore structure should be the main reasons for the catalyst deactivation when KOH content was higher than 30 wt%.展开更多
A series of 3.0Mo/MCM-22-Al2O3 catalysts with γ-Al2O3 contents in the range of 0-100 wt% were prepared and applied in the metathesis reaction of ethene and butene-2. Addition of γ-Al2O3did not affect the structure o...A series of 3.0Mo/MCM-22-Al2O3 catalysts with γ-Al2O3 contents in the range of 0-100 wt% were prepared and applied in the metathesis reaction of ethene and butene-2. Addition of γ-Al2O3did not affect the structure of MCM-22 zeolite as evidenced by XRD and N2 adsorption measurements. It was deduced from TPR experiments that γ-Al2O3 phase favored the formation of polymolybdate or multilayered Mo oxide, while more Al2（MoO4）3 species were generated over MCM-22 zeolites. Alumina content in the support was directly related to the metathesis activity of ethene and butene-2 to propene. Mo species with higher valence （Mo6＋or Mo5＋） contributed more to the excellent performance of catalyst than metallic Mo. The best catalyst activity and stability was obtained over 3.0Mo/（MCM-22-30%Al2O3） under the reaction condition of 1.0 MPa and 125℃ using N2 as the pretreatment gas.展开更多
A series of catalysts were prepared using the kneading molding method and the impregnation method as well as the dry mix method by using different raw materials. By using X-ray diffraction (XRD), X-ray photoelectron s...A series of catalysts were prepared using the kneading molding method and the impregnation method as well as the dry mix method by using different raw materials. By using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and temperature-programmed reduction (TPR) techniques, we studied the relationship between the catalyst performance and the Cr-Al interaction in the catalytic dehydrogenation of isobutane. The results demonstrated that the Cr-Al interaction in the catalyst had a direct influence on the catalytic activity and the selectivity of isobutene. The catalysts prepared using the kneading molding method had higher catalytic activity and isobutene selectivity than those prepared using the dry mix method. By comparison, XRD, XPS, and TPR results showed that the greater the Cr-Al interaction in the catalyst was, the higher the catalytic activity was. Here, we propose a mechanism of isobutane dehydrogenation.展开更多
Three kinds of new type solid strong acid catalysts S2O 2-8/ZrO2-Al2O3-M2O3（M=Cr,Ce,La） were prepared. Their crystal structure, surface area, acid strength and sulfur content were determined by means of XRD, BET, fl...Three kinds of new type solid strong acid catalysts S2O 2-8/ZrO2-Al2O3-M2O3（M=Cr,Ce,La） were prepared. Their crystal structure, surface area, acid strength and sulfur content were determined by means of XRD, BET, flow Hammett indicator method and chemical analysis. Their catalytic activities in esterification reaction of acetic acid with n-butanol were studied. The results showed that ZrO2 in the catalysts mainly in tetragonal phase and few in monoclinic phase. The tetragonal phase of ZrO2 and S2O 2-8 are the key factors that guarantee the catalytic activity. Incorporation of appropriate amounts of metallic oxides（Cr2O3,Ce2O3,La2O3） into the catalyst favors the stabilization of sulfur species and surface area, which increase the activity sites on the catalyst. The experimental results showed that three catalysts S2O 2-8/ZrO2-Al2O3（2%）-M2O3（1%）（M=Cr,Ce,La） had higher catalytic activity in mentioned esterification, with the conversion of acetic acid reached 96.8%, 95.7% and 96.1%, respectively. The preparation condition of the catalysts showed great influence on the catalytic activity.展开更多
基金supported by the Natural Science Foundation of Shandong Provence of China(ZR2013BM008)
文摘Deactivation mechanism of Cr-Al2O3catalyst and the interaction of Cr-A1 in the dehydrogenation of isobutane, as well as the nature of the catalytic active center, were studied using XRD, SEM, XPS, H2-TPR, isobutane-TPR and TPO techniques. The results revealed that the deactivation of Cr-Al2O3 catalyst was mainly caused by carbon deposition on its surface. The Cr3＋ ion could not be reduced by hydrogen but could be reduced to Cr2＋ by hydrocarbons and monoxide carbon. The active center for isobutane dehydrogenation could be Cr2＋/Cr3＋ produced from Cr6＋ by the on line reduction of hydrocarbon and carbon monoxide. The binding energy of Al3＋ was strongly affected by the state of chromium cations in the catalysts.
基金supported by the Institute of Chemical Materials Foundation of CAEP(No.626010937)
文摘Alumina supports modified by lanthanum （La） and barium （Ba） were prepared by peptization. Catalysts with different KOH contents supported on modified alumina were prepared by impregnation method. Various techniques, including N2 adsorption-desorption （Brunauer-Emmet-Teller method, BET）, X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and fourier transform infrared absorption spectroscopy （FT-IR）. Catalytic activity for microalgae oil conversion to methyl ester via transesterification was evaluated and analyzed by GC-MS and GC. BET results showed that the support possessed high specific surface area, suitable pore volume and pore size distribution. Activity results indicated that the catalyst with 25 wt% KOH showed the best activity for microalgae oil conversion. XRD and SEM results revealed that Al-O-K compound was the active phase for microalgae oil conversion. The agglomeration and changing of pore structure should be the main reasons for the catalyst deactivation when KOH content was higher than 30 wt%.
基金supported by the National Natural Science Foundation of China (Grant No. 20903088 and 20773120)the Ministry of Science and Technology of China through the National Key Project of Fundamental Research (Grant No.2009CB623507)
文摘A series of 3.0Mo/MCM-22-Al2O3 catalysts with γ-Al2O3 contents in the range of 0-100 wt% were prepared and applied in the metathesis reaction of ethene and butene-2. Addition of γ-Al2O3did not affect the structure of MCM-22 zeolite as evidenced by XRD and N2 adsorption measurements. It was deduced from TPR experiments that γ-Al2O3 phase favored the formation of polymolybdate or multilayered Mo oxide, while more Al2（MoO4）3 species were generated over MCM-22 zeolites. Alumina content in the support was directly related to the metathesis activity of ethene and butene-2 to propene. Mo species with higher valence （Mo6＋or Mo5＋） contributed more to the excellent performance of catalyst than metallic Mo. The best catalyst activity and stability was obtained over 3.0Mo/（MCM-22-30%Al2O3） under the reaction condition of 1.0 MPa and 125℃ using N2 as the pretreatment gas.
文摘A series of catalysts were prepared using the kneading molding method and the impregnation method as well as the dry mix method by using different raw materials. By using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and temperature-programmed reduction (TPR) techniques, we studied the relationship between the catalyst performance and the Cr-Al interaction in the catalytic dehydrogenation of isobutane. The results demonstrated that the Cr-Al interaction in the catalyst had a direct influence on the catalytic activity and the selectivity of isobutene. The catalysts prepared using the kneading molding method had higher catalytic activity and isobutene selectivity than those prepared using the dry mix method. By comparison, XRD, XPS, and TPR results showed that the greater the Cr-Al interaction in the catalyst was, the higher the catalytic activity was. Here, we propose a mechanism of isobutane dehydrogenation.
文摘Three kinds of new type solid strong acid catalysts S2O 2-8/ZrO2-Al2O3-M2O3（M=Cr,Ce,La） were prepared. Their crystal structure, surface area, acid strength and sulfur content were determined by means of XRD, BET, flow Hammett indicator method and chemical analysis. Their catalytic activities in esterification reaction of acetic acid with n-butanol were studied. The results showed that ZrO2 in the catalysts mainly in tetragonal phase and few in monoclinic phase. The tetragonal phase of ZrO2 and S2O 2-8 are the key factors that guarantee the catalytic activity. Incorporation of appropriate amounts of metallic oxides（Cr2O3,Ce2O3,La2O3） into the catalyst favors the stabilization of sulfur species and surface area, which increase the activity sites on the catalyst. The experimental results showed that three catalysts S2O 2-8/ZrO2-Al2O3（2%）-M2O3（1%）（M=Cr,Ce,La） had higher catalytic activity in mentioned esterification, with the conversion of acetic acid reached 96.8%, 95.7% and 96.1%, respectively. The preparation condition of the catalysts showed great influence on the catalytic activity.