Microstructure and corrosion resistance of sputtered TiN coatings on surface of Zr-4 alloy

To improve the oxidation resistance and corrosion resistance of Zr-4 alloy, titanium nitride （TIN） coatings were prepared on the Zr-4 alloy with a TiN ceramic target with different ratios of N2. Microstructure and high-temperature properties of the TiN coated samples were studied by scanning electron microscopy （SEM）, energy dispersive spectrometer （EDS）, X-ray diffraction meter （XRD）, X-ray photoelectron spectroscopy （XPS）, heat treatment furnace and autoclaves, respectively. The x value of the TiN coatings （TiN） ranges from 0.96 to 1.33. After the introduction of N2, TiN coating exhibits a weak （200） plane and a preferred （111） orientation. The coating prepared with an N2 flow ratio of 15% shows an optimal oxidation resistance in the atmospheric environment at 800 ℃. In either 1 200 ℃ steam environment for one hour, or deionized water at 360 ℃ and a pressure of 18.6 Mpa for 16 d, the opitimized TiN coated samples have no delamination or spallation; and the gains in the masses of samples are much smaller than Zr-4 alloy. These results demonstrate the effectiveness of the optimized TiN coating as the protective coating on the Zr-4 alloy under extreme conditons.

Characteristics of Faigue Crack Initiation in Ti-5Al-4Sn-2Zr-1Mo-0.7Nd-0.25Si Alloy

The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.

Hot deformation behaviors and dynamic recrystallization mechanism of Ti-35421 alloy inβsingle field

Hot deformation behaviors and microstructure evolution of Ti-3Al-5Mo-4Cr-2Zr-1Fe(Ti-35421)alloy in theβsingle field are investigated by isothermal compression tests on a Gleeble-3500 simulator at temperatures of 820-900°C and strain rates of 0.001-1 s^(-1).The research results show that discontinuous yield phenomenon and rheological softening are affected by the strain rates and deformation temperatures.The critical conditions for dynamic recrystallization and kinetic model of Ti-35421 alloy are determined,and the Arrhenius constitutive model is constructed.The rheological behaviors of Ti-35421 alloys aboveβphase transformation temperature are predicted by the constitutive model accurately.The EBSD analysis proves that the deformation softening is controlled by dynamic recovery and dynamic recrystallization.In addition,continuous dynamic recrystallization is determined during hot deformation,and the calculation model for recrystallization grain sizes is established.Good linear dependency between the experimental and simulated values of recrystallized grain sizes indicates that the present model can be used for the prediction of recrystallized grain size with high accuracy.

Effect of predeformation on globularization of Ti-5Al-2Sn-2Zr-4Mo-4Cr during annealing

The microstructure evolution during annealing of Ti-5Al-2Sn-2Zr-4Mo-4Cr alloy was investigated. The results show that for the alloy compressed at 810 °C and 1.0 s^-1, deformation amount（height reduction） 20% and 50% and annealed at 810 °C, thermal grooving by penetration of β phase is sufficient during the first 20 min annealing, resulting in a sharp increase in globularization fraction. The globularization fraction continuously increases with the increase of annealing time, and a height reduction of 50% leads to a near globular microstructure after annealing for 4 h. For the alloy with deformation amount of 50% by compressing at 810 °C, 0.01 s^-1, and then annealed at 810 °C, thermal grooving is limited during the first 20 min of annealing and large quantities of high-angle grain boundaries（HABs） remain. With long time annealing, the chain-like α grains are developed due to the HABs, termination migration and Ostwald ripening. The present results suggest that a higher strain rate and a larger height reduction are necessary before annealing to achieve a globular microstructure of Ti-5Al-2Sn-2Zr-4Mo-4Cr.

Intragranular Rare Earth－rich Phases in As－cast High－temperature Ti－5Al－4Sn－2Zr－1MO－0．25Si－1Nd Alloy

In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0～14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher than those at other sites. The intragranular phases grow preferably at the region on the grain boundaries, which causes the formation of the elliptical morphology of the intragranular phases.

Ultraviolet-accelerated formation of bone-like apatite on oxidized Ti-24Nb-4Zr-7.9Sn alloy

A novel method has been developed to rapidly deposit bone-like apatite with the assistance of ultraviolet （UV） light irradiation on the nanostructured titania in the simulated body fluid （SBF）. The process has three main steps： Ti-24Nb-4Zr-7.9Sn alloy was heated at 650℃ for 3 h, UV-light illumination in air for 4 h and soaking in the SBF for 3 d. A titania coating consisted of main rutile formed on the thermal oxidized Ti-24Nb-4Zr- 7.9Sn alloy. The UV not only converted the futile surface from hydrophilic to hydrophobic but also stimulated high surface activity. After 4 h UV illumination, the contents of Ti3＋ and hydroxyl groups on the oxidized sample were increased, while that of lattice O decreased. After 3 d of soaking in the SBF, a compact and uniform layer of carbonated hydroxyapatite （CHA） particles was formed on the UV-illuminated rutile surface whereas there was a few of HA to be viewed on the surface of as-oxidized Ti-24Nb-4Zr-7.9Sn alloy. Our study demonstrates a simple, fast and cost-effective technique for growing bone-like apatite on titanium alloys.